<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN"^^ . "Ferosemen adalah konstruksi beton bertulang tipis yang dibuat dari\r\ncampuran pasir dan semen hidrolik dengan penulangan kawat jala berdiameter kecil\r\nberlapis-lapis dan menerus diseluruh bagian strukturnya. Sebagai struktur beton\r\nbertulang yang tipis, retakan kecil pada struktur ferosemen dapat meluas ke seluruh\r\nstruktur dan dapat menyebabkan keruntuhan. Penambahan fiber polypropylene\r\n(PPF) dalam penelitian ini bertujuan untuk memperkuat sifat mekanik plat\r\nferosemen.\r\nPenelitian ini menyajikan pengaruh fiber polypropylene terhadap kuat tekan\r\ndan kuat lentur pada benda uji mortar ferosemen dengan dimensi 160 mm x 40 mm\r\nx 40 mm dan plat ferosemen dimensi 240 mm x 60 mm x 25 mm. Penelitian ini\r\nmenggunakan komposisi mortar dengan perbandingan 1 : 2,5 : 0,35 untuk\r\nperbandingan semen, pasir dan air, dengan jumlah lapisan jaring kawat sebanyak 2\r\nlapis dan 4 lapis, serta terdapat variasi menggunakan tulangan dan tanpa\r\nmenggunakan tulangan didalamnya. Variasi fiber polypropylene yang digunakan\r\nadalah 0%, 1% dan 2% dari volume benda uji. Pengujian dilakukan pada benda uji\r\nberumur 28 hari. Berdasarkan hasil pengujian, nilai kuat tekan dan kuat lentur\r\noptimum pada benda uji mortar ferosemen terdapat pada penambahan PPF 1%.\r\nPenambahan fiber polypropylene pada benda uji plat ferosemen tidak\r\nmempengaruhi kekuatan pada benda uji plat ferosemen, hal ini terjadi dikarenakan\r\npenambahan fiber yang terdapat pada campuran mortar tidak tersebar secara merata\r\ndan membentuk air void atau rongga udara, sehingga mengurangi kekuatan pada\r\nbenda uji plat ferosemen. Nilai beban maksimum tertinggi bada benda uji plat\r\nferosemen terdapat pada kode benda uji PLT.0%.4.B (variasi PPF 0%, dengan\r\ntulangan diameter 6 mm serta 4 lapis jaring kawat). Tulangan dan jawing kawat\r\nmemiliki peranan yang sangat penting pada benda uji plat ferosemen. Benda uji plat\r\nferosemen yang memilik tulangan di dalamnya mengalami retak secara perlahan\r\ndan tidak terbagi menjadi beberapa bagian. Hal ini terjadi dikarenakan tulangan dan\r\njaring kawat dapat menahan gaya tarik.\r\n\r\nKata kunci: fiber polypropylene, mortar ferosemen, plat ferosemen, kuat tekan, kuat\r\nlentur, beban maksimum \r\n\r\nFerrocement is a thin reinforced concrete construction made from a mixture\r\nof sand and hydraulic cement by reinforcing small diameter wire mesh in layers and\r\ncontinuously throughout the structure. As a thin reinforced concrete structure, small\r\ncracks in the ferrocement structure can extend throughout the structure and can\r\ncause collapse. The addition of polypropylene fiber (PPF) in this study aims to\r\nstrengthen the mechanical properties of the ferrocement plate.\r\nThis study presents the effect of polypropylene fiber on compressive\r\nstrength and flexural strength on ferrocement mortar specimens with dimensions of\r\n160 mm x 40 mm x 40 mm and ferrocement plates with dimensions of 240 mm x\r\n60 mm x 25 mm. This study used a mortar composition with a ratio of 1 : 2.5 : 0.35\r\nfor the ratio of cement, sand and water, with a number of layers of wire mesh of 2\r\nlayers and 4 layers, and there were variations using reinforcement and without using\r\nreinforcement in it. Variations of polypropylene fiber used are 0%, 1% and 2% of\r\nthe volume of the test object. Tests were carried out on specimens aged 28 days.\r\nBased on the test results, the optimum compressive strength and flexural strength\r\nvalues on the ferrocement mortar test specimens were found in the addition of 1%\r\nPPF. The addition of polypropylene fiber to the ferrocement plate specimen did not\r\naffect the strength of the ferrocement plate test object, this occurred because the\r\nadded fiber contained in the mortar mixture was not spread evenly and formed air\r\nvoids or air voids, thereby reducing the strength of the ferrocement plate test object.\r\nThe highest maximum load value for the ferrocement plate test object is found in\r\nthe test object code PLT.0%.4.B (0% PPF variation, with 6 mm diameter\r\nreinforcement and 4 layers of wire mesh). Reinforcement and wire jaws have a very\r\nimportant role in the ferrocement plate test object. The ferrous cement plate test\r\nobject which has reinforcement in it cracks slowly and is not divided into several\r\nparts. This happens because the reinforcement and wire mesh can withstand the\r\ntensile force.\r\n\r\nKeywords: polypropylene fiber, ferrocement mortar, ferrocement plate,\r\ncompressive strength, flexural strength, maximum load\r\n "^^ . "2023-07-26" . . . . . "FAKULTAS TEKNIK"^^ . . . . . . . "Adam Nabil"^^ . "Gerry "^^ . "Adam Nabil Gerry "^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (File PDF)"^^ . . . "ABSTRAK.pdf"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (File PDF)"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (File PDF)"^^ . . . "FILE SKRIPSI TANPA BAB PEMBAHASAN.pdf"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "preview.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "medium.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "small.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "preview.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "medium.jpg"^^ . . . "PENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN (Other)"^^ . . . . . . "small.jpg"^^ . . "HTML Summary of #74732 \n\nPENGARUH FIBER POLYPROPYLENE TERHADAP SIFAT MEKANIK PLAT FEROSEMEN\n\n" . "text/html" . . . "600 Teknologi (ilmu terapan)" . . . "620 Ilmu teknik dan ilmu yang berkaitan" . . . "690 Pembangunan gedung" . .