Telah dilakukan penelitian sebagai upaya peningkatan nilai tambah limbah padat
industri menjadi produk cellular glass ceramic berupa batu basalt dan slag boiler.
Penelitian ini menggunakan variasi komposisi basalt:slag boiler sebesar 90:10%,
80:20%, 70:30%, 60:40%, dan 50:50%. Kemudian variasi poliuretan yang
digunakan sebesar 30%,40%, dan 50% sebagai foaming agent dengan pemanasan
sampai suhu 950°C dengan penahanan pada suhu 400°C dan 700°C selama 2 jam
dengan pendinginan di dalam tungku. Berdasarkan hasil karakterisasi dan uji
mekanis serta fisis pada sampel didapatkan hasil yang cukup baik. Pada sampel
didominasi SiO2, Fe2O3, CaO dan Al2O3 yang cukup tinggi dengan fase kristal yang cukup
banyak terbentuk yakni quartz dan augite, yang memiliki ukuran pori sebesar ukuran ?
1 mm sekitar 85% dan > 1 mm sekitar 15%. Nilai kuat tekan densitas, dan porositas
terbaik berturut- turut sebesar 8,68 MPa; 1,14 g/cm3; dan 13,55%.
Kata Kunci: cellular glass ceramic, basalt, slag boiler, foaming agent, poliuretan
Research has been carried out as an effort to increase the added value of industrial solid waste into cellular glass ceramic products in the form of basalt stone and boiler slag. This research uses variations in basalt:slag boiler composition of 90:10%, 80:20%, 70:30%, 60:40%, and 50:50%. Then the polyurethane variations used were 30%, 40%, and 50% as a foaming agent by heating to a temperature of 950°C with holding at a temperature of 400°C and 700°C for 2 hours with cooling in a furnace. Based on the results of characterization and mechanical and physical tests on the samples, quite good results were obtained. The samples are dominated by SiO2, Fe2O3, CaO and Al2O3 which are quite high with quite a lot of crystal phases formed, namely quartz and augite, which have pore sizes of ?1 mm, around 85% and >1 mm, around 15%. The best compressive strength, density and porosity values respectively were 8.68 MPa; 1.14 g/cm3; and 13.55%.
Keywords: cellular glass ceramic, basalt, boiler slag, foaming agent, polyurethane
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - PENGARUH VARIASI KOMPOSISI DAN POLIURETAN TERHADAP
PEMBENTUKAN CELLULAR GLASS CERAMIC BERBASIS BASALT
DAN SLAG BOILER MELALUI METODE DIRECT FOAMING