The repository administrator has not yet configured an RDF license.
PENGARUH VARIASI TEMPERING TERHADAP STRUKTUR MIKRO DAN SIFAT TANGGUH BAJA K-460 (EFFECT OF TEMPERING VARIATION TO MICROSTRUCTURE AND TOUGHNESS OF STEEL K-460)
Telah dilakukan penelitian mengenai “Pengaruh Variasi Tempering terhadap Struktur mikro dan Sifat Tangguh Baja K-460”. Pengujian mikro menggunakan alat mikroskop optik, dan pengujian ketangguhan baja dilakukan dengan menggunakan alat uji impak charpy dengan menggunakan variasi tempering yaitu 450 ºC dan 550 ºC. Hasil pengujian mikro untuk sampel yang tidak mengalami perlakuan panas, terdapat fasa ferrit dan sementit. Sedangkan pada baja yang mengalami perlakuan panas untuk quenching dan tempering, baja yang diquenching menunjukan fasa martensit yang berbentuk jarum dimana pada fasa ini terjadi karena adanya proses pendinginan secara cepat yang membuat atom-atom bergerak dan tidak sempat berdifusi. untuk mikro yang mengalami proses tempering memperlihatkan struktur karbida speroidit, dimana ketika berada pada temperatur yang tinggi atau pemanasan sampai disekitar temperatur kritis A1 yaitu 723 ºC, dan dalam waktu yang lama maka sementit yang tadinya berbentuk plat atau lempengan itu akan hancur menjadi bola-bola kecil (sphere). Pada hasil uji impak memperlihatkan bahwa hasil terbaik didapatkan pada hasil tempering 550 ºC yaitu dengan nilai ketangguhan 0,08 J/mm2, dan hasil ketanguhan terendah terdapat pada baja yang mengalami quenching yaitu dengan nilai ketangguhan 0,04 j/mm2. Kata kunci: baja karbon tinggi, pengujian impak, martensit temper, quenching. (The research has been carried out about “Effect of Tempering Variation To Microstructure and Toughness Steel Of K-460”. Micro testing used optic microscopy and toughness testing used charpy impact testing with variation of tempering were 450 and 550 oC. The results of micro testing for sample without heating treatment including ferrit and cementite phase. The sample result occured by heating treatment of quenching revealed martensite phase which has needle shaped, this phase occurred because of rapid cooling process that makes the atoms move and no diffuse. Whereas the result of sample occured by heating treatment of tempering shown the structure of speroidit carbide, when it is located at a high temperature or warming up around the critical temperature A1 is 723 º C, and for a long time so cementite that had plate shaped will crumble into small balls (sphere). The impact testing results showed the best result obtained at 550 oC tempering with toughness value of 0.08 J/mm2 and the lowest value of toughness obtained at steel is quenched with toughness value of 0.04 j/mm2. Keywords: high carbon steel, tempered martensite, quenching.)
PENGARUH VARIASI TEMPERING TERHADAP STRUKTUR MIKRO DAN SIFAT TANGGUH BAJA K-460 (EFFECT OF TEMPERING VARIATION TO MICROSTRUCTURE AND TOUGHNESS OF STEEL K-460) (File PDF)
PENGARUH VARIASI TEMPERING TERHADAP STRUKTUR MIKRO DAN SIFAT TANGGUH BAJA K-460 (EFFECT OF TEMPERING VARIATION TO MICROSTRUCTURE AND TOUGHNESS OF STEEL K-460) (Archive)
PENGARUH VARIASI TEMPERING TERHADAP STRUKTUR MIKRO DAN SIFAT TANGGUH BAJA K-460 (EFFECT OF TEMPERING VARIATION TO MICROSTRUCTURE AND TOUGHNESS OF STEEL K-460) (Other)
HTML Summary of #78 PENGARUH VARIASI TEMPERING TERHADAP STRUKTUR MIKRO DAN SIFAT TANGGUH BAJA K-460 (EFFECT OF TEMPERING VARIATION TO MICROSTRUCTURE AND TOUGHNESS OF STEEL K-460)
Q Science (General)
QP Physiology