Digital Library: No conditions. Results ordered -Date Deposited. 2024-03-29T11:37:52ZEPrintshttp://digilib.unila.ac.id/images/sitelogo.pnghttp://digilib.unila.ac.id/2016-12-13T07:21:11Z2016-12-13T07:21:11Zhttp://digilib.unila.ac.id/id/eprint/24640This item is in the repository with the URL: http://digilib.unila.ac.id/id/eprint/246402016-12-13T07:21:11ZANALISIS STRUKTUR DAN LUAS PERMUKAAN SPESIFIK ZEOLIT
BERBASIS SILIKA SEKAM PADI AKIBAT VARIASI SUHU KALSINASI
150 oC, 250 oC, DAN 350oCABSTRAK
Penelitian tentang “Analisis Struktur dan Luas Permukaan Spesifik Zeolit
Berbasis Silika Sekam Padi Akibat Variasi Suhu Kalsinasi 150oC, 250oC, dan
350oC. Penelitian ini bertujuan untuk mempelajari pengaruh suhu kalsinasi
terhadap perubahan fasa dan luas permukaan spesifiknya. Sintesis zeolit dibuat
dari bahan silika sekam padi, NaOH, dan alumina dengan metode sol gel dan
perlakuan kalsinasi suhu 150oC, 250oC, dan 350oC. Sampel zeolit dikarakterisasi
dengan difraksi sinar-X (XRD) dan Surface Area Analyzer (SAA). Dari hasil
XRD diperoleh fasa yang terbentuk dan ukuran kristalit menggunakan persamaan
Scheerer. Pada suhu 150oC, fasa yang terbentuk gibbsite dengan ukuran kristalit
61,21 nm. Sedangkan pada suhu 250oC terdapat fasa gibbsite, bohmite, dan quartz
dengan ukuran kristalit berturut-turut adalah 58,71 nm; 180,06 nm; dan 80,35 nm.
Pada suhu 350oC fasa gibbsite telah berubah sepenuhnya menjadi bohmite dengan
ukuran kristalit 112,37 nm dan adanya quartz dengan ukuran kristalit 30,14 nm.
Semakin kecil ukuran kristalit, maka luas permukaan spesifik zeolit akan semakin
besar. Dari hasil analisis SAA luas permukaan spesifik akibat suhu kalsinasi
150oC, 250oC, dan 350oC masing-masing adalah 106,900 m2/g; 90,650 m2/g; dan
241,970 m2/g. Dari hasil penelitian diketahui ukuran kristalit fasa pada suhu
350oC memiliki nilai paling kecil, sehingga diperoleh luas permukaan spesifik
paling besar.
Kata kunci: Fasa, kalsinasi, luas permukaan spesifik, ukuran kristalit, dan zeolit.
ABSTRACT
The synthesis and analysis zeolite based silica rice husk was conducted by a
variety temperature of calcination at 150oC, 250oC, and 350oC. This research has
purpose to study influence temperature of calcination to the phase and specific
surface area zeolite. Zeolite was synthesized from silica rice husk, NaOH, and
alumina by sol gel method, and thermally treated 150oC, 250oC, and 350oC, then
characterized using X-ray Diffraction (XRD) and Surface Area Analyzer (SAA).
XRD characterization was obtained phase and crystalline size using Scheerer
equation. At temperature 150oC results gibbsite phase with crystalline size 61,21
nm. At temperature 250oC results gibbsite, bohmite, and quartz with crystalline
size successively 58,71 nm; 180,06 nm; and 80,35 nm. At temperature 350oC
results gibbsite phase had transformed to bohmite phase with crystalline size
112,37 nm, then quartz phase with crystalline size 30,14 nm. Small crystalline
size produce high specific surface area. The smaller crystalline size, the higher
specific surface area. SAA results specific surface area at temperature 150oC,
250oC, and 350oC respectively are106,900 m2/g; 90,650 m2/g; and 241,970 m2/g.
Based on the result, it can be concluded that the smallest crystalline size and the
largest specific surface area in temperature 350oC.
Keywords: Crystalline size, calcinations, phase, specific surface area, and zeolite.