title: PENGARUH PERLAKUAN PANAS MULTI AUSTEMPERING  TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO   BAJA AISI 4140
creator: PURNOMO, PURNOMO
subject: 600 Teknologi (ilmu terapan)
subject: 604 Menggambar teknik, bahan berbahaya
subject: 620 Ilmu teknik dan ilmu yang berkaitan
description:   Penyelidikan dilakukan untuk mengetahui masing-masing parameter hasil   rekayasa struktur mikro dibawah kondisi perlakuan panas pada baja AISI 4140  yang mempunyai komposisi kimia dalam % berat: 0.443C, 0.198 Mo, 0.805Mn,  1.150Cr,  0.308Si, 0.021P, dikenakan perlakuan panas anil penuh (AN),  austempering satu dan multi langkah (SA) dan (MA). Spesimen uji tarik dengan  standar ASTM E8 telah disiapkan. Proses AN dilakukan dengan memanaskan  semua sampel di dalam tanur suhu konstan 800°C selama 2 jam, dilanjutkan  pendinginan di dalam tanur. Kemudian, spesimen diberi perlakukan panas SA1,  SA2. SA3 dan MA . Proses SA dan MA masing-masing dilakukan dengan  memanaskan semua sampel dalam tanur pada suhu 800°C selama 1 jam dan  dilanjutkan dengan perendaman dalam media larutan garam 50% NaNO  3  +  50%KNO  3   pada temperatur 312, 362 dan 412°C selama 1 jam. Proses AN  menghilangkan tegangan internal dengan kelembutan struktur mikro yang tinggi,  sedangkan proses SA dan MA menghasilkan struktur mikro fasa bainit yang halus,  yang meningkatkan sifat-sifat mekanik (kekuatan tarik dan kekuatan impak)  dengan elastisitas yang baik. Mikroskop elektron pemindaian digunakan untuk  mengetahui konsentrasi pengotor dan perubahan struktur mikro pada sifat mekanik  spesimen yang bersangkutan. Hasil penelitian menunjukkan bahwa sampel SA1  memiliki ketangguhan terbaik dengan nilai 41 Joule, sedangkan sampel MA  bernilai 32.67 Joule. Spesimen dengan nilai kekerasan tertinggi adalah SA2 dengan  nilai kekerasan 43.67 HRC, sedangkan pada benda uji MA 43.00 HRC. Spesimen  SA1 menjadi benda uji yang mampu menerima beban maksimum terbesar sebelum  mengalami kegagalan dengan nilai UTS 922.36 MPa dengan regangan 13,09%.   Sementara itu, spesimen MA menjadi benda uji yang mampu menahan beban  maksimum tanpa mengalami deformasi plastis yang permanen tertinggi dengan  nilai Yield Strenght 579.32 MPa.   Kedepan hasil penelitian ini akan menjadi solusi alternatif bagi permasalahan   ketersediaan bahan baku baja AISI 4140 yang melimpah, dengan biaya murah dan  ketangguhan yang dihasilkan.    Kata kunci : AISI 4140, Kekerasan, Mikrostruktur, Anealling, Single  Austempering               This research investigates the effects of different heat treatment parameters on the  microstructure of AISI 4140 steel, which has the following chemical composition in  weight %: 0.443C, 0.198 Mo, 0.805Mn, 1.150Cr, 0.308Si, 0.021P. The heat  treatments applied are full annealing (AN), single-step austempering (SA), and  multi-step austempering (MA). Tensile test specimens were prepared according to  ASTM E8 standards. The AN process involved heating all samples in a furnace at a  constant temperature of 800°C for 2 hours, followed by furnace cooling.  Subsequently, the specimens underwent SA1, SA2, SA3, and MA heat treatments.  The SA and MA processes consisted of heating all samples in a furnace at 800°C  for 1 hour and then quenching them in a 50% NaNO3 + 50% KNO3 salt solution  at temperatures of 312°C, 362°C, and 412°C for 1 hour.  The AN process eliminated internal stresses, resulting in a highly soft  microstructure, while the SA and MA processes produced a fine bainitic  microstructure, enhancing mechanical properties (tensile strength and impact  strength) with good elasticity. The research results indicated that the SA1 sample  exhibited the best toughness with a value of 41 Joules, while the MA sample had a  value of 32.67 Joules. The highest hardness value was observed in the SA2  specimen with a hardness of 43.67 HRC, whereas the MA test piece had a hardness  of 43.00 HRC. The SA1 specimen exhibited the highest maximum load-bearing  capacity before failure with a value of 922.36 MPa tensile strength and 13.09%  elongation. On the other hand, the MA specimen had the highest ability to  withstand maximum loads without undergoing permanent plastic deformation, with  a Yield Strength of 579.32 MPa.  In the future, the findings of this research can offer an alternative solution to the  issue of abundant availability of AISI 4140 steel raw materials, providing costeffectiveness  and improved  toughness.        Keywords:  AISI  4140, Hardness,  Microstructure,  Annealing,  Single  Austempering          
date: 2023-08-01
type: Tesis
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/75102/1/ABSTRAK.pdf
format: text
identifier: http://digilib.unila.ac.id/75102/2/TESIS%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/75102/3/TESIS%20FULL%20TANPA%20PEMBAHASAN.pdf
identifier:   PURNOMO, PURNOMO  (2023) PENGARUH PERLAKUAN PANAS MULTI AUSTEMPERING TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO BAJA AISI 4140.  Masters thesis, UNIVERSITAS LAMPUNG.   
relation: http://digilib.unila.ac.id/75102/