?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+VARIASI+SUHU+SINTERING+DAN+TEKANAN+TERHADAP%0D%0APEMBENTUKAN+KERAMIK+GERABAH+BERBAHAN+TANAH+LIAT%0D%0A%0D%0ADAN+SLAG+BOILER&rft.creator=Alya+%2C+Hafiz%09&rft.subject=530+Fisika&rft.description=Keramik+gerabah+merupakan+salah+satu+contoh+dari+keramik+tradisional.+Dalam%0D%0Aproses+pembuatannya+dilakukan+pemanasan+pada+suhu+tinggi.+Kualitas+keramik%0D%0Agerabah+dipengaruhi+oleh+suhu+sintering.+Bahan+pembuatan+keramik+gerabah+terdiri%0D%0Adari+tanah+liat+sebesar+75%25+dan+slag+sebesar+25%25.+Bahan+dilakukan+penghalusan%0D%0Adengan+ukuran+lolos+100+mesh.+Lalu+dicampur+dan+dibentuk+badan+keramik.+Proses%0D%0Asintering+dilakukan+pada+suhu+700%C2%B0C%2C+800%C2%B0C%2C+dan+900%C2%B0C+dengan+waktu+tahan%0D%0Aselama+3+jam.+Dilakukan+pengujian+terhadap+sampel+keramik+gerabah%2C+pengujian%0D%0Asampel+terdiri+dari+uji+kuat+tekan%2C+uji+densitas%2C+uji+porositas%2C+uji+absorptivitas.%0D%0ASampel+terbaik+diperoleh+pada+suhu+900%C2%B0C+yang+ditekan+menggunakan+mesin+press%0D%0Adengan+nilai+kuat+tekan+20%2C16+MPa%2C+absorptivitas+9%2C5%25%2C+porositas+20%2C44%25+dan%0D%0Adensitas+2%2C15+g%2Fcm3%0D%0A%0D%0A.+Berdasarkan+hasil+uji+kuat+tekan+tertinggi+maka+dilakukan%0D%0Akarakterisasi+menggunakan+alat+XRF%2C+XRD+dan+SEM-EDS.+Hasil+karakterisasi%0D%0Asampel+menggunakan+XRF+menunjukan+keramik+gerabah+didominasi+oleh+senyawa%0D%0ASiO2%2C+Al2O3+dan+Fe2O3.+Hasil+karakterisasi+sampel+menggunakan+XRD+terlihat+fasa%0D%0Ayang+terbentuk+pada+keramik+gerabah+adalah+Silicon+Oxide+(SiO2)%2C+Anorthite%0D%0A(Al2Ca08Si2)+dan+Wustite+(Fe1.98O2).+Selain+itu%2C+hasil+karakterisasi+sampel%0D%0Amenggunakan+SEM-EDS+menunjukkan+unsur+Si+dan+Al+yang+paling+mendominasi.%0D%0A%0D%0AKata+Kunci%3A+Keramik+gerabah%2C+suhu+sintering%2C+tekanan%2C+tanah+liat%2C+slag+boiler.%0D%0APottery+ceramics+are+one+example+of+traditional+ceramics.+In+the+manufacturing%0D%0Aprocess+is+carried+out+heating+at+high+temperatures.+The+quality+of+pottery+ceramics%0D%0Ais+affected+by+the+sintering+temperature.+The+material+for+making+pottery+ceramics%0D%0Aconsists+of+clay+by+75%25+and+slag+by+25%25.+The+material+is+smoothed+with+a+pass+size%0D%0Aof+100+mesh.+Then+mixed+and+formed+ceramic+body.+The+sintering+process+is+carried%0D%0Aout+at+temperatures+of+700%C2%B0C%2C+800%C2%B0C%2C+and+900%C2%B0C+with+a+holding+time+of+3+hours.%0D%0ATesting+of+pottery+ceramic+samples+is+carried+out%2C+sample+testing+consists+of%0D%0Acompressive+strength+tests%2C+density+tests%2C+porosity+tests%2C+absorptivity+tests.+The+best%0D%0Asamples+were+obtained+at+900%C2%B0C+pressed+using+a+press+with+compressive+strength%0D%0Avalues+of+20.16+MPa%2C+absorptivity+9.5%25%2C+porosity+20.44%25+and+density+2.15+g%2Fcm3.%0D%0ABased+on+the+results+of+the+highest+compressive+strength+test%2C+characterization+was%0D%0Acarried+out+using+XRF%2C+XRD+and+SEM-EDS+tools.+The+results+of+sample%0D%0Acharacterization+using+XRF+showed+that+pottery+ceramics+were+dominated+by+SiO2%2C%0D%0AAl2O3+and+Fe2O3+compounds.+The+results+of+sample+characterization+using+XRD%0D%0Ashow+that+the+phases+formed+in+pottery+ceramics+are+Silicon+Oxide+(SiO2)%2C+Anorthite%0D%0A(Al2Ca08Si2)+and+Wustite+(Fe1.98O2).+In+addition%2C+the+results+of+sample%0D%0Acharacterization+using+SEM-EDS+showed+the+most+dominating+Si+and+Al+elements.%0D%0A%0D%0AKeywords%3A+Pottery+ceramics%2C+sintering+temperature%2C+pressure%2C+clay%2C+boiler+slag.&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM&rft.date=2024-04-22&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F84802%2F1%2FAbstrak-Alya%2520-%2520Alya%2520Hafiz.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F84802%2F2%2FFull%2520Skripsi-Alya%2520-%2520Alya%2520Hafiz.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F84802%2F3%2FTanpa%2520Bab%2520Pembahasan-Alya%2520-%2520Alya%2520Hafiz.pdf&rft.identifier=++Alya+%2C+Hafiz+++(2024)+PENGARUH+VARIASI+SUHU+SINTERING+DAN+TEKANAN+TERHADAP+PEMBENTUKAN+KERAMIK+GERABAH+BERBAHAN+TANAH+LIAT+DAN+SLAG+BOILER.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F84802%2F