PENGARUH STRUKTUR AGGREGATE KARBON HITAM TERHADAP KEKUATAN TARIK KOMPOSIT KARET ALAM / KARBON HITAM

RISKI ARI PRATAMA , 1015021051 (2017) PENGARUH STRUKTUR AGGREGATE KARBON HITAM TERHADAP KEKUATAN TARIK KOMPOSIT KARET ALAM / KARBON HITAM. FAKULTAS TEKNIK , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRACT (ABSTRAK).pdf Download (24Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1685Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1686Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Karet alam merupakan salah satu komoditi perkebunan yang sangat penting peranannya dalam ekonomi Indonesia. Karet alam dijadikan sebagai sumber pendapatan dan kesejahteraan masyarakat serta sebagai pendorong pertumbuhan ekonomi sentra-sentra baru di wilayah sekitar perkebunan karet. Sebagian besar petani karet di Indonesia lebih memilih menjual karet alam hasil sadapan mereka kepada pengepul dengan harga yang relatif murah. Hal ini disebabkan oleh kurang mengertinya petani karet tentang cara pemrosesan karet olahan agar menghasilkan produk olahan karet yang berkualitas dan tentunya bernilai jual tinggi sehingga dapat menambah keuntungan bagi para petani karet. Salah satu peningkatan nilai ekonomis karet adalah dengan membuat komposit berbahan dasar karet alam. Komposit merupakan salah satu alternatif untuk menghasilkan material yang dari sifat mekaniknya lebih baik dari material lainnya. Tujuan dari penelitian ini adalah mengetahui kekuatan tarik komposit karet alam / karbon hitam. Bahan pengisi komposit yang digunakan pada penelitian ini adalah karbon hitam dengan seri N220, N330, N550, dan N660. Pengujian komposit ini, menggunakan pengujian tarik dengan ASTM D-412. Dari hasil pengujian tarik tersebut diperoleh nilai pada komposit karet alam – karbon hitam dengan penguat karbon hitam N220 memiliki kekuatan tarik tertinggi yaitu sebesar 1.216 MPa. Sedangkan kekuatan tarik terendah 0.610 MPa pada komposit dengan penguat karbon hitam N550. Dikarenakan struktur pada penguat karbon hitam N220 lebih komplek dan rapat dibandingkan dengan struktur penguat karbon hitam N550 yang lebih sederhana. Berdasarkan hasil foto makro dan hasil Scanning Electron Microscope menunjukkan besarnya kekuatan tarik tidak hanya dipengaruhi oleh struktur, aglomerat adalah penyebab kekuatan tarik komposit. Kata kunci :Komposit, karet alam, karbon hitam, struktur, kekuatan tarik, Scanning Electron Microscope (SEM). abstract Natural rubber is one of the most important plantation commodities in Indonesia's economy. Natural rubber used as a source of income and welfare of the community and as a driver of economic growth of new centers in the area around the rubber plantation. Most of the rubber farmers in Indonesia prefer to sell natural rubber from their tappers to the collectors with a relatively cheap price. This is caused by the lack of understanding of rubber farmers on how to process processed rubber to produce high quality rubber processing products and of course high selling value so as to increase profits for rubber farmers. One of the increasing economic value of rubber is by making composite based on natural rubber. Composites are an alternative to produce materials that are of better mechanical properties than other materials. The purpose of this research is to know the tensile strength of natural rubber composite / carbon black. The composite filler used in this study is carbon black with N220, N330, N550, and N660 series. This composite test, using tensile testing with ASTM D-412. From the tensile test results obtained value on natural rubber composite - carbon black with carbon black reinforcement N220 has the highest tensile strength of 1.216 MPa. While the lowest tensile strength of 0.610 MPa on composites with black carbon N550. Because the structure of the N220 carbon black reinforcement is more complex and denser than the simpler N550 carbon black reinforcement structure. Based on the results of macro photographs and the results of Scanning Electron Microscope shows the magnitude of tensile strength is not only influenced by the structure, agglomerates are the cause of composite tensile strength. Keywords: Composite, natural rubber, carbon black, structure, tensile strength, Scanning Electron Microscope (SEM).

Jenis Karya Akhir:	Skripsi
Subyek:	> Mesin (General). Mesin Sipil (General) > Mesin (General). Mesin Sipil (General) Mesin (General). Mesin Sipil (General)
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	49830468 . Digilib
Date Deposited:	27 Oct 2017 03:19
Terakhir diubah:	27 Oct 2017 03:19
URI:	http://digilib.unila.ac.id/id/eprint/28975

Actions (login required)

Lihat Karya Akhir