N2  - ABSTRAK
STUDI TRANSPOR MALACHITE GREEN MENGGUNAKAN METODE
POLYMER INCLUSION MEMBRANE (PIM) DENGAN POLYEUGENOL
SEBAGAI SENYAWA PEMBAWA

Penelitian transpor Malachite Green (MG) dengan polyeugenol sebagai senyawa
pembawa menggunakan metode PIM (Polymer Inclusion Membrane) telah
dilakukan. Penelitian ini bertujuan untuk mempelajari pengaruh pH pada fasa
sumber, konsentrasi HNO3 pada fasa penerima, ketebalan membran, konsentrasi
senyawa pembawa, dan waktu transpor MG menggunakan polyeugenol sebagai
senyawa pembawa dengan metode PIM serta mempelajari kompetisi transpor MG
pada limbah buatan. Preparasi membran dilakukan dengan melarutkan
polyeugenol, polivinil klorida (PVC), dan dibenzil eter (DBE) ke dalam pelarut
tetrahidrofuran (THF). Konsentrasi MG setelah transpor ditentukan dengan
spektrofotometer UV-Vis dan absorbansinya diukur pada panjang gelombang 613
nm. Hasil penelitian menunjukkan bahwa membran PIM dengan senyawa
pembawa polyeugenol mampu mentranspor MG pada pH fasa sumber 7,
konsentrasi fasa penerima 0,75M, ketebalan membran PIM T54, konsentrasi
senyawa pembawa 0,04M dengan waktu transpor 24 jam dengan %removal
sebesar 89,09%. Membran PIM sebelum dan setelah transpor dikarakterisasi
menggunakan FT-IR dan SEM. Transpor MG dengan logam Cu(II) dan Pb(II)
menghasilkan %removal MG lebih kecil dibandingkan transpor MG tanpa logam.
Keberadaan logam kompetitor menjadi pengganggu pada proses transpor MG dari
fasa sumber menuju fasa penerima.
Kata kunci : Malachite Green, Polyeugenol, Polymer Inclusion Membrane.

Malachite Green (MG) transport research using polyeugenol as a carrier applying
the PIM (Polymer Inclusion Membrane) method had been conducted. This
research aim to study the effect of pH on the source phase, HNO3 concentration
on the receiving phase, membrane thickness, the carrier concentration, and MG
transport time and learning the competition for MG transport in artificial waste.
Membrane preparation was carried out by dissolving polyeugenol, polyvinyl
chloride (PVC), and dibenzyl ether (DBE) in tetrahydrofuran (THF) solvent. The
concentration of MG after transport was determined with a UV-Vis
spectrophotometer at a wavelength of 613 nm. The results showed that the PIM
membrane with the polyeugenol carrier was able to transport MG at the source
phase pH of 7, the concentration of the receiving phase was 0.75M, the thickness
of the PIM T54 membrane, the concentration of the carrier was 0.04M with the
transport time of 24 hours with the rate of %removal was 89.09%. PIM
membranes before and after transport were characterized using FT-IR and SEM.
PIM membranes before and after transport were characterized using FT-IR and
SEM. MG transport with Cu(II) and Pb(II) metals resulted in a lower %removal of
MG than MG transport without metal. The presence of competing metals
interfered with the MG transport process from the source phase to the receiving
phase.
Keywords: Malachite Green, Polyeugenol, Polymer Inclusion Membrane.
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - STUDI TRANSPOR MALACHITE GREEN MENGGUNAKAN METODE
POLYMER INCLUSION MEMBRANE (PIM) DENGAN POLYEUGENOL
SEBAGAI SENYAWA PEMBAWA
AV  - restricted
ER  -