?url_ver=Z39.88-2004&rft_id=1917011009&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=SINTESIS+DAN+KARAKTERISASI+ZSM-5+DAN+MOR+PORI+HIRARKI%0D%0ASEBAGAI+KATALIS+PADA+REAKSI+HIDROLISIS+SELULOSA&rft.creator=Shilvia+%2C+Putri+&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=540+Kimia+dan+ilmu+yang+berhubungan&rft.description=Pada+penelitian+ini+telah+dilakukan+sintesis+ZSM-5+dan+MOR+pori+hirarki+dari%0D%0Asilika+LUDOX+dengan+memanfaatkan+pati+dari+tepung+tapioka+sebagai%0D%0Abiomesoporogen+dan+benih+ZSM-5+sebagai+pembentuk+kerangka+ZSM-5.%0D%0ARangkaian+tahap+penelitian+yang+dilakukan+yaitu%2C+sintesis+ZSM-5+dan+MOR+pori%0D%0Ahirarki+dengan+dan+tanpa+biomesoporogen%2C+pertukaran+ion+menjadi+H-ZSM-5+dan%0D%0AH-MOR+pori+hirarki+serta+uji+aktivitas+katalitik+pada+reaksi+hidrolisis.%0D%0AKarakterisasi+ZSM-5+dan+MOR+dengan+dan+tanpa+biomesoporogen+menggunakan%0D%0AXRD+dan+BET.+Karakterisasi+XRD+menunjukkan+fasa+kristalin+dengan%0D%0Akristalinitas+pada+ZSM-5+dengan+dan+tanpa+biomesoporogen+masing-masing%0D%0Asebesar+59%2C25+dan+65%2C16%25%2C+sedangkan+pada+MOR+masing-masing+sebesar+64%2C2%0D%0Adan+68%2C4%25.+ZSM-5+dan+MOR+pori+hirarki+memiliki+distribusi+ukuran+pori%0D%0Amasing-masing+sebesar+3%2C6+dan+2%2C14+nm.+Hasil+uji+katalitik+menunjukkan+kondisi%0D%0Areaksi+optimum+berada+pada+suhu+140%CB%9AC+selama+3+jam+dengan+rasio%0D%0Akatalis%2Fsubstrat+0%2C03%3A0%2C05+menggunakan+katalis+H-ZSM-5+dan+H-MOR.+Konversi%0D%0Ahidrolisis+selulosa+tertinggi+diperoleh+menggunakan+katalis+H-ZSM-5+dan+H-MOR%0D%0Apori+hirarki+yaitu+sebesar+62%2C2+dan+48%2C8%25.%0D%0AKata+Kunci+%3A+Silika+LUDOX%2C+biomesoporogen%2C+ion+exchange%2C+hidrolisis%0D%0A%0D%0AIn+this+research%2C+the+synthesis+of+ZSM-5+and+hierarchical+pore+MOR+from%0D%0ALUDOX+silica+has+been+carried+out+utilizing+starch+from+tapioca+flour+as+a%0D%0Abiomesoporogen+and+ZSM-5+seeds+as+the+ZSM-5+framework.+The+steps+of+the%0D%0Aresearch+were+carried+out+by+synthesis+of+ZSM-5+and+hierarchical+pore+MOR+with%0D%0Aand+without+biomesoporogen%2C+ion+exchange+to+become+H-ZSM-5+and+hierarchical%0D%0Apore+H-MOR+and+catalytic+activity+tests+in+the+hydrolysis+reaction.%0D%0ACharacterization+of+ZSM-5+and+MOR+with+and+without+biomesoporogens+using%0D%0AXRD+and+BET.+XRD+characterization+showed+a+crystalline+phase+with%0D%0Acrystallinity+in+ZSM-5+with+and+without+biomesoporogen+of+59.25+and+65.16%25%0D%0Arespectively%2C+while+in+MOR+it+was+64.2+and+68.4%25+respectively.+ZSM-5+and%0D%0Ahierarchical+pore+MOR+have+pore+size+distributions+of+3.6+and+2.14+nm%2C%0D%0Arespectively.+The+catalytic+test+results+show+that+the+optimum+reaction+conditions%0D%0Aare+at+a+temperature+of+140%CB%9AC+for+3+hours+with+a+catalyst%2Fsubstrate+ratio+of%0D%0A0.03%3A0.05+using+H-ZSM-5+and+H-MOR+catalysts.+The+highest+cellulose+hydrolysis%0D%0Aconversion+was+obtained+using+the+H-ZSM-5+and+H-MOR+hierarchical+pore%0D%0Acatalysts%2C+namely+62.2+and+48.8%25.%0D%0AKeywords+%3A+Silica+LUDOX%2C+biomesoporogen%2C+ion+exchange%2C+hydrolysis&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM&rft.date=2023-12-04&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F78125%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F78125%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F78125%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++Shilvia+%2C+Putri+++(2023)+SINTESIS+DAN+KARAKTERISASI+ZSM-5+DAN+MOR+PORI+HIRARKI+SEBAGAI+KATALIS+PADA+REAKSI+HIDROLISIS+SELULOSA.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F78125%2F