Digital Library: No conditions. Results ordered -Date Deposited. 2024-03-28T13:32:24ZEPrintshttp://digilib.unila.ac.id/images/sitelogo.pnghttp://digilib.unila.ac.id/2016-04-29T08:32:59Z2016-04-29T08:32:59Zhttp://digilib.unila.ac.id/id/eprint/22082This item is in the repository with the URL: http://digilib.unila.ac.id/id/eprint/220822016-04-29T08:32:59ZPENGARUH WAKTU PEMERAMAN TERHADAP UJI KUAT TEKAN
PAVING BLOK MENGGUNAKAN CAMPURAN TANAH DAN KAPUR
DENGAN ALAT PEMADAT MODIFIKASIPaving block merupakan segmen-segmen kecil yang terbuat dari beton dengan
bentuk segi empat atau segi banyak yang memiliki sifat kuat tekan yang baik,
dapat menahan beban dalam batasan tertentu, dan mudah dalam pekerjaan
pemasangan. Paving block terbuat dari campuran semen portland atau bahan
perekat hidrolisis sejenisnya, air, dan agregat dengan atau tanpa bahan lainnya.
Pada penelitian ini proses pembuatan paving block akan menggunakan campuran
tanah dan kapur. Selain itu, dilakukan pemeraman terhadap paving block yang
diharapkan akan meningkatkan kekuatan paving block sesuai SNI 03-0691-1996.
Sampel tanah yang diuji berasal dari daerah Kota Baru, Lampung Selatan.
Komposisi campuran tanah dan kapur dengan variasi waktu pemeraman 7 hari, 14
hari, 21 hari dan 28 hari serta dengan perlakuan pra pembakaran dan pasca
pembakaran sampel paving block. Berdasarkan hasil pengujian fisik tanah asli,
USCS mengklasifikasikan sampel tanah sebagai tanah berbutir halus dan termasuk
ke dalam kelompok ML.
Hasil dari penelitian ini adalah pembuatan paving block menggunakan material
tanah lanau dan kapur tidak memenuhi SNI 03-0691-1996. Untuk nilai kuat tekan
paving block pra pembakaran dan pasca pembakaran paling baik ditunjukkan pada
waktu pemeraman 28 hari. Nilai kuat tekan yang dihasilkan secara keseluruhan
masih belum memenuhi spesifikasi dari paving block SK SNI 03-0691-1996 yaitu
minimal kuat tekan sebesar 85 kg/cm2. Begitu pula dengan nilai uji daya serap air
belum memenuhi spesifikasi dari paving block SK SNI – 03 – 0691– 1996 yaitu
berkisar 3% - 10%.
Kata kunci : Paving block, tanah lanau, kuat tekan, pembakaran tanah. EFFECT OF CURING TIME ON COMPRESSIVE STRENGTH TEST
PAVING BLOCK BY USING THE MIXTURE OF SOIL AND LIMESTONE
WITH MODIFICATION COMPACTOR Paving block is smaller segments made of concrete with rectangular or square
shape many of which have good compressive strength properties, has good
compressive strength properties, can withstand the load in some extent, and easy
installation work. Paving blocks made from a mixture of portland cement or a
kind of adhesive hydrolysis, water, and aggregates with or without other
ingredients. In this study the process of manufacture of paving blocks will use a
mix of soil and limestone. Moreover, curing of the paving blocks that are expected
to increase the strength of paving blocks is according to SNI 03-0691-1996.
Soil samples tested were from Kota Baru, South Lampung. The composition of
the soil mix and limestone with a variety of curing time 7 days, 14 days, 21 days
and 28 days as well as to the treatment of pre-combustion and post-combustion of
the sample of paving blocks. Based on the results of physical testing the original
soil, USCS classify soil samples as fine-grained soil and belong to the group ML.
Results from this study is the manufacture of paving blocks using silt soil and
limestone soil material that does not meet the specifications of SNI 03-0691-1996.
For the compressive strength of paving blocks pre-combustion and postcombustion
are best shown in curing time of 28 days. The compressive strength
that generated as a whole still does not meet the specifications of the paving block
SK SNI 03-0691-1996 that is a minimum compressive strength at 85 kg / cm2. As
well as the water absorption the test value not meet the specifications of the
paving block SK SNI - 03 - 0691- 1996 is around 3% - 10%.
Keywords: Paving blocks, silt soil, compressive strength, soil combustion1215011068 MARTHA HELMAHERAmarthahelmahera@yahoo.co.id