N2  -    Pada  penelitian  ini,  zeolit-X  disintesis  dari  silika  sekam  padi  dan  aluminium  foil yang dilakukan dengan metode hidrotermal pada suhu 100 °C selama 96 jam dan dikalsinasi  selama  6  jam  pada  suhu  550  °C.  Zeolit-X  kemudian  dimodifikasi menjadi zeolit-X terprotonasi (H-X) melalui proses pertukaran ion menggunakan larutan NH4NO3 dengan variasi konsentrasi 2M (HX1); 2,5M (HX2); 3M (HX3) dan 3,5M  (HX4).  Zeolit-X  dan  zeolit-X  terprotonasi  (H-X)  dikarakterisasi menggunakan instrumen XRD, XRF, SEM-EDX dan FTIR. Karakterisasi dengan XRD mengindikasikan bahwa zeolit-X dan zeolit H-X dalam fase kristal. Zeolit-X berhasil  diprotonasi  dan  telah  dikarakterisasi  dengan  XRF  untuk  menunjukkan persentase konversi Na menjadi H. Karakterisasi dengan SEM menunjukkan bahwa zeolit-X dan zeolit H-X memiliki morfologi kubus oktahedral tetapi masih tertutup oleh cluster dan EDX menunjukkan komposisi zeolit yang terdiri dari Si, O, Al, dan Na.  Karakterisasi  zeolit-X  dan  H-X  dengan  FTIR  terdeteksi  adanya  situs  asam Bronsted-Lowry.  Pengujian  aktivitas  katalitik  dilakukan  dengan  pirolisis  BCO (Bio-Crude  Oil)  hasil  pirolisis  minyak  kelapa  sawit  yang  diidentifikasi menggunakan GC-MS. Hasil penelitian menunjukkan bahwa persentase kandungan biogasolin  C5-C12  pada  sampel  cair  menggunakan  katalis  NaX  sebesar  61,63%; HX1 52,34%; HX2 37,91%; HX3 55,89% dan HX4 30,91%.   
Kata kunci: zeolit-X terprotonasi (HX), zeolit-X, BCO, pirolisis, biogasolin.

   In  this  study,  zeolite-X  was  synthesized  from  rice  husk  silica  and  aluminum  foil which was carried out by hydrothermal method at 100 ? for 96 hours and calcined for 6 hours at 550 ?. Zeolite-X was then modified into protonated zeolite-X (H-X) through  an  ion  exchange  process  using  NH4NO3  solutions  with  concentration variations of 2M (HX1); 2.5M (HX2); 3M (HX3) and 3.5M (HX4). Zeolite-X and protonated  zeolite-X  (H-X)  are  characterized  using  XRD,  XRF,  SEM-EDX  and FTIR instruments. XRD characterization of zeolite-X and zeolite H-X indicate the crystalline phase. Successfully protonated zeolite-X is performed characterized by XRF to indicate the percent conversion of Na to H. SEM characterization shows zeolite-X and zeolite H-X have the octahedral cube morphology but still enclosed by clusters, and EDX shows the composition of zeolite consisting Si, O,  Al, and Na.  Characterization  of  zeolite-X  and  H-X  with  FTIR  detected  the  presence  of bronsted-Lowry acid sites. Catalytic activity testing was carried out by pyrolysis of BCO (Bio-Crude Oil) resulting from palm oil pyrolysis identified using GC-MS. The  results  showed  that  the  percentage  of  biogasolin  C5-C12  content  in  liquid samples using NaX catalysts was 61.63%; HX1 52.34%; HX2 37.91%; HX3 55.89% and HX4 30.91%.   Keywords: protonated zeolite-X (HX), zeolite-X, BCO, pyrolysis, biogasoline. 


PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - PENGOLAHAN LANJUT BIO-CRUDE OIL HASIL PIROLISIS MINYAK KELAPA SAWIT DENGAN METODE CATALYTIC UPGRADING MENGGUNAKAN ZEOLIT-X TERPROTONASI (H-X) SEBAGAI KATALIS 