PENGARUH HEAT TREATMENT DENGAN VARIASI MEDIA QUENCHING OLI DAN SOLAR TERHADAP STRUKTUR MIKRO DAN NILAI KEKERASAN BAJA PEGAS DAUN AISI 6135

Okti Bela Palupi, 1217041040 (2016) PENGARUH HEAT TREATMENT DENGAN VARIASI MEDIA QUENCHING OLI DAN SOLAR TERHADAP STRUKTUR MIKRO DAN NILAI KEKERASAN BAJA PEGAS DAUN AISI 6135. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK (ABSTRACT).pdf

Download (180Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya pengguna terdaftar

Download (3481Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (2643Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Heat treatment dengan variasi media quenching oli dan solar terhadap struktur mikro dan nilai kekerasan baja pegas daun AISI 3165 dilakukan proses austenisasi dengan temperatur 800 selama 60 menit. Proses selanjutnya, quenching dengan variasi media quenching 100% oli dan campuran 50% oli : 50% solar, kemudian tempering dengan temperatur 600 selama 40 menit. Hasil uji komposisi kimia baja pegas daun mengandung 0,3383% C untuk raw material, 0,3156% C untuk quench-temper menggunakan media 100% oli, dan 0,3333% C untuk quench-temper menggunakan media campuran 50 % oli : 50 % solar. Hasil uji kekerasan untuk sampel raw material yaitu 42,2 HRc, untuk sampel hasil tempering dengan media quenching 100% oli maupun campuran 50% oli : 50% solar berturut-turut yaitu 36,8 HRc dan 37,3 HRc. Hasil uji struktur mikro pada sampel raw material terbentuk fasa ferit dan perlit, sedangkan untuk sampel hasil quench-temper campuran 50% oli : 50% solar fasa yang terbentuk yaitu martensit temper yang lebih menyebar dibanding 100% oli. Kata Kunci: AISI 6135, austenit, ferit, HRc, martensit, perlit, quenching, raw material , tempering. THE EFFECT OF HEAT TREATMENT WITH VARIATIONS OF THE OIL AND DIESEL FUEL QUENCHING MEDIUM TO MICROSTRUCTURE AND HARDNESS VALUE IN THE LEAF SPRING STEEL AISI 6135. By Okti Bela Palupi Heat treatment with variations of the oil and diesel fuel quenching medium to microstructure and hardness value in the leaf spring steel AISI 6135 conducted austenisasi process with temperature of 800 for 60 minutes. The next process, quenching with a variation of 100% oil and mixture of 50% oil : 50% diesel fuel quenching medium, then tempering with temperature 600 for 40 minutes. Chemical composition test result of steel leaf springs containing 0.3383% C for the raw material, 0.3156% C to quench-tempering using 100% oil medium, and 0.3333% C to quench-tempering using mixture of 50% oil: 50 % diesel fuel medium. Hardness test results for samples of raw material that is 42,2 HRc, for samples of tempering with 100% oil nor mixture of 50% oil : 50% diesel fuel quenching medium respectively are 36,8 HRc dan 37,3 HRc. The test results microstructure on the samples raw material formed ferrite and pearlite phase, while the samples of quench-temper mix of 50% oil : 50% diesel fuel formed martensit temper phase more spread out than 100% oil. Keywords: AISI 6135, austenit, ferit, HRc, martensit, perlit, quenching, raw material , tempering.

Jenis Karya Akhir: Skripsi
Subyek: > Q Science (General)
> QC Physics
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: 1635286 . Digilib
Date Deposited: 24 Jun 2016 01:20
Terakhir diubah: 24 Jun 2016 01:20
URI: http://digilib.unila.ac.id/id/eprint/22817

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir