ANALISIS PENGARUH ARTIFICIAL AGING TERHADAP SIFAT MEKANIS PADA ALUMINIUM SERI 6061

Nur Imam Subagyo, 1215021061 (2017) ANALISIS PENGARUH ARTIFICIAL AGING TERHADAP SIFAT MEKANIS PADA ALUMINIUM SERI 6061. FAKULTAS TEKNIK , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (22Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (2973Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2155Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Penelitian proses artificial aging terhadap aluminium seri 6061 bertujuan untuk memperbaiki sifat mekanisnya. Aluminium seri 6061 diberi perlakuan panas dengan suhu 4500C selama 15 menit, kemudian diquenching dengan media pendingin berupa oli. Selanjutnya diberi perlakuan panas kembali pada suhu 1900C dengan variasi holding time 1 jam, 5 jam, dan 11 jam, kemudian didinginkan secara lambat dengan suhu ruangan. Hasil uji komposisi kimia menggunakan Spectromax menunjukan persentase Mg sebesar 1,41%, Si sebesar 0,911%, dan Al sebesar 96,7%. Hasil uji kekerasan menggunakan Rockwell Hardness Tester didapatkan nilai kekerasan bahan tanpa perlakuan panas sebesar 49,4 (HRB), holding time 1 jam sebesar 53,8 (HRB), holding time 5 jam sebesar 79,6 (HRB) dan holding time 11 jam sebesar 50,4 (HRB). Dari hasil uji SEM EDX menggunakan alat Zeiss Evo ® MA 10, menunjukan persentase unsur Al dari bahan tanpa perlakuan panas (96,7%) menurun terhadap bahan bahan dengan holding time 1 jam (89,55%), dan bahan dengan holding time 5 jam (81,58%) penurunan tersebut menunjukan terdapat fasa kedua pada bahan yang diberi perlakuan artifial aging. Kata kunci : Aluminium Seri 6061, Artificial aging, Kekerasan, SEM EDX ABSTRACT Research of artificial aging process on aluminum series 6061 is required to improve the mechanical properties of it. Aluminum 6061 series had heat treatment with temperature 4500C for 15 minutes, then quenching it with medium oil cooler. Furthermore, the aluminum itselves had heat treatment for the second time at 1900C with aholding time variation of 1 hour, 5 hours, and 11 hours, then cooled slowly with room temperature. The result of chemical composition test using Spectromax showed Mg percentage of 1.41%, Si 0.911%, and Al of 96.7%. Result of hardness test using Rockwell Hardness Tester got hardness value material without heat treatment equal to 49,4 (HRB), holding time 1 hour equal to 53,8 (HRB), holding time 5 hour equal to 79,6 (HRB) and holding time 11 hours of 50.4 (HRB). SEM EDX result showed test using Zeiss Evo ® MA 10 tool, obtained percentage of Al element from material without heat treatment (96,7%) decrease to material with holding time 1 hour (89,55%), and material with holding time 5 hour (81.58%) the decrease indicates that there is a second phase in the artificial aging treated material. Keywords: Aluminum Series 6061, Artificial aging, Violence, SEM EDX

Jenis Karya Akhir:	Skripsi
Subyek:	> Mesin (General). Mesin Sipil (General) > Mesin (General). Mesin Sipil (General) Mesin (General). Mesin Sipil (General)
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	08927295 . Digilib
Date Deposited:	19 Oct 2017 04:09
Terakhir diubah:	19 Oct 2017 04:09
URI:	http://digilib.unila.ac.id/id/eprint/28684

Actions (login required)

Lihat Karya Akhir