%A 1617041028 Risky Putra Ramadhan
%T ANALISIS PERTUMBUHAN FASE SUPERKONDUKTOR BSCCO-2212
DAN BPSCCO-2212 AKIBAT VARIASI SUHU SINTERING
MENGGUNAKAN METODE PENCAMPURAN BASAH
%X Penelitian dilakukan untuk mengetahui pengaruh variasi suhu sintering terhadap
tingkat kemurnian fase superkonduktor BSCCO-2212 dan BPSCCO-2212
menggunakan metode pencampuran basah. Variasi suhu sintering yang digunakan
adalah 825, 830, 835 dan 840?C selama 20 jam. Hasil XRD menunjukkan bahwa
tingkat kemurnian fase pada superkonduktor BSCCO-2212 dan BPSCCO-2212
meningkat hingga mencapai titik optimum pada suhu sintering 835?C kemudian
mengalami penurunan pada suhu sintering 840?C. Fraksi volume tertinggi sampel
BSCCO-2212 didapatkan pada suhu sintering 835?C sebesar 71,09% dan derajat
orientasi tertinggi didapatkan pada suhu sintering 830?C sebesar 23,38%. Pada
sampel BPSCCO-2212 fraksi volume tertinggi didapatkan pada suhu sintering
835?C sebesar 52,59% dan derajat orientasi tertinggi pada suhu sintering 830?C
sebesar 43,49%. Hasil perbandingan sampel BSCCO-2212 dan BPSCCO-2212
diperoleh bahwa sampel BPSCCO-2212 memiliki tingkat kemurnian fase yang
lebih tinggi dibandingkan BSCCO-2212.

Kata kunci : Superkonduktor BSCCO-2212, Suhu Sintering, Fraksi Volume
The research is done to see how variations of sintering temperatures would affect
the level of chasteness of the superconducting phases of BSCCO-2212 and the
BPSCCO-2212 using methods of moist mixing. Variations of sintering
temperatures used are 825, 830, 835 and 840?C over 20 hours. XRD results show
that the level of phase innocence on the superconductors of BSCCO-2212 and the
BPSCCO-2212 increased to the point of optimum at sintering temperature 835?C

then went down at sintering 840?C. The higher-volume fraction of the BSCCO-
2212 obtained at sintering temperature 835?C by 71,09% and the highest degree

of orientation obtained at sintering temperature 830?C by 23.38%. On sample
BPSCCO-2212 fractions of the highest volume found at sintering temperature
835?C for 52.59% and the highest degree of orientation at sintering temperature
830?C by 43.49%. The ratio of sample BSCCO-2212 and BPSCCO-2212 were
obtained that sample BPSCCO-2212 had a higher level of phase purity than
BSCCO-2212.

Keywords: Superconductor BSCCO-2212, Sintering Temperature, Volume

Fraction
%C UNIVERSITAS LAMPUNG
%D 2021
%I FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
%L eprints68122