%T ANALISIS MIKROSTRUKTUR BETON YANG DIBUAT DENGAN  CAMPURAN BAHAN MENGANDUNG GARAM  
%U http://digilib.unila.ac.id/81549/
%X Penelitian ini menganalisis mikrostruktur beton K350 yang dibuat dengan  campuran bahan mengandung garam menggunakan metode SEM-EDX. Beton diuji  dalam enam variabel: curing air tawar (NCT), curing air laut (NCL), campuran air  laut (ALCT), pasir pantai (PPCT), dan serbuk kerang (KALCT, KCT). Hasil  pengujian menunjukkan variasi kuat tekan dan mikrostruktur yang signifikan  berdasarkan komposisi material dan metode curing. SEM-EDX mengidentifikasi  senyawa seperti ettringite, trikalsium silikat, dan garam Friedel. Penggunaan air laut  sebagai curing beton meningkatkan kadar ettringite dan tobermorite C-S-H, yang  berkontribusi pada penurunan kuat tekan. Analisis juga menunjukkan bahwa  campuran pasir pantai dan serbuk kerang memiliki efek berbeda terhadap kekuatan  beton, dengan serbuk kerang menunjukkan peningkatan kekuatan tanpa efek negatif  dari air laut. Studi ini memberikan pemahaman mendalam tentang pengaruh  komposisi kimia dan mikrostruktur terhadap karakteristik mekanik beton.  Kata kunci: mikrostruktur beton, SEM-EDX, air laut, pasir pantai, serbuk kerang.    ABSTRACT    MICROSTRUCTURAL ANALYSIS OF CONCRETE MADE WITH SALT-  CONTAINING MATERIALS    By:    MOCHAMMAD DANY FAUZAN    This study analyzes the microstructure of K350 concrete made with salt-containing  materials using the SEM-EDX method. The concrete was tested in six variables:  fresh water curing (NCT), seawater curing (NCL), seawater mix (ALCT), beach  sand (PPCT), and shell powder (KALCT, KCT). The test results showed significant  variations in compressive strength and microstructure based on the material  composition and curing method. SEM-EDX identified compounds such as  ettringite, tricalcium silicate, and Friedel's salt. The use of seawater for curing  concrete increased the levels of ettringite and tobermorite C-S-H, contributing to a  decrease in compressive strength. The analysis also showed that beach sand and  shell powder mixtures had different effects on concrete strength, with shell powder  showing increased strength without the negative effects of seawater. This study  provides a deeper understanding of the influence of chemical composition and  microstructure on the mechanical characteristics of concrete.  Keywords: concrete microstructure, SEM-EDX, seawater, beach sand, shell  powder.