?url_ver=Z39.88-2004&rft_id=1914051043&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+PENAMBAHAN+GLISEROL+DAN+CMC+(Carboxyl+Methyl+Cellulose)+TERHADAP+KARAKTERISTIK+BIODEGRADABLE+FILM+BERBASIS+SELULOSA+KULIT+BUAH+PINANG+(Areca+catechu+L)&rft.creator=SELA+%2C+JULITA+&rft.subject=630+Pertanian+dan+teknologi+yang+berkaitan&rft.description=Biodegradable+film+merupakan+bahan+pengganti+plastik+yang+bersifat+ramah+lingkungan.++Kulit+buah+pinang+potensial+dalam+pembuatan+biodegradable+film+karena+mengandung+selulosa+yang+tinggi+yaitu+sebesar+34%2C18%25.++Tujuan+penelitian+ini+ialah+mengetahui+pengaruh+penambahan+gliserol+terhadap+karakteristik+biodegradable+film+berbahan+dasar+kulit+buah+pinang%2C+mengetahui+pengaruh+CMC+terhadap+karakteristik+biodegradable+film+berbahan+dasar+kulit+buah+pinang%2C+dan+mengetahui+interaksi+gliserol+dan+CMC+untuk+menghasilkan+karakteristik+biodegradable+film+terbaik+berbahan+dasar+kulit+buah+pinang.++Penelitian+disusun+dalam+RAKL+dengan+2+faktor+dan+3+ulangan.++Faktor+pertama+penambahan+gliserol+dengan+konsentrasi+0%2C5%25+(G1)%2C+1%25+(G2)%2C+dan+1%2C5%25+(G3)%2C+dan+faktor+kedua+dengan+penambahan+CMC+terdiri+dari+konsentrasi+1%25+(C1)%2C+2%25+(C2)%2C+dan+3%25+(C3).++Kulit+buah+pinang+dikeringkan%2C+dihaluskan%2C+disaring%2C+direndam+menggunakan+NaOH+2%2C5%25+dan+hidrolisis+menggunakan+H2O2+2%25%2C+kemudian+dicampur+dengan+bahan+lainnya.++Data+yang+diperoleh+dianalisis+sidik+ragam+dan+diuji+lanjut+dengan+uji+beda+nyata+terkecil+(BNT)+pada+taraf+5%25.++Hasil+penelitian+terbaik+diperoleh+pada+interaksi+perlakuan+gliserol+1%25+dan+CMC+3%25+dengan+nilai+kuat+tarik+sebear+71%2C87+MPa%2C+persen+pemanjangan+26%2C27%25%2C+ketebalan+0%2C32+mm%2C+permeabilitas+uap+air+7%2C41+g%2Fm2%2Fjam%2C+dan+biodegradabilitas+selama+28+hari.%0D%0A%0D%0AKata+Kunci%3A+Biodegradable+film%2C+selulosa+kulit+buah+pinang%2C+gliserol%2C+CMC%0D%0A%0D%0ABiodegradable+film+is+an+environmentally+friendly+plastic+replacement+packaging.++Areca+fruit+peel+has+the+potential+in+making+biodegradable+film+because+it+contains+high+cellulose+which+is+34.18%25.+This+study+aims+to+determine+the+effect+of+glycerol+and+on+the+characteristics+of+areca+nut+peel-based+biodegradable+film%2C+to+determine+the+effect+of+CMC+on+the+characteristics+of+areca+nut+peel-based+biodegradable+film%2C+and+to+determine+the+interaction+of+glycerol+and+CMC+to+produce+the+best+characteristics+of+areca+nut+peel-based+biodegradable+film.++The+study+was+arranged+in+RAKL+with+2+factors+and+3+replications.++The+first+factor+was+the+addition+of+glycerol+with+concentrations+of+0.5%25+(G1)%2C+1%25+(G2)%2C+and+1.5%25+(G3)%2C+and+the+second+factor+was+the+addition+of+CMC+consisting+of+concentrations+of+1%25+(C1)%2C+2%25+(C2)%2C+and+3%25+(C3).++Areca+fruit+peels+were+dried%2C+mashed%2C+filtered%2C+soaked+using+2.5%25+NaOH+and+hydrolyzed+using+2%25+H2O2%2C+then+mixed+with+other+ingredients.++The+data+obtained+were+analyzed+for+variance+and+further+tested+with+the+Least+Significant+Difference+Test+(BNT)+at+the+5%25+level.++The+best+research+results+were+obtained+in+the+interaction+of+1%25+glycerol+and+3%25+CMC+treatment+with+a+tensile+strength+of+71.87+MPa%2C+percent+elongation+value+of+26.27%25%2C+thickness+of+0.32+mm%2C+water+vapor+permeability+of+7.41+g%2Fm2%2Fhour%2C+and+biodegradability+for+28+days.%0D%0A%0D%0AKeywords%3A+Biodegradable+film%2C+areca+nut+peel%2C+cellulose%2C+glycerol%2C+CMC+%0D%0A&rft.publisher=FAKULTAS+PERTANIAN&rft.date=2023-04-11&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F71172%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F71172%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F71172%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++SELA+%2C+JULITA+++(2023)+PENGARUH+PENAMBAHAN+GLISEROL+DAN+CMC+(Carboxyl+Methyl+Cellulose)+TERHADAP+KARAKTERISTIK+BIODEGRADABLE+FILM+BERBASIS+SELULOSA+KULIT+BUAH+PINANG+(Areca+catechu+L).++FAKULTAS+PERTANIAN%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F71172%2F