%T SINTESIS ZEOLIT MOR DAN ZSM-5 PORI HIRARKI MENGGUNAKAN  BIO-MESOPOROGEN PATI JAGUNG DAN UJI KATALITIKNYA PADA  REAKSI HIDROLISIS SELULOSA KULIT SINGKONG
%U http://digilib.unila.ac.id/78127/
%X Pada penelitian ini dilakukan sintesis, karakterisasi dan uji aktivitas katalitik zeolit  ZSM-5 dan mordenit (MOR) pori hirarki berbasis silika LUDOX pada reaksi  hidrolisis selulosa kulit singkong. Rangkaian penelitian yang dilakukan ialah  sintesis ZSM-5 (seed assisted) dan MOR pori hirarki menggunakan pati dari tepung  jagung sebagai bio-mesoporogen, serta tanpa penambahan bio-mesoporogen  sebagai pembanding. Sintesis zeolit dilakukan secara hidrotermal pada suhu 180oC  selama 144 jam. Zeolit diubah menjadi H-ZSM-5 dan H-MOR melalui pertukaran  ion untuk meningkatkan situs asam. Karakterisasi dengan XRD menunjukkan  bahwa ZSM-5 dan MOR berhasil disintesis karena memiliki kecocokan dengan  difraktogram standar. ZSM-5 dan MOR pori hirarki memiliki luas permukaan  masing-masing sebesar 270,39 dan 420,80 m2/g serta diameter pori sebesar 2,48  dan 3,09 nm. Hasil uji katalitik kedua zeolit menunjukkan kondisi optimum pada  suhu 140oC selama 3 jam dengan rasio selulosa/katalis 0,05:0,03. Tingkat konversi  hidrolisis selulosa tertinggi diperoleh pada H-MOR pori hirarki sebesar 62%  sedangkan H-ZSM-5 pori hirarki diperoleh sebesar 59,8%.  Kata Kunci : Silika LUDOX, bio-mesoporogen, H-ZSM-5, H-MOR, hidrolisis    In this research the synthesis, characterization, and catalytic activity testing of  ZSM-5 and mordenite (MOR) zeolites with hierarchical silica-based LUDOX pores  were conducted in the hydrolysis reaction of cassava peel cellulose. The research  series included the synthesis of ZSM-5 (seed-assisted) and MOR with hierarchy  pore using corn starch as a bio-mesoporogen, and without the addition of biomesoporogen  as a comparison. The zeolite synthesis was carried out  hydrothermally at 180°C for 144 hours. Zeolites were transformed into H-ZSM-5  and H-MOR through ion exchange to enhance acidic sites. Characterization by  XRD indicated that ZSM-5 and MOR were successfully synthesized because it has  a conformity with the standard diffractogram. ZSM-5 and MOR hierarchy pore had  surface areas of 270,39 and 420,80 m²/g, respectively, and pore diameters of 2,48  and 3,09 nm. Catalytic test results for both zeolites showed optimum conditions at  140°C for 3 hours with a cellulose/catalyst ratio of 0,05:0,03. The highest cellulose  hydrolysis conversion rate was achieved with H-MOR hierarchy pore at 62%, while  H-ZSM-5 hierarchy pore obtained a conversion rate of 59,8%.  Keywords : Silica LUDOX, bio-mesoporogen, H-ZSM-5, H-MOR, hydrolysis