ELECTRODE DIAMETER INFLUENCE TO STRENGTH OF SINGLE V WELD JOINT AT STEEL AISI 1045

NN, Chandra Hardiyuda (2010) ELECTRODE DIAMETER INFLUENCE TO STRENGTH OF SINGLE V WELD JOINT AT STEEL AISI 1045. Digital Library.

[img]
Preview
Text
BAB III.pdf

Download (332Kb) | Preview
[img]
Preview
Text
BAB I.pdf

Download (82Kb) | Preview
[img]
Preview
Text
BAB V.pdf

Download (8Kb) | Preview
[img]
Preview
Text
DAFTAR PUSTAKA.pdf

Download (61Kb) | Preview
[img]
Preview
Text
ABSTRACT.pdf

Download (5Kb) | Preview
[img]
Preview
Text
BAB IV new.pdf

Download (253Kb) | Preview

Abstrak

abstrak One of the most common process in manufacture industry is welding, where approximately 40-60 % of all the machining process is welding. In this the quality needed for the process is joint strength and avoiding welding defect. One of the variable that influence the welding quality is value of electrode diameter. If the diameter is too big, the penetration become enwell when doing root welding, so the root formed improperly. Root perfection affected greatly whit the joint strength. That phenomena encouraging the writer to do a research about affect of electrode diameter with the welding joint strength on the AISI 1045 materials. The purposes is to acquire a good knowledge about welding so the welding process can be planned well. To get the valueof the joint strength, the writer did the Destructive Testing (DT), such as tensile test with the specimen that appropriated with the ASTM E-8. This research used 3 variations on the electrode diameter, that is (2.6 mm, 3.2 mm, 4.0mm) The results of this research is follows. The highest tensile strength of the material is 653.3 MPa at the welding condition (Ø electrode : 3.2 mm, I : 110 Ampere), and the lowest is 500 MPa at the welding condition (Ø electrode : 4.0 mm, I : 130 Ampere). The value of electrode diameter affected the tensile strength, especially on some cases when the electrode diameter that is used is not suited with the seam welding that is formed. As there are variations on diameter on the seam welding width. So there are differences on the sum of multypass layer that is formed.

Tipe Karya Ilmiah: Artikel
Subyek: A General Works = Karya Karya Umum
Program Studi: Fakultas Teknik > Prodi Teknik Kimia
Depositing User: tik 24 . Digilib
Date Deposited: 26 Jan 2016 04:23
Last Modified: 26 Jan 2016 04:23
URI: http://digilib.unila.ac.id/id/eprint/20230

Actions (login required)

View Item View Item