title: SINTESIS DAN KARAKTERISASI ZEOLIT ANALSIM PORI HIERARKI MENGGUNAKAN PATI SEBAGAI MESOPOROGEN SERTA UJI AKTIVITAS KATALITIK PADA REAKSI  ISOMERISASI GLUKOSA
creator: Ester , Hellen Novalina Lumban Gaol
subject: 500 ilmu pengetahuan alam dan matematika
subject: 540 Kimia dan ilmu yang berhubungan
description: Limbah biomassa yang melimpah di Provinsi Lampung seperti ampas tebu belum banyak dimanfaatkan menjadi produk yang lebih bernilai terkhusus dibidang industri, sehingga dilakukan penelitian ini untuk mempelajari aktivitas katalitik H-ANA termodifikasi logam Ni yang disintesis menggunakan silika berbasis abu ampas tebu (Sugarcane Bagasse Ash/SCBA) dalam reaksi isomerisasi glukosa. Tahapan yang dilakukan pada penelitian ini yaitu ekstraksi silika SCBA sebagai prekursor dalam mensintesis zeolit ANA pada suhu 170 C selama 120 jam melalui metode Steam-Assisted Crystallization (SAC) dengan penambahan pati sebagai mesoporogen dan disinteis zeolit ANA tanpa penambahan pati sebagai pembanding, pertukaran ion menjadi bentuk H-ANA pori hierarki dan impregnasi menggunakan logam Ni serta uji aktivitas katalitik pada reaksi isomerisasi. Silika SCBA memiliki rendemen sebesar 3.19 % dominan berfasa amorf dari hasil XRD. Rasio Si/Al 1,42 dan terkonfirmasi memiliki gugus silanol (Si-OH) dan siloksan (Si-O-Si). ANA dengan penambahan pati dan ANA tanpa penambahan pati telah berhasil disintesis karena memiliki kemiripan dengan pola difraksi standar ANA serta memiliki kristalinitas masing-masing 76,08 % dan 74,53 %, ANA dengan penambahan pati memiliki luas permukaan 61.635 m2g-1, volume pori 0.04 cm3g-1 dan pori tambahan sebesar 2.30 nm. Kondisi optimum uji katalitik pada reaksi isomerisasi yaitu pada suhu 80 C selama 30 menit dengan jumlah katalis sebesar 0.03 g. Konversi glukosa tertinggi diperoleh menggunakan katalis Ni/H-ANA dengan penambahan pati yaitu sebesar 38,14 %.    Kata Kunci: Silika SCBA, H-ANA, Mesoporogen Pati, Impregnasi, Reaksi Isomerisasi.            ABSTRACT    Abundant biomass waste in Lampung province such as bagasse has not been widely used as a more valuable product, especially in the industrial field, so this study was conducted to study the catalytic activity of H-ANA modified Ni metal synthesized using silica-based bagasse ash (Sugarcane Bagasse Ash/SCBA) in glucose isomerization reaction. The steps carried out in this study were the extraction of silica SCBA as a precursor in synthesizing ANA zeolite at 170 °C for 120 hours through the Steam-Assisted Crystallization (SAC) method with the addition of starch as a mesoporous and the synthesis of ANA zeolite without the addition of starch as a comparison, exchange ions into hierarchical pore H-ANA forms and impregnation using Ni metal as well as testing the catalytic activity in the isomerization reaction. Silica SCBA has a dominant amorphous yield of 3.19 % from the XRD results. Si/Al ratio of 1.42 and confirmed to have silanol (Si-OH) and siloxane (Si-O-Si) groups. ANA with the addition of starch and ANA without the addition of starch have been successfully synthesized because they are similar to the standard ANA diffraction pattern and have a crystallinity of 76.08 % and 74.53 % respectively, ANA with the addition of starch has a surface area of 61.635 m2g-1, pore volume of 0.04 cm3g-1 and an additional pore of 2.30 nm. The optimum condition for the catalytic test for the isomerization reaction was at 80 °C for 30 minutes with a catalyst amount of 0.03 g. The highest glucose conversion was obtained using a Ni/H-ANA catalyst with the addition of starch which was 38.14 %.    Keywords: Silica SCBA, H-ANA, Starch as a Mesoporogen, Impregnation, Isomerization Reaction
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM 
date: 2023-01-18
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/69279/1/ABSTRAK.pdf
format: text
identifier: http://digilib.unila.ac.id/69279/2/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/69279/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   Ester , Hellen Novalina Lumban Gaol  (2023) SINTESIS DAN KARAKTERISASI ZEOLIT ANALSIM PORI HIERARKI MENGGUNAKAN PATI SEBAGAI MESOPOROGEN SERTA UJI AKTIVITAS KATALITIK PADA REAKSI ISOMERISASI GLUKOSA.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/69279/