%A 1717041029 MAYANG SHAVIRA
%T ANALISIS PEMANFAATAN VARIASI KONSENTRASI ALUMINA DAN CARBON DALAM JEMBATAN GARAM PADA SEL ELEKTROKIMIA
Zn|Zn2+(Aq)||Ag+(Aq)|Cu(Ag) DENGAN ELEKTROLIT AIR LAUT DAN
ACID ZINC SEBAGAI SUMBER ENERGI ALTERNATIF
%X Penelitian ini dilakukan untuk menganalisis perbandingan variasi jembatan garam pada sel volta dua kompartemen dengan electrode Cu(Ag)-Zn terhadap nilai karakteristik elektrik yang dihasilkan. Pasangan Cu(Ag)-Zn digunakan untuk menghasilkan tegangan dan arus dalam sel dengan elektrolit air laut dan acid zinc. Dua kompartemen dibatasi dengan jembatan garam yang terbuat dari Al2O3 (aluminium oksida), dan Carbon, NaCl (air laut) yang terlarut dalam semen putih tiga roda. Sel volta terdiri dari 4 sel yang tersusun secara seri yang setiap sel terisi dengan ?200 ml air laut (bagian katode) dan ?200 ml larutan acid zinc (bagian anode). Sel volta diukur dengan multitester setiap 1 jam sekali selama 3 hari. Berdasarkan penelitian yang telah dilakukan diperoleh kesimpulan bahwa variasi jembatan garam carbon 12 gram memiliki nilai karakteristik elektrik yang paling besar.

Kata kunci: Air laut, jembatan garam, larutan acid zinc, sel volta





ABSTRACT

This study was conducted to analyze the comparison of variations in the salt bridge in a two-compartment voltaic cell with a Cu(Ag)-Zn electrode on the resulting electrical characteristics. The Cu(Ag)-Zn pair is used to generate voltage and current in the cell with seawater electrolyte and zinc acid. The two compartments are lined with a salt bridge made of Al2O3 (aluminum oxide), and Carbon, NaCl (seawater) dissolved in Tiga Roda white cement. The voltaic cell consists of 4 cells arranged in series, each cell filled with ?200 ml of seawater (cathode part) and ?200 ml of acid zinc solution (anode part). The voltaic cell was measured with a multitester every 1 hour for 3 days. Based on the research that has been done, it can be concluded that the variation of the carbon salt bridge with a concentration of 12 grams has the greatest electrical characteristic value.

Keywords: seawater, salt bridge, zinc acid, voltaic cell