title: SINTESIS ZEOLIT MOR DAN ZSM-5 PORI HIRARKI MENGGUNAKAN
BIO-MESOPOROGEN PATI JAGUNG DAN UJI KATALITIKNYA PADA
REAKSI HIDROLISIS SELULOSA KULIT SINGKONG
ispublished: pub
subjects: 500
subjects: 540
full_text_status: restricted
abstract: Pada penelitian ini dilakukan sintesis, karakterisasi dan uji aktivitas katalitik zeolit
ZSM-5 dan mordenit (MOR) pori hirarki berbasis silika LUDOX pada reaksi
hidrolisis selulosa kulit singkong. Rangkaian penelitian yang dilakukan ialah
sintesis ZSM-5 (seed assisted) dan MOR pori hirarki menggunakan pati dari tepung
jagung sebagai bio-mesoporogen, serta tanpa penambahan bio-mesoporogen
sebagai pembanding. Sintesis zeolit dilakukan secara hidrotermal pada suhu 180oC
selama 144 jam. Zeolit diubah menjadi H-ZSM-5 dan H-MOR melalui pertukaran
ion untuk meningkatkan situs asam. Karakterisasi dengan XRD menunjukkan
bahwa ZSM-5 dan MOR berhasil disintesis karena memiliki kecocokan dengan
difraktogram standar. ZSM-5 dan MOR pori hirarki memiliki luas permukaan
masing-masing sebesar 270,39 dan 420,80 m2/g serta diameter pori sebesar 2,48
dan 3,09 nm. Hasil uji katalitik kedua zeolit menunjukkan kondisi optimum pada
suhu 140oC selama 3 jam dengan rasio selulosa/katalis 0,05:0,03. Tingkat konversi
hidrolisis selulosa tertinggi diperoleh pada H-MOR pori hirarki sebesar 62%
sedangkan H-ZSM-5 pori hirarki diperoleh sebesar 59,8%.
Kata Kunci : Silika LUDOX, bio-mesoporogen, H-ZSM-5, H-MOR, hidrolisis

In this research the synthesis, characterization, and catalytic activity testing of
ZSM-5 and mordenite (MOR) zeolites with hierarchical silica-based LUDOX pores
were conducted in the hydrolysis reaction of cassava peel cellulose. The research
series included the synthesis of ZSM-5 (seed-assisted) and MOR with hierarchy
pore using corn starch as a bio-mesoporogen, and without the addition of biomesoporogen
as a comparison. The zeolite synthesis was carried out
hydrothermally at 180°C for 144 hours. Zeolites were transformed into H-ZSM-5
and H-MOR through ion exchange to enhance acidic sites. Characterization by
XRD indicated that ZSM-5 and MOR were successfully synthesized because it has
a conformity with the standard diffractogram. ZSM-5 and MOR hierarchy pore had
surface areas of 270,39 and 420,80 m²/g, respectively, and pore diameters of 2,48
and 3,09 nm. Catalytic test results for both zeolites showed optimum conditions at
140°C for 3 hours with a cellulose/catalyst ratio of 0,05:0,03. The highest cellulose
hydrolysis conversion rate was achieved with H-MOR hierarchy pore at 62%, while
H-ZSM-5 hierarchy pore obtained a conversion rate of 59,8%.
Keywords : Silica LUDOX, bio-mesoporogen, H-ZSM-5, H-MOR, hydrolysis
date: 2023-12-01
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
place_of_pub: UNIVERSITAS LAMPUNG
id_number: 1917011011
citation:   Yesica , Sitorus  (2023) SINTESIS ZEOLIT MOR DAN ZSM-5 PORI HIRARKI MENGGUNAKAN BIO-MESOPOROGEN PATI JAGUNG DAN UJI KATALITIKNYA PADA REAKSI HIDROLISIS SELULOSA KULIT SINGKONG.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/78127/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/78127/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/78127/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf