@misc{eprints82544,
           month = {Februari},
           title = {PENGGUNAAN BENTONIT YANG DIAKTIVASI SECARA FISIK
MENGGUNAKAN MICROWAVE ATAU OVEN UNTUK
MENINGKATKAN PRESTASI MESIN SERTA MEREDUKSI EMISI GAS
BUANG MESIN BENSIN 4 LANGKAH TECQUIPMENT TD201},
          author = { Yosua Aruan	 Daud},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS TEKNIK},
            year = {2024},
             url = {http://digilib.unila.ac.id/82544/},
        abstract = {Menurut Badan Pusat Statistik (BPS) pada tahun 2021 penambahan kendaraan
bermotor sebanyak 120.042.298 unit meningkat sebesar 4,1 persen dari tahun
sebelumnya. Menanggapi permasalahan tersebut, salah satu cara penghematan
bahan bakar dapat dicapai dengan meningkatkan prestasi mesin menggunakan filter
udara yang terbuat dari bentonit. Filter udara yang terbuat dari bentonit memiliki
kemampuan menyerap uap air (H2O) dan nitrogen (N2) yang terkandung dalam
udara pembakaran. Penggunaan filter bentonit dapat memberikan udara yang kaya
oksigen yang masuk ke ruang bakar untuk meningkatkan kualitas dari proses
pembakaran. Dalam penelitian ini, filter dibuat dari bentonit konsentrasi 70\% dan
air 30\%, yang diaktivasi fisik pemanasan menggunakan microwave, dan pada
berbagai massa 25 gram, 50 gram, dan 100 gram. Pengujian dilakukan
menggunakan mesin bensin 4-langkah Tequipment TD201 yang berlokasi di
Laboratorium Motor Bakar dan Propulsi Jurusan Teknik Mesin Universitas
Lampung. Berdasarkan pengujian, diperoleh bahwa filter udara bentonit yang
diaktivasi microwave dapat meningkatkan prestasi mesin. Hasil pengujian
menunjukkan bahwa peningkatan daya engkol terbaik terjadi pada penggunaan
massa 100 gram dengan temperatur aktivasi 65oC, diperoleh sebesar 9,80\%, diikuti
terbaik kedua terjadi pada massa 100 gram temperatur aktivasi 77?C sebesar 9,29\%,
dan terbaik ketiga terjadi pada massa 25 gram temperatur aktivasi 77?C sebesar
4,73\%. Sementara itu, emisi gas buang mengalami penurunan terbaik terjadi pada
putaran mesin 1500 rpm, massa 100 gram temperatur aktivasi 65oC, mampu
menurunkan kadar CO sebesar 8\% (mereduksi sebesar 54,55\%), dapat menurunkan
kadar HC sebesar 10 ppm (mereduksi sebesar 33,33\%), dapat menurunkan kadar
CO2 sebesar 18\% (mereduksi sebesar 40,00\%).
Kata kunci : filter udara, adsorben bentonit, prestasi mesin, emisi.

According to the Central Statistics Agency (BPS), in 2021 the addition of motorized
vehicles was 120,042,298 units, an increase of 4.1 percent from the previous year.
In response to this problem, one way to save fuel can be achieved by improving
engine performance using an air filter made from bentonite. Air filters made from
bentonite have the ability to absorb water vapor (H2O) and nitrogen (N2) contained
in combustion air. The use of a bentonite filter can provide oxygen-rich air into the
combustion chamber to improve the quality of the combustion process. In this
research, filters were made from 70\% bentonite and 30\% water, which were
activated by physical heating using a microwave, and at various masses of 25
grams, 50 grams and 100 grams. Tests were carried out using a Tequipment TD201
4-stroke petrol engine located at the Combustion Motor and Propulsion
Laboratory, Department of Mechanical Engineering, University of Lampung.
Based on testing, it was found that microwave-activated bentonite air filters can
improve engine performance. The test results showed that the best increase in
cranking power occurred when using a mass of 100 grams with an activation
temperature of 65oC, which was obtained at 9.80\%, followed by the second best
occurring at a mass of 100 grams with an activation temperature of 77?C at 9.29\%,
and the third best occurring at mass of 25 grams, activation temperature of 77?C
is 4.73\%. Meanwhile, the best reduction in exhaust emissions occurred at an engine
speed of 1500 rpm, a mass of 100 grams, an activation temperature of 65oC,
capable of reducing CO levels by 8\% (reducing by 54.55\%), able to reduce HC
levels by 10 ppm (reducing by 33 .33\%), can reduce CO2 levels by 18\% (reducing
by 40.00\%).

Keywords: air filter, bentonite adsorbent, engine performance, emissions.}
}