<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC)"^^ . "ABSTRACT\r\n\r\nSelf Compacting Concrete (SCC) is an innovative concrete that can compact itself \r\n(without a vibrator) and is able to flow under its own weight to saturate the formwork \r\nwithout experiencing segregation. This can overcome problems in terms of \r\nproductivity, quality and work safety. Concrete is a composite building material that is \r\nstrong in withstanding compressive forces, but weak against tensile forces, is also \r\nbrittle and easily cracks. Steel fibers are added to the concrete mixture to improve the \r\ncharacteristics of the concrete. In this study, 3D Dramix steel fibers were used in SCC \r\nwith a volume fraction of 1% at each length variation of 20 mm, 40 mm and 60 mm. \r\nThe samples used in the split compressive and tensile strength test specimens were \r\ncylindrical with a diameter of 150 mm and a height of 300 mm. Meanwhile, the flexural \r\ntensile strength test is a beam sample measuring 100x100x400 mm. Sample testing was \r\ncarried out at 28 days of age. The highest increase in compressive strength values \r\noccurred at a length variation of 40 mm, amounting to 5.99% of normal concrete. The \r\nhighest increase in splitting tensile strength values occurred at the 60 mm length \r\nvariation of 36.44% and the highest increase in bending tensile strength values \r\noccurred at the 60 mm length variation of 531.7%. The research results show that \r\nvariations in steel fiber length in SCC can affect compressive strength, tensile strength, \r\nand also reduce the workability or ease of casting concrete.\r\nKey words : steel fibre, compressive strength, split tensile strength, flexural tensile \r\nstrength\r\n\r\nABSTRAK\r\n\r\nSelf Compacting Concrete (SCC) merupakan beton inovatif yang dapat memadat \r\nsendiri (tanpa vibrator) dan mampu mengalir dengan beratnya sendiri untuk mengisi \r\nbekisting dengan jenuh tanpa mengalami segregasi. Hal ini dapat mengatasi masalah \r\ndalam hal produktivitas, kualitas, dan juga keselamatan kerja. Beton adalah bahan \r\nbangunan komposit yang kuat dalam menahan gaya tekan, tetapi lemah terhadap gaya \r\ntarik, juga getas dan mudah retak. Serat baja ditambahkan dalam campuran beton untuk \r\nmemperbaiki karakteristik beton tersebut. Pada penelitian ini menggunakan serat baja \r\nDramix 3D pada SCC dengan volume fraksi 1% pada setiap variasi panjang 20 mm, \r\n40 mm, dan 60 mm. Sampel yang digunakan pada benda uji kuat tekan dan tarik belah \r\nberupa silinder dengan diameter 150 mm dan tinggi 300 mm. Sedangkan uji kuat tarik \r\nlentur berupa sampel balok dengan ukuran 100x100x400 mm. Pengujian sampel \r\ndilakukan pada umur 28 hari. Peningkatan nilai kuat tekan tertinggi terjadi pada variasi \r\npanjang 40 mm sebesar 5,99% dari beton normal. Peningkatan nilai kuat tarik belah \r\ntertinggi terjadi pada variasi panjang 60 mm sebesar 36,44% dan peningkatan nilai kuat \r\ntarik lentur tertinggi terjadi pada variasi panjang 60 mm sebesar 531,7%. Hasil \r\npenelitian menunjukkan bahwa variasi panjang serat baja pada SCC dapat \r\nmempengaruhi kuat tekan, kuat tarik, dan juga mengurangi workability atau \r\nkemudahan pengecoran beton.\r\nKata kunci : serat baja, kuat tekan, kuat tarik belah, kuat tarik lentur\r\n"^^ . "2023-10-26" . . . . . "FAKULTAS TEKNIK"^^ . . . . . . . "NAPATINO RAMADHAN"^^ . "VERNADY"^^ . "NAPATINO RAMADHAN VERNADY"^^ . . "UNIVERSITAS LAMPUNG"^^ . . . . . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (File PDF)"^^ . . . "Abstrak.pdf"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (File PDF)"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (File PDF)"^^ . . . "Skripsi Tanpa Bab 4.pdf"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "preview.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "medium.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "small.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "preview.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "medium.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "small.jpg"^^ . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . . "ANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \r\nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \r\nCONCRETE (SCC) (Other)"^^ . . . . . "HTML Summary of #76890 \n\nANALISIS PERBANDINGAN PENGARUH VARIASI UKURAN PANJANG \nSERAT BAJA DRAMIX 3D TERHADAP BETON SELF COMPACTING \nCONCRETE (SCC)\n\n" . "text/html" . . . "620 Ilmu teknik dan ilmu yang berkaitan" . . . "690 Pembangunan gedung" . .