?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+VARIASI+KADAR+CaCO3+TERHADAP+PEMBENTUKAN%0D%0AFASE+SUPERKONDUKTOR+BSCCO-2212+PADA+SUHU+SINTERING%0D%0A835%C2%B0C+MENGGUNAKAN+METODE+PENCAMPURAN+BASAH&rft.creator=%09Cahlia+%2C+Kurnia+%09&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=530+Fisika&rft.description=Telah+dilakukan+sintesis+superkonduktor+BSCCO-2212+menggunakan+metode%0D%0Apencampuran+basah+pada+suhu+835%C2%B0C+.+Pada+penelitian+ini+dibuat+4+sampel+dengan%0D%0Avariasi+kadar+CaCO3+sebesar+0%2C95+mol%2C+1%2C00+mol%2C+1%2C05+mol%2C+dan+1%2C10+mol.+Sampel%0D%0Ayang+telah+dibuat+dilakukan+karakterisasi+X-Ray+Diffraction+(XRD)+dan+Scanning%0D%0AElectron+Microscopy+(SEM).+Hasil+analisis+XRD+menunjukkan+fraksi+volume%0D%0Ameningkat+seiring+dengan+bertambahnya+kadar+CaCO3.+Fraksi+volume+tertinggi%0D%0Asebesar+88%2C44%25+pada+sampel+BSCCO-2212%2F1%2C10.+Sedangkan+fraksi+volume%0D%0Aterendah+sebesar+81%2C02%25+pada+sampel+BSCCO-2212%2F0%2C95.+Sementara+derajat%0D%0Aorientasi+tertinggi+pada+sampel+BSCCO-2212%2F0%2C95+sebesar+29%2C01%25.+Hasil%0D%0Akarakterisasi+SEM+menunjukkan+bahwa+sampel+sudah+terorientasi+meskipun+belum%0D%0Asempurna+serta+terdapat+ruang+kosong+antar+lempengan+(void).%0D%0A%0D%0AKata+kunci%3A+superkonduktor%2C+BSCCO-2212%2C+sintering%2C+fraksi+volume%2C+dan+derajat%0D%0A%0D%0Aorientasi.%0D%0AThe+synthesis+of+the+BSCCO-2212+superconductor+was+carried+out+using+the+wet%0D%0Amixing+method+at+a+temperature+of+835%C2%B0C.+In+this+study%2C+4+samples+were+made+with%0D%0Avarying+levels+of+CaCO3+which+is+0%2C95+mol%2C+1%2C00+mol%2C+1%2C05+mol+and+1%2C10+mol.+The%0D%0Asamples+that+haveb+been+made+are+characyerization+to+X-Ray+Diffraction+(XRD)%0D%0Aand+Scanning+Electron+Microscopy+(SEM)+tests.+The+results+of+XRD+analysis+show%0D%0Athat+the+volume+fraction+increases+with+increasing+CaCO3+levels.+The+highest%0D%0Avolume+fraction+was+obtained+at+88%2C44%25+in+sample+BSCCO-2212%2F1%2C00.+While+the%0D%0Ahighest+degree+of+orientation+in+the+sample+BSCCO-2212%2F0%2C95+is+29%2C01%25.+SEM%0D%0Acharacyerization+results+show+that+the+sample+oriented+although+not+perfect+and%0D%0Athere+is+an+empty+space+between+the+plates.%0D%0A%0D%0AKey+words%3A+superconductor%2C+BSCCO-2212%2C+sintering%2C+volume+fraction%2C+and%0D%0A%0D%0Adegree+of+orientation.&rft.publisher=MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+&rft.date=2024-02-05&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85648%2F1%2Fabstrak%2520-%2520Cahlia%2520Kurnia.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85648%2F2%2Fskripsi%2520full%25282%2529%2520-%2520Cahlia%2520Kurnia.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F85648%2F3%2Ftanpa%2520pembahasan%2520-%2520Cahlia%2520Kurnia.pdf&rft.identifier=+++Cahlia+%2C+Kurnia+++(2024)+PENGARUH+VARIASI+KADAR+CaCO3+TERHADAP+PEMBENTUKAN+FASE+SUPERKONDUKTOR+BSCCO-2212+PADA+SUHU+SINTERING+835%C2%B0C+MENGGUNAKAN+METODE+PENCAMPURAN+BASAH.++MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+%2C+UNIVERSITAS+LAMPUNG+.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F85648%2F