?url_ver=Z39.88-2004&rft_id=1817011037&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=STABILITAS+DAN+KEMAMPUAN+COPOLY-EUGENOL+DIVINIL+BENZENA+10%25+UNTUK+TRANSPOR+FENOL+MENGGUNAKAN+METODE+POLYMER+INCLUSION+MEMBRANE+(PIM)&rft.creator=KHARISMA+CITRA+APRILIA%2C+1817011037&rft.subject=000+Ilmu+komputer%2C+informasi+dan+pekerjaan+umum&rft.description=Penelitian+stabilitas+dan+kemampuan+transpor+fenol+menggunakan+Co-EDVB+(Kopoli+Eugenol+Divinil+Benzena)+10%25+sebagai+senyawa+carrier+dengan+metode+polymer+inclusion+membrane+(PIM)+telah+dilakukan.+Penelitian+ini+bertujuan+untuk+mengetahui+stabilitas+membran+PIM+dengan+pengaruh+konsentrasi+plasticizer%2C+jenis+dan+konsentrasi+garam%2C+serta+kemampuan+membran+PIM+melalui+pemakaian+berulang+dan+umur+membran.+Membran+dipreparasi+dengan+melarutkan+Co-EDVB+10%25%2C+polivinil+klorida+(PVC)+dan+dibenzil+eter+(DBE)+ke+dalam+pelarut+tetrahidrofuran+(THF).+Penentuan+konsentrasi+fenol+sesudah+proses+transpor+dilakukan+dengan+metode+spektrofotometri+UV-Vis+dengan+penambahan+4-aminoantipirin+dan+absorbansinya+diukur+pada+panjang+gelombang+456+nm.+Hasil+penelitian+menunjukkan+bahwa+stabilitas+membran+dicapai+pada+konsentrasi+plasticizer+3%2C32%25+dengan+konsentrasi+fenol+tertransfor+sebesar+83%2C91%25.+Penambahan+jenis+garam+NaNO3+pada+sumber+menunjukkan+hasil+optimum+dibandingkan+jenis+garam+lainnya%2C+yakni+mampu+mentranspor+fenol+pada+fasa+penerima+sebesar+85%2C84%25.+Transpor+fenol+dengan+melakukan+penambahan+NaNO3+0%2C01+M+di+fasa+sumber+dan+penerima+menghasilkan+fenol+yang+tertranspor+sebanyak+89%2C93%25+dan+86%2C76%25.+Pada+uji+kemampuan+membran+PIM+melalui+pemakaian+berulang+dilakukan+5+kali+pengulangan+transpor.+Pemakaian+berulang+tanpa+pencucian+mampu+mentranspor+fenol+sebesar+72%2C19%25%2C+69%2C23%25%2C+62%2C71%25%2C+55%2C91%25%2C+dan+58%2C16%25%2C+serta+pada+pemakaian+berulangan+dengan+pencucian+mampu+mentranspor+fenol+sebesar+70%2C85%25%2C+64%2C10%25%2C+56%2C72%25%2C+49%2C26%25%2C+dan+27%2C19%25.+Tanpa+penambahan+NaNO3%2C+kemampuan+transpor+membran+hanya+29+hari+tetapi+dengan+penambahan+NaNO3+0%2C1+M+kemampuannya+meningkat+menjadi+58+hari.%0D%0A%0D%0AKata+kunci%3A+Co-EDVB%2C+fenol%2C+PIM%2C+stabilitas%2C+kemampuan%0D%0A%0D%0A%0D%0A%0D%0A%0D%0A%0D%0A%0D%0Aabstract%0D%0A%0D%0AResearch+on+the+stability+and+ability+of+phenol+transport+using+Co-EDVB+(Copoly+Eugenol+Divinyl+Benzene)+10%25+as+a+carrier+using+the+polymer+inclusion+membrane+(PIM)+method+had+been+carried+out.+The+purposes+of+this+research+were+to+determine+the+stability+of+PIM+membranes+with+the+addition+of+plasticizer+concentration%2C+type+and+concentration+of+salt%2C+and+the+ability+of+PIM+membranes+through+repeated+using+and+membrane+lifetime.+The+membrane+was+prepared+by+dissolving+Co-EDVB+10%25%2C+polyvinyl+chloride+(PVC)+and+dibenzyl+eter+(DBE)+in+tetrahydrofuran+(THF)+solvent.+Determination+of+the+concentration+of+phenol+after+the+transport+process+was+carried+out+by+UV-Vis+spectrophotometry+method+with+the+addition+of+4-+aminoantipyrine+and+its+absorbance+was+measured+at+a+wavelength+of+456+nm.+The+results+showed+that+the+membrane+stability+was+achieved+at+a+plasticizer+concentration+of+3.32%25+with+a+transported+phenol+concentration+of+83.91%25.+The+addition+of+NaNO3+salt+at+the+source+phase+was+an+optimum+result+compared+with+other+types+of+salt%2C+which+was+able+to+transport+phenol+in+the+receiving+phase+of+85.84%25.+Phenol+transport+by+adding+0.01+M+NaNO3+in+the+source+and+receiver+phases+resulted+in+89.93%25+and+86.76%25.+In+the+test+of+the+ability+of+the+PIM+membrane+through+repeated+using%2C+5+transport+repetitions+were+carried+out.+Repeated+using+without+washing+was+able+to+transport+phenol+by+72.19%25%2C+69.23%25%2C+62.71%25%2C+55.91%25%2C+and+58.16%25%2C+and+in+repeated+using+with+washing+it+was+able+to+transport+phenol+by+70.85%25%2C+64+.10%25%2C+56.72%25%2C+49.26%25%2C+and+27.19%25.+Without+the+addition+of+NaNO3%2C+the+membrane+transport+ability+was+only+29+days+but+the+addition+of+0.1+M+NaNO3%2C+the+ability+increased+to+58+days.%0D%0A%0D%0AKeywords%3A+Co-EDVB%2C+phenol%2C+PIM%2C+stability%2C+ability&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+&rft.date=2022-10-10&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F67380%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F67380%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F67380%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++KHARISMA+CITRA+APRILIA%2C+1817011037++(2022)+STABILITAS+DAN+KEMAMPUAN+COPOLY-EUGENOL+DIVINIL+BENZENA+10%25+UNTUK+TRANSPOR+FENOL+MENGGUNAKAN+METODE+POLYMER+INCLUSION+MEMBRANE+(PIM).++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F67380%2F