%A PATRAINI  CHYNTIA GUSTIYANDA 
%T PEMANFAATAN EKSTRAK SABUT SAWIT, ASAP CAIR CANGKANG SAWIT, DAN CAMPURANNYA SEBAGAI INHIBITOR PEMBENTUKAN KERAK KALSIUM KARBONAT (CaCO3) 
%X Industri  minyak  dan  gas  memerlukan  inhibitor  kerak  untuk  mengatasi  masalah operasional dan ekonomi yang disebabkan oleh pembentukan kerak.  Oleh karena itu, pada  penelitian  ini  digunakan  ekstrak  sabut  sawit,  asap  cair  cangkang  sawit,  serta campuran ekstrak sabut sawit dan asap cair cangkang sawit dan dibandingkan dengan asam EDTA sebagai inhibitor pertumbuhan kerak CaCO3.Pada penelitian ini digunakan ekstrak sabut sawit, asap cair cangkang sawit, serta campuran ekstrak sabut sawit dan asap cair cangkang sawit dan dibandingkan dengan asam EDTA pada masing-masing larutan 5, 15, 25, 35 dan 45% dengan  variasi  konsentrasi larutan pertumbuhan 0,05; 0,075  dan  0,10  M  pada  suhu  90oC  menggunakan  metode  seeded  experiment  dan unseeded experiment. Hasil penelitian menunjukkan bahwa nilai persentase efektivitas optimum  dari  masing-masing  sampel  diperoleh  pada  konsentrasi  inhibitor  25%  dan konsentrasi  larutan  pertumbuhan  0,05  M  menggunakan  metode  seeded  experiment. Efektivitas inhibitor ekstrak sabut sawit mencapai  65,24%, asap cair cangkang sawit sebesar 63,11%, campuran ekstrak sabut sawit dengan asap cair cangkang sawit sebesar 63,19%, dan asam EDTA sebesar 97,77%. Penelitian ini menunjukkan bahwa seluruh sampel dapat berfungsi sebagai inhibitor yang efektif dalam mengontrol pembentukan kerak  CaCO3.  Hasil  analisis  PSA  menunjukkan  bahwa  penambahan  inhibitor menghasilkan  ukuran  partikel  yang  lebih  seragam  dan  kristal  yang  lebih  kecil. Pengamatan  SEM  mengungkapkan  perubahan  morfologi  kristal  menjadi  lebih  halus dan tidak teratur. Selain itu, analisis XRD mengonfirmasi perubahan fase dari kalsit menjadi  aragonit  dan  vaterit  yang  lebih  lunak  dan  mudah  dibersihkan.  Secara keseluruhan, seluruh inhibitor terbukti mampu mengganggu kristalisasi normal kalsit dan menawarkan solusi alternatif untuk mencegah pembentukan kerak dalam aplikasi industri. 
Kata Kunci : CaCO3, inhibitor kerak, ekstrak sabut sawit, asap cair cangkang sawit. 

The oil and gas industry requires scale inhibitors to address operational and economic issues caused by scale formation. Therefore, this study utilizes palm fiber extract, palm shell  liquid  smoke,  as  well  as  a  mixture of  palm  fiber  extract  and  palm  shell  liquid smoke and compares them with EDTA acid as inhibitors of CaCO3 scale growth. In this  study,  palm  fiber  extract,  palm  shell  liquid  smoke,  and  their  mixture  were compared with EDTA acid at concentrations of 5%, 15%, 25%, 35%, and 45%, with growth solution concentrations of 0.05 M, 0.075 M, and 0.10 M at a temperature of 90?C using both the seeded experiment and unseeded experiment methods. The results showed that the optimum percentage effectiveness for each sample was achieved at an inhibitor concentration of 25% and a growth solution concentration of 0.05 M using the seeded experiment method. The effectiveness of the inhibitors was 65.24% for palm fiber extract, 63.11% for palm shell liquid smoke, 63.19% for the mixture of palm fiber extract and palm shell liquid smoke, and 97.77% for EDTA. This study demonstrates that  all  samples  can  function  effectively  as  inhibitors  in  controlling  CaCO3  scale formation.  PSA  analysis  revealed  that  adding  inhibitors  resulted  in  more  uniform particle  sizes  and  smaller  crystals.  SEM  observations  indicated  changes  in  crystal morphology  to  smoother  and  more  irregular  forms.  Furthermore,  XRD  analysis confirmed phase transitions from calcite to softer and more easily removable aragonite and  vaterite.  Overall,  all  inhibitors  proved  capable  of  disrupting  normal  calcite crystallization  and  offer  alternative  solutions  for  preventing  scale  formation  in industrial applications. 
Keywords: CaCO3, scale inhibitor, palm fiber extract, palm shell liquid smoke. 
%D 2024
%I UNIVERSITAS LAMPUNG 
%L eprints80754