title: PEMBENTUKAN FASE BAHAN SUPERKONDUKTOR Bi-2223 DENGAN  DOPING Pb (BPSCCO-2223) PADA KADAR Ca = 2,10 DENGAN VARIASI  SUHU SINTERING (PHASE FORMATION OF BSCCO-2223 SUPERCONDUCTING  MATERIALS WITH Pb DOPING (BPSCCO-2223) ON THE LEVEL OF Ca  = 2,10 WITH VARIATION OF SINTERING TEMPERATURE)
creator: Sumardi, Febri Reviana
subject: Q Science (General)
subject: QP Physiology
description: Sintesis superkonduktor BSCCO-2223 dengan doping Pb (BPSCCO-2223) pada  kadar Ca = 2,10 telah dilakukan dengan metode padatan. Sintesis dilakukan  selama 10 jam pada suhu kalsinasi 800oC dan selama 20 jam pada suhu sintering  yang bervariasi yaitu 840oC, 845oC, 850oC, dan 855oC. Variasi dilakukan untuk  mengetahui pengaruh suhu sintering terhadap pembentukan fase bahan  superkonduktor yang dilihat berdasarkan fraksi volume, impuritas, dan derajat  orientasi. Hasil penelitian menunjukkan bahwa peningkatan suhu sintering dapat  meningkatkan fraksi volume dan menurunkan impuritas. Fraksi volume  BPSCCO-2223 yang relatif tinggi adalah 86,80% pada suhu sintering 855oC.  Sedangkan fraksi volume terendah adalah 76,88% pada suhu sintering 840oC.  Derajat orientasi tertinggi adalah 47,87% pada suhu 850oC. Sedangkan derajat  orientasi terendah adalah 37,28% pada suhu 845oC. Berdasarkan hasil SEM  diinformasikan bahwa semua sampel telah menunjukkan lapisan-lapisan yang  tersusun searah (terorientasi) dengan ruang kosong antara lempengan (void) relatif  kecil.  Kata kunci : superkonduktor BPSCCO-2223, sintering, fraksi volume,impuritas, derajat orientasi.    (The synthesis of BSCCO-2223 superconducting materials with Pb doping  (BPSCCO-2223) has been administered with solid reaction. The synthesis was  performed for 10 hours by calcination at temperature of 800oC and for 20 hours  to varied at the temperature 840oC, 845oC, 850oC, and 855oC. This variation was  performed to determine the effect of sintering temperature on phase formation of  superconductor being viewed based on volume fraction, impurities, and the degree  of orientation. Result of the research show the increase of sintering temperature  could increase the volume fraction and decrease impurity. Volume fraction of  BPSCCO-2223 that is relatively high is 86,80% on the sintering temperature of  855oC. The lowest volume fraction is 76,88% on the sintering temperature of  840oC. The highest degree of orientation is 47,87% on sintering temperature  850oC. The lowest degree of orientation is 37,28% on sintering temperature  845oC. Result of SEM show that all the samples have shown that layers arranged  in the direction of the empty space between the plates (void) is relatively small.  Keywords: superconductor BPSCCO-2223, sintering, volume fraction, impurity,  degree of orientation.)  
publisher: Fakultas MIPA
date: 2013-12-23
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/76/1/COVER%20DALAM.pdf
format: text
identifier: http://digilib.unila.ac.id/76/2/ABSTRAK.pdf
format: text
identifier: http://digilib.unila.ac.id/76/3/ABSTRACT.pdf
format: text
identifier: http://digilib.unila.ac.id/76/4/MENYETUJUI.pdf
format: text
identifier: http://digilib.unila.ac.id/76/5/PERNYATAAN.pdf
format: text
identifier: http://digilib.unila.ac.id/76/6/DAFTAR%20ISI.pdf
format: text
identifier: http://digilib.unila.ac.id/76/7/BAB%201.pdf
format: text
identifier: http://digilib.unila.ac.id/76/8/BAB%20II.pdf
format: text
identifier: http://digilib.unila.ac.id/76/9/BAB%20III.pdf
format: text
identifier: http://digilib.unila.ac.id/76/10/BAB%20IV.pdf
format: text
identifier: http://digilib.unila.ac.id/76/11/BAB%20V.pdf
format: text
identifier: http://digilib.unila.ac.id/76/12/DAFTAR%20PUSTAKA.pdf
format: archive
identifier: http://digilib.unila.ac.id/76/13/LAMPIRAN.zip
identifier:   Sumardi, Febri Reviana  (2013) PEMBENTUKAN FASE BAHAN SUPERKONDUKTOR Bi-2223 DENGAN DOPING Pb (BPSCCO-2223) PADA KADAR Ca = 2,10 DENGAN VARIASI SUHU SINTERING (PHASE FORMATION OF BSCCO-2223 SUPERCONDUCTING MATERIALS WITH Pb DOPING (BPSCCO-2223) ON THE LEVEL OF Ca = 2,10 WITH VARIATION OF SINTERING TEMPERATURE).  Fakultas MIPA, Universitas Lampung.     
relation: http://digilib.unila.ac.id/76/