%A  Renaria	 Yurita
%T EKSTRAKSI MAGNETIT (Fe3O4) DARI PASIR BESI PESISIR BARAT
SEBAGAI NANOPARTIKEL DENGAN METODE KOPRESIPITASI

%X Pasir besi di Provinsi Lampung tersebar di beberapa wilayah salah satunya
Kabupaten Pesisir Barat. Pasir Pantai Mandiri Kabupaten Pesisir Barat berwarna
abu-abu kehitaman yang mengindikasikan mengandung mineral besi, seperti
magnetit. Sampel pasir besi dari Pantai Mandiri dikarakterisasi menggunakan XRF,
dari hasil karakterisasi XRF pasir besi Pantai Mandiri mengandung unsur
diantaranya Fe 52,854%; Si 20,553%; Ti 7,600%; Al 7,449% dan Ca 6,873%.
Metode kopresipitasi merupakan metode yang banyak digunakan untuk
menghasilkan nanopartikel magnetit, karena metode ini yang paling sederhana dan
memberikan hasil yang tinggi. Pada penelitian ini dilakukan ekstraksi magnetit dari
pasir besi Pantai Mandiri menggunakan metode kopresipitasi dengan pelarut HCl
37% serta agen pengendap NH4OH 25% dan dikarakterisasi menggunakan X-Ray
Fluorescence (XRF), X-Ray Diffraction (XRD) dan Scanning Electron Microscope
(SEM). Hasil ekstraksi magnetit dari pasir besi Pantai Mandiri dengan variasi pH
pada proses pengendapan yaitu pH 9;10;11 diperoleh endapan berwarna hitam
dengan persen rendemen berturut-turut 16,42%; 18,24%; dan 21,6%. Hasil
ekstraksi Fe3O4 dikarakterisasi menggunakan instrumen XRF diperoleh kandungan
Fe3O4 pada masing-masing pH yaitu 84,074% untuk pH 9; 85,094 untuk pH 10 dan
91,747 untuk pH 11. Hasil ekstraksi pada variasi pH 11 dikarakterisasi
menggunakan XRD. Dari hasil analisa XRD diperoleh fasa magnetit dengan ukuran
19,23 nm berstruktur kubik dan memiliki konstanta kisi a = b = c = 8,3200? dengan
? = ? = ? = 90?. Hasil karakterisasi mengggunakan Scanning Electron Microscope
(SEM) morfologi Fe3O4 bentuknya tidak beraturan dan terjadi aglomerasi.
Kata kunci: Pasir Besi, Magnetit, Kopresipitasi, Nanopartikel
Iron sand in Lampung Province is spread in several areas, one of which is Pesisir
Barat Regency. The sand of Mandiri Beach Pesisir Barat Regency is gray-black
which indicates it contains iron minerals, such as magnetite. Iron sand samples from
Pantai Mandiri were characterized using XRF, from the XRF characterization
results the iron sand of Pantai Mandiri contained elements including Fe 52.854%;
Si 20.553%; Ti 7,600%; Al 7.449% and Ca 6.873%. The coprecipitation method is
a widely used method for producing magnetite nanoparticles, because it is the
simplest and gives high yields. In this study, magnetite extraction was carried out
from the iron sand of Pantai Mandiri using the coprecipitation method with 37%
HCl solvent and 25% NH4OH precipitating agent and characterized using X-Ray
Fluorescence (XRF), X-Ray Diffraction (XRD) and Scanning Electron Microscope
(SEM). The results of magnetite extraction from the iron sand of Mandiri Beach
with pH variations in the deposition process, namely pH 9; 10; 11 obtained a
precipitate of black color with a successive percent yield of 16.42%; 18,24%; and
21.6%. Fe3O4 extraction results were characterized using XRF instruments obtained
Fe3O4 content at each pH which is 84.074% for pH 9; 85.094 for pH 10 and 91.747
for pH 11. Extraction results at pH variation 11 were characterized using XRD.
From the results of XRD analysis, a magnetite phase with a size of 19.23 nm is
obtained with a cubic structure and has a lattice constant a = b = c = 8.3200? with
? = ? = ? = 90 ?. The results of characterization using Scanning Electron Microscope
(SEM) morphology Fe3O4 irregular shape and agglomeration occur.
Keywords: Iron Sands, Magnetite, Coprecipitation, Nanoparticles.