title: PERILAKU PERAMBATAN RETAK FATIK STAINLESS STEEL 304
YANG DILAPISI ALUMINIUM CELUP PANAS SECARA
EKSPERIMENTAL DAN NUMERIKAL
ispublished: pub
subjects: 000
full_text_status: restricted
abstract: Analisa perambatan retak fatik stainless steel 304 yang dilapisi aluminium dengan
metode hot-dip secara ekperimen dan numerikal untuk mengetahui perubahan sifat
mekanik pada SS304 serta memprediksi hasil uji perambatan retak fatik secara metode
numerik yang berbasis program CFD dengan hasil secara ekperimen. Hasil simulasi
siklus perambatan retak fatik menunjukkan hasil yang sama. SS 304 dengan difusi 1
jam memiliki siklus terpendek yaitu pada data simulasi terjadi retakan di siklus 8778
dengan Panjang retak 0,70 mm, sedangkan untuk hasil eksperimen retakan terjadi di
siklus 5000 dengan panjang retak 0,27 mm. Lalu SS304 tanpa pelapisan memiliki
siklus terpanjang yaitu, retakan pada hasil simulasi terjadi di siklus 8103 dengan
Panjang retak 0,63 mm, sedangkan pada data hasil eksperimen awal retakan di siklus
8700 dengan Panjang retak 0,6 mm. Berdasarkan analisis laju perambatan retak fatik
dan tegangan, pemberian perlakuan difusi pada SS304 memberikan dampak baik untuk
umur kelelahan maupun tegangan untuk merambatkan retak. Kekuatan dan plastisitas
SS304 terdegradasi oleh perlakuan aluminisasi. Setelah perlakuan, SS304
menunjukkan keuletan yang lebih tinggi dan kekuatan yang lebih rendah.
Kata Kunci : SS304, Hot-dip, Perambatan Retak Fatik, CFD.
Analysis of fatigue crack propagation of 304 stainless steel coated with aluminum by
hot-dip method experimentally and numerically to determine changes in mechanical
properties of SS304 and predict fatigue test results numerically based on CFD program
with experimental results. The simulation results of the fatigue crack propagation cycle
show the same results. SS 304 with 1 hour diffusion has the shortest cycle, namely in
the simulation data a crack occurs at cycle 8778 with a crack length of 0.70 mm, while
for experimental results the crack occurs at cycle 5000 with a crack length of 0.27 mm.
Then SS304 without coating has the longest cycle, namely, cracks in simulation results
occur in cycle 8103 with a crack length of 0.63 mm, while in the experimental data the
initial crack in cycle 8700 with a crack length of 0.6 mm. Based on the analysis of
fatigue crack propagation rate and stress, giving diffusion treatment to SS304 has an
impact on both fatigue life and stress to propagate cracks. The strength and plasticity
of SS304 were degraded by the aluminization treatment. After treatment, SS304 showed
higher ductility and lower strength.
Keywords : SS304, Hot-dip, Fatigue Crack Propagation, CFD
date: 2023-06-10
date_type: published
institution: UNIVERSITAS LAMPUNG
department:  FAKULTAS TEKNIK 
thesis_type: masters
citation:   FARID NANDA , SYANUR  (2023) PERILAKU PERAMBATAN RETAK FATIK STAINLESS STEEL 304 YANG DILAPISI ALUMINIUM CELUP PANAS SECARA EKSPERIMENTAL DAN NUMERIKAL.  Masters thesis, UNIVERSITAS LAMPUNG.   
document_url: http://digilib.unila.ac.id/72662/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/72662/2/TESIS%20FULL.pdf
document_url: http://digilib.unila.ac.id/72662/3/TESIS%20TANPA%20BAB%20PEMBAHASAN.pdf