?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+VARIASI+KOMPOSISI+SEMEN+PCC+AKTIF+%3A+SEMEN+PCC%0D%0ABEKU+DAN+WAKTU+PERENDAMAN+TERHADAP+SIFAT+MEKANIS%2C%0D%0ASIFAT+FISIS+DAN+KARAKTERISTIK+PADA+MORTAR&rft.creator=%09Yuyun%09%2C++Savela&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=530+Fisika&rft.description=Mortar+adalah+campuran+yang+tersusun+atas+semen%2C+pasir+dan+air+yang+memiliki%0D%0Apersentase+berbeda.+Semen+merupakan+salah+satu+komponen+dalam+campuran%0D%0Apembuatan+mortar+yang+berfungsi+sebagai+bahan+perekat.+Senyawa-senyawa+kimia%0D%0Adari+semen+Portland+adalah+tidak+stabil%2C+sehingga+sangat+cenderung+untuk+bereaksi%0D%0Adengan+air.+Karena+itu+apabila+semen+dibiarkan+terbuka%2C+maka+semen+bisa+mengeras%0D%0Aatau+menjadi+beku+karena+senyawa+tersebut+bereaksi+dengan+uap+air+yang+ada+di%0D%0Audara.+Oleh+karena+itu%2C+dilakukan+penelitian+mengenai+proses+aktivasi+semen+PCC%0D%0Abeku+dengan+menambahkan+semen+PCC+aktif+sebagai+campuran+pembuatan+mortar.%0D%0AVariasi+komposisi+semen+PCC+aktif+%3A+semen+PCC+beku+sebesar+100%25+%3A+0%25%2C+35%25+%3A%0D%0A65%25%2C+30%25+%3A+70%25%2C+25%25+%3A+75%25%2C+20%25+%3A+80%25%2C+15%25+%3A+85%25+dan+0%25+%3A+100%25.+Mortar%0D%0Adicetak+dengan+ukuran+5x5x5+cm3%0D%0A%0D%0A%2C+direndam+dalam+air+selama+7+hari%2C+14+hari+dan%0D%0A28+hari.+Uji+mekanis+dilakukan+yaitu+kuat+tekan%2C+uji+fisis+meliputi+uji+massa+jenis%2C%0D%0A%0D%0Auji+porositas+dan+uji+absorpsi+serta+karakterisasi+mortar+semen+yaitu+XRF+dan+SEM-%0D%0AEDS.+Mortar+dengan+variasi+semen+PCC+aktif+100%25+dan+0%25+semen+PCC+beku+pada%0D%0A%0D%0Aumur+perendaman+28+hari+memiliki+nilai+kuat+tekan+tertinggi+sebesar+6%2C1+MPa%2C%0D%0Asedangkan+mortar+semen+dengan+variasi+semen+PCC+aktif+0%25+dan+100%25+semen%0D%0APCC+beku+pada+waktu+perendaman+7+hari+memiliki+nilai+kuat+tekan+terendah+sebesar%0D%0A1%2C5+MPa.%0D%0AKata+Kunci%3A+semen+PCC+aktif%2C+semen+PCC+beku%2C+kuat+tekan%2C+massa+jenis%2C+porositas%2C%0D%0Aabsorpsi%2C+XRF%2C+SEM-EDS.%0D%0AMortar+is+a+mixture+composed+of+cement%2C+sand+and+water+that+has+different%0D%0Apercentages.+Cement+is+one+of+the+components+in+the+mortar+manufacturing+mixture%0D%0Athat+functions+as+an+adhesive.+The+chemical+compounds+of+Portland+cement+are%0D%0Aunstable%2C+so+it+is+very+likely+to+react+with+water.+Therefore%2C+if+the+cement+is+left+open%2C%0D%0Athe+cement+can+harden+or+become+frozen+because+the+compound+reacts+with+water%0D%0Avapor+in+the+air.+Therefore%2C+research+was+conducted+on+the+activation+process+of%0D%0Afrozen+PCC+cement+by+adding+active+PCC+cement+as+a+mixture+for+making+mortar.%0D%0AVariation+of+active+PCC+cement+composition%3A+frozen+PCC+cement+by+100%25+%3A+0%25%2C%0D%0A35%25+%3A+65%25%2C+30%25+%3A+70%25%2C+25%25+%3A+75%25%2C+20%25+%3A+80%25%2C+15%25+%3A+85%25+and+0%25+%3A+100%25.%0D%0AMortar+molded+with+a+size+of+5x5x5+cm3%0D%0A%0D%0A%2C+soaked+in+water+for+7+days%2C+14+days+and%0D%0A28+days.+Mechanical+tests+are+carried+out%2C+namely+compressive+strength%2C+physical%0D%0Atests+include+density+tests%2C+porosity+tests+and+absorption+tests+and+characterization%0D%0Aof+cement+mortar%2C+namely+XRF+and+SEM-EDS.+Mortar+with+a+variation+of+100%25%0D%0Aactive+PCC+cement+and+0%25+frozen+PCC+cement+at+28+days+soaking+age+has+the%0D%0Ahighest+compressive+strength+value+of+6.1+MPa%2C+while+cement+mortar+with+0%25+active%0D%0APCC+cement+variation+and+100%25+frozen+PCC+cement+at+7+days+soaking+time+has%0D%0Athe+lowest+compressive+strength+value+of+1.5+MPa.%0D%0AKeywords%3A+active+PCC+cement%2C+frozen+PCC+cement%2C+compressive+strength%2C+density%2C%0D%0Aporosity%2C+absorption%2C+XRF%2C+SEM-EDS.&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+&rft.date=2024-05-13&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F86553%2F1%2FABSTRAK%2520-%2520Yuyun%2520Savela.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F86553%2F2%2FFULL%2520SKRIPSI%2520-%2520Yuyun%2520Savela.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F86553%2F3%2FFULL%2520SKRIPSI%2520TANPA%2520PEMBAHASAN%2520-%2520Yuyun%2520Savela.pdf&rft.identifier=+++Yuyun+%2C+Savela++(2024)+PENGARUH+VARIASI+KOMPOSISI+SEMEN+PCC+AKTIF+%3A+SEMEN+PCC+BEKU+DAN+WAKTU+PERENDAMAN+TERHADAP+SIFAT+MEKANIS%2C+SIFAT+FISIS+DAN+KARAKTERISTIK+PADA+MORTAR.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F86553%2F