?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PEMBUATAN+PEMBUATAN+MORTAR+POLIMER+MENGGUNAKAN%0D%0APOLIMER+POLYETHYLENE+TEREPHTHALATE+(PET)+DAN+ETHYLENE%0D%0AVINYL+ACETATE+(EVA)+DENGAN+METODE+PERENDAMAN%0D%0A%0D%0ASELAMA+7+DAN+14+HARI%0D%0A&rft.creator=Herfira+%2C+Salsabila+Putri&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=530+Fisika&rft.description=Mortar+merupakan+salah+satu+material+bahan+bangunan+yang+terbuat+dari+campuran%0D%0Asemen%2C+agregat+halus+(pasir)%2C+dan+air.+Mortar+memiliki+kelemahan+yaitu+mudah%0D%0Aterkikis+sehingga+menyebabkan+keretakan+pada+bidang+konstruksi.+Oleh+karena+itu%2C%0D%0Adilakukan+penelitian+mortar+yang+dimodifikasi+polimer+agar+dapat+meningkatkan%0D%0Akinerja+perbaikan+pada+mortar.+Pada+penelitian+ini+menggunakan+polimer+Ethylene%0D%0AVinyl+Acetate+(EVA)+sebagai+bahan+substitusi+semen%2C+polimer+Polyethylene%0D%0ATerephthalate+(PET)+sebagai+bahan+substitusi+pasir%2C+dan+air.+Variasi+komposisi%0D%0Apolimer+Ethylene+Vinyl+Acetate+(EVA)+yang+digunakan+pada+penelitian+ini+sebesar%0D%0A2%25%3B+4%25%3B+6%25%3B+8%25%3B+10%25+dan+variasi+komposisi+polimer+Polyethylene+Terephthalate%0D%0A(PET)+sebesar+0%2C2%25%3B+0%2C5%25%3B+0%2C8%25%3B+1%2C1%25%3B+1%2C4%25.+Seluruh+bahan+baku+mortar+polimer%0D%0Adilakukan+karakterisasi+menggunakan+XRF%2C+XRD%2C+SEM-EDS%2C+dan+FTIR.+Seluruh%0D%0Abahan+baku+dicampur+dan+dicetak+dengan+cetakan+kubus+5%C3%975%C3%975+cm3%0D%0A%0D%0A.+Sampel+mortar%0D%0Apolimer+dilakukan+perendaman+selama+7+hari+dan+14+hari.+Berdasarkan+hasil%0D%0Apenelitian+didapatkan+nilai+kuat+tekan+dari+mortar+polimer+menurun+seiring+dengan%0D%0Apenambahan+variasi+komposisi+polimer.+Nilai+kuat+tekan+yang+optimum+diperoleh%0D%0Apada+mortar+polimer+dengan+waktu+perendaman+14+hari.+Hasil+karakterisasi+XRF%0D%0Amenunjukan+senyawa+paling+dominan+pada+mortar+polimer+ialah+CaO+dan+SiO2%0D%0Ayaitu+sebesar+38%2C65%25+dan+30%2C34%25+dengan+fasa+dominan+berupa+calcite%2C+quartz%2C%0D%0Acorundum%2C+dan+hematite.+Hasil+analisis+SEM-EDS+menunjukkan+unsur+yang%0D%0Atersebar+secara+merata+pada+mortar+polimer+yaitu+adalah+unsur+Ca+dan+Si.+Serta+hasil%0D%0Akarakterisasi+FTIR+pada+mortar+polimer+menunjukkan+adanya+gugus+fungsi+yang%0D%0Aterbentuk+yaitu+C%3DC%2C+C-H%2C+Si-O%2C+dan+O-H.%0D%0A%0D%0AKata+kunci%3A+mortar%2C+polimer%2C+uji+mekanis%2C+uji+fisis%2C+karakterisasi.%0D%0A%0D%0Aii%0D%0AABSTRACT%0D%0A%0D%0AMANUFACTURING+OF+POLYMER+MORTAR+USING+POLYETHYLENE%0D%0ATEREPHTHALATE+(PET)+AND+ETHYLENE+VINYL+ACETATE+(EVA)%0D%0APOLYMERS+BY+SOAKING+METHOD+FOR+7+AND+14+DAYS%0D%0A%0D%0ABy%0D%0A%0D%0AHerfira+Salsabila+Putri%0D%0A%0D%0AMortar+is+produced+by+mixing+cement%2C+fine+aggregate+(sand)%2C+and+water+into+a%0D%0Abuilding+material.+Mortar+is+susceptible+to+erosion%2C+which+can+lead+to+cracks+in%0D%0Aconstruction+surfaces.+Therefore%2C+research+on+polymer-modified+mortar+is%0D%0Aconducted+to+improve+the+performance+of+mortar+repairs.+In+this+research%2C+Ethylene%0D%0AVinyl+Acetate+(EVA)+polymer+as+a+substitute+for+cement%2C+Polyethylene%0D%0ATerephthalate+(PET)+polymer+as+a+substitute+for+sand%2C+and+water.+The+variation+of%0D%0AEthylene+Vinyl+Acetate+(EVA)+polymer+composition+used+in+this+research+is+2%25+%3B%0D%0A4%25%3B+6%25%3B+8%25%3B+10%25%2C+and+the+variation+of+Polyethylene+Terephthalate+(PET)+polymer%0D%0Acomposition+is+0%2C2%25%3B+0%2C5%25%3B+0%2C8%25%3B+1%2C1%25%3B+1%2C4%25.+All+raw+materials+of+the+polymer%0D%0Amortar+are+characterized+using+XRF%2C+XRD%2C+SEM-EDS%2C+and+FTIR.+All+raw+materials%0D%0Aare+mixed+and+cast+with+a+5%C3%975%C3%975+cm3%0D%0A%0D%0A.+Subsequently%2C+polymer+mortar+samples+are%0D%0Aimmersed+for+7+and+14+days.+Based+on+the+research+results%2C+the+compressive+strength%0D%0Aof+polymer+mortar+decreases+with+the+addition+of+polymer+composition+variations.%0D%0AThe+optimum+compressive+strength+is+obtained+in+polymer+mortar+with+14+day%0D%0Aimmersion+time.+XRF+characterization+results+show+that+the+most+dominant%0D%0Acompounds+in+polymer+mortar+are+CaO+and+SiO2%2C+at+38%2C65%25+and+30%2C34%25%0D%0Arespectively%2C+with+dominant+phases+consisting+of+calcite%2C+quartz%2C+corundum+and%0D%0Ahematite.+SEM-EDS+analysis+results+indicate+the+morphology+and+evenly%0D%0Adistributed+elements+in+polymer+mortar%2C+namely+Ca+and+Si.+The+FTIR%0D%0Acharacterization+results+for+the+polymer+mortar+indicate+the+formation+of+functional%0D%0Agroups+C%3DC%2C+C-H%2C+Si-O%2C+and+O-H.%0D%0A%0D%0AKeywords%3A+mortar%2C+polymer%2C+mechanical+testing%2C+physical+testing%2C+characterization.&rft.publisher=FAKULTAS+MATEMATIKAN+DAN+ILMU+PENGETAHUAN+ALAM&rft.date=2024-06-25&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85501%2F1%2F2057041004-Herfira%2520Salsabila%2520Putri-ABSTRAK%2520-%2520Herfira%2520Salsabila.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85501%2F2%2F2057041004-Herfira%2520Salsabila%2520Putri-Skripsi%2520Full%2520Tanpa%2520Lampiran%2520-%2520Herfira%2520Salsabila.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85501%2F3%2F2057041004-Herfira%2520Salsabila%2520Putri-%2520Skripsi%2520Tanpa%2520Bab%2520Pembahasan%2520-%2520Herfira%2520Salsabila.pdf&rft.identifier=++Herfira+%2C+Salsabila+Putri++(2024)+PEMBUATAN+PEMBUATAN+MORTAR+POLIMER+MENGGUNAKAN+POLIMER+POLYETHYLENE+TEREPHTHALATE+(PET)+DAN+ETHYLENE+VINYL+ACETATE+(EVA)+DENGAN+METODE+PERENDAMAN+SELAMA+7+DAN+14+HARI.++FAKULTAS+MATEMATIKAN+DAN+ILMU+PENGETAHUAN+ALAM%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F85501%2F