title:     PEMBUATAN   NANOSELULOSA    DARI  KAYU LUNAK  PINUS  (Pinus merkusii)   MENGGUNAKAN METODE HIDROLISIS ASAM  
creator: ANISYAH ANGGRAINI, 1817041013
subject: 001 Ilmu pengetahuan
description:   Telah   dilakukan   pembuatan   nanoselulosa   berbasis   kayu   lunak   pinus   (Pinus merkusii)   menggunakan   metode  hidrolisis   asam.  Pada  penelitian   ini  dibuat  4 sampel dengan variasi konsentrasi  H2S04. Sampel yang telah dibuat dilakukan  uji X-Ray Diffraction  (XRD), Scanning Electron Microscopy  (SEM) dan Fourier Transformed   Infrared   (FTIR).  Hasil  uji  XRD  dianalisis   secara  kualitatif   dan kuantitatif.  Analisis  XRD merujuk  bahwa  semakin besar konsentrasi  H2S04 yang digunakan  maka  persentase   kemurnian   dari  masing-masing   sampel  meningkat. Hasil identifikasi  fasa diperoleh bahwa sampel dengan penambahan  H2S04 19, 29, dan   39%  terbentuk   fasa  la,   I~  dan   lignin.   Sementara,   pada   sampel   dengan penambahan  H2S04 45% hanya terbentuk  fasa I«;  dan I~. Identifikasi  gambar hasil uji  SEM   diperoleh   bahwa   pola   gambar   memiliki   struktur   bentuk   distribusi menyerupai   susunan   lempengan   batu   yang  rap at  dan  saling  tumpang   tindih. Analisis  FTIR menunjukkan  gugus fungsi  yang terbentuk  yaitu O-H, C-H, C=C, C=C, H-C-H, C-O dan C-O-C yang menunjukkan  kehadiran  selulosa.    Kata  Kunci:  Nanoselulosa,  Pinus, hidrolisis  asam, H2S04.    Research  has  been  conducted  on nanocellulose  from  the main  material  of soft pine  wood  (Pinus  merkusii)  by  acid  hydrolysis  method.  In  this  study,  4  study samples were made using variations  in the concentration  of H2S04. The prepared samples  were tested by X-Ray Diffraction  (XRD), Scanning  Electron  Microscopy (SEM) and Fourier  Transformed  Infrared  (FTIR). XRD test results were analyzed qualitatively   and  quantitatively.   XRD  analysis   indicated   that  the  greater   the concentration  of H2S04 used, the percentage  of purity  of each sample  increased. Phase  identification  results obtained  that the sample  with the addition  of H2S04  19, 29, and 39% formed  phases  la,  Ip and  lignin.  While  in the sample  with  the  addition  of 45% H2S04 only Ia and Ip phases  are formed.  The addition  of H2S04 affects  the molar percent  of each phase.  The higher  the concentration  of H2S04 the  greater   the  value   of  the  molar  percentage   of  phases   L; and  Ip.  Image identification   from   SEM   test   results   shows   that   the   image  pattern   has   a distribution   structure   resembling  a  compact  and  overlapping   arrangement   of stone  slabs.  FTIR  analysis  shows  the functional   groups formed   are  O-H,  C-H, C=C, C=C, H-C-H,  C-O and C-O-C which indicate the presence  of cellulose.    Keywords:  nanocellulose,  pine,  hydrolysis method, H2S04.      
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM 
date: 2022-11-28
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/67523/1/ABSTRAK.pdf
format: text
identifier: http://digilib.unila.ac.id/67523/3/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/67523/2/SKRIPSI%20TANTA%20BAB%20PEMBAHASAN.pdf
identifier:   ANISYAH ANGGRAINI, 1817041013  (2022)  PEMBUATAN NANOSELULOSA DARI KAYU LUNAK PINUS (Pinus merkusii) MENGGUNAKAN METODE HIDROLISIS ASAM.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/67523/