@misc{eprints82343,
           month = {Agustus},
           title = {ANALISIS PERAMBATAN RETAK FATIK MAGNESIUM AZ31B},
          author = { UMAR FAJRI ALDITA},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS TEKNIK},
            year = {2024},
             url = {http://digilib.unila.ac.id/82343/},
        abstract = {Magnesium AZ31B dipilih karena merupakan material yang banyak digunakan
dalam industri otomotif dan biomaterial karena sifat mekaniknya yang unggul
seperti ringan, rasio kekuatan terhadap berat yang tinggi, dan kekakuan spesifik
yang tinggi. Tujuan dari penelitian ini adalah untuk mengetahui karakteristik
perambatan retak lelah material Magnesium AZ31B. Uji tarik (ASTM 8) dan uji
perambatan retak lelah (ASTM E647) menggunakan benda uji Compact Tension
(CT). Parameter yang digunakan pada pengujian adalah Pmax = 1 kN, Pmin = 0,1
kN, R=0,1, {\ensuremath{\sigma}}yield = 188.407 MPa dan f = 10 Hz. Pengukuran panjang retak
menggunakan metode kepatuhan dan data panjang retak serta jumlah siklus
dianalisis menggunakan metode polinomial inkremental untuk mengetahui laju
perambatan retak lelah (da/dN) dan faktor intensitas tegangan ({\ensuremath{\Delta}}K). Plot data
da/dN vs {\ensuremath{\Delta}}K dilakukan untuk menentukan koefisien persamaan Paris pada daerah
perambatan retakan tahap II yang stabil. Nilai konstanta m = 3,067 dan nilai
konstanta C = 3,747x10-10. Pengamatan SEM pada permukaan rekahan
menunjukkan pola rekahan intergranular. Selain itu, permukaan rekahan
menunjukkan lurik, retakan sekunder, belahan dan rongga.

Kata Kunci : Magnesium AZ31B, Perambatan retak fatik, Fraktografi.


Magnesium AZ31B was chosen because it is a material widely used in the
automotive and biomaterial industries due to its superior mechanical properties
such as light weight, high strength-to-weight ratio, and high specific stiffness. The
purpose of this study is to determine the fatigue crack propagation characteristics
of AZ31B Magnesium material. The tensile test (ASTM 8) and fatigue crack
propagation test (ASTM E647) used Compact Tension (CT) specimens. The
parameters used during the test were Pmax = 1 kN, Pmin = 0,1 kN, R=0,1, {\ensuremath{\sigma}}yield
= 188.407 MPa and f = 10 Hz. Crack length measurements using the compliance
method and data on crack length and number of cycles were analyzed using the
incremental polynomial method to determine the fatigue crack propagation rate
(da/dN) and stress intensity factor ({\ensuremath{\Delta}}K). A plot of da/dN vs {\ensuremath{\Delta}}K data was
performed to determine the coefficients of the Paris equation in the stable-stage
II crack propagation region. The constant value m = 3,067 and the constant value
C = 3,747x10-10. SEM observation of the fracture surface showed an
intergranular fracture pattern. In addition, the fracture surface showed striations,
secondary cracks, cleavage and voids.

Keywords : Magnesium AZ31B, Fatigue crack propagation, Fractografi.
}
}