STUDI PIROLISIS MINYAK BIJI JARAK KALIKI MENGGUNAKAN PREKURSOR ZEOLIT BERBASIS SILIKA SEKAM PADI SEBAGAI KATALIS

YUDHA ARI SATRIA, 1317011079 (2017) STUDI PIROLISIS MINYAK BIJI JARAK KALIKI MENGGUNAKAN PREKURSOR ZEOLIT BERBASIS SILIKA SEKAM PADI SEBAGAI KATALIS. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (11Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (1456Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1456Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pirolisis minyak jarak kaliki menggunakan prekursor zeolit sebagai katalis telah dipelajari dalam penelitian ini. Prekursor zeolit dibuat dari sol silika dan logam aluminium menggunakan metode elektrokimia dengan variasi potensial: 8, 10, dan 12 volt, serta variasi waktu: 1, 2, dan 3 jam, lalu dikalsinasi pada suhu 600ºC. Hasil menunjukkan bahwa semakin tinggi nisbah Si/Al rendemen liquid fuel yang diperoleh semakin besar. Liquid fuel dianalisis menggunakan GC-MS, kandungan hidrokarbon tertinggi diperoleh menggunakan katalis Pre-Zeo8:1 yang dikalsinasi pada suhu 800ºC dengan kandungan hidrokarbon sebesar 85,97%. Karakterisasi XRD menunjukkan bahwa Pre-Zeo8:1 dengan suhu kalsinasi 600ºC didominasi oleh fasa amorf, namun pada suhu kalsinasi 800 dan 900ºC terdapat fasa kristalin berupa albite dan cristobalite yang menunjukkan bahwa sampel belum menjadi zeolit sehingga dianggap sebagai prekursor zeolit. Karakterisasi SEM menunjukkan bahwa Pre-Zeo8:1 memiliki morfologi permukaan yang heterogen, pada suhu kalsinasi 600ºC belum tampak adanya pori-pori pada permukaan katalis. Spektrum FTIR menunjukkan bahwa Pre-Zeo8:1 mengandung situs asam Brønsted-Lowry. Karakterisasi fisik menunjukkan bahwa viskositas liquid fuel hasil pirolisis minyak jarak kaliki telah memenuhi syarat berdasarkan SNI 7431- 2008. Kata kunci: pirolisis, minyak jarak kaliki, prekursor zeolit, metode elektrokimia abstract Pyrolysis of castor oil using zeolite precursor as catalyst was studied. Zeolite precursor was prepared from rice husk silica sol and aluminium metal by electrochemical method using different potentials of 8, 10, and 12 volt, and reaction times of 1, 2, and 3 hours, to produce the samples with different Si/Al ratios. The samples were then calcined at 600ºC,and tested as catalyst. The results show that the higher the Si/Al ratio of the catalyst, the higher the yield of the reaction. Liquid fuel was analyzed by GC-MS, and revealed that the liquid fuel with the highest hydrocarbon content was obtained using Pre-Zeo8:1 calcined at 800ºC with hydrocarbon content of 85.97%. The results of XRD characterization show that Pre-Zeo8:1 with calcination temperature of 600ºC was dominated by amorphous phase, but at higher temperatures of 800 and 900ºC, the crystalline phases of albite and cristobalite were detected. However, complete formation of zeolite was not displayed by the results. SEM characterization shows that Pre-Zeo8:1 has heterogeneous surface morphology, and the existence of the sample as porous material with the porosity influenced by the calcination temperatures. FTIR spectrum shows that Pre-Zeo8:1 contains Brønsted-Lowry acid site. The physical characterization indicates that the viscosity of liquid fuel obtained fulfilled the requirement for viscosity based on SNI 7431-2008. Keywords: pyrolysis, castor oil, zeolite precursor, electrochemical method

Jenis Karya Akhir:	Skripsi
Subyek:	> QD Chemistry
Program Studi:	FKIP > Prodi Pendidikan Kimia
Pengguna Deposit:	46669888 . Digilib
Date Deposited:	21 Dec 2017 02:46
Terakhir diubah:	21 Dec 2017 02:46
URI:	http://digilib.unila.ac.id/id/eprint/29377

Actions (login required)

Lihat Karya Akhir