STUDI PENAMBAHAN ASAP CAIR SABUT KELAPA SEBAGAI INHIBITOR KERAK KALSIUM KARBONAT (CaCO3) MENGGUNAKAN METODE UNSEEDED EXPERIMENT

SRI BUDI ASIH, 151701126 (2019) STUDI PENAMBAHAN ASAP CAIR SABUT KELAPA SEBAGAI INHIBITOR KERAK KALSIUM KARBONAT (CaCO3) MENGGUNAKAN METODE UNSEEDED EXPERIMENT. Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (145Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2575Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2577Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Permasalahan yang sering dijumpai pada bidang industri khususnya industri yang menggunakan pipa sebagai proses aliran fluida seperti industri minyak dan gas adalah terbentuknya kerak. Salah satu kerak yang banyak dijumpai yaitu kalsium karbonat (CaCO3). Oleh karena itu, pada penelitian ini telah digunakan asap cair sabut kelapa sebagai inhibitor ramah lingkungan untuk kerak CaCO3 dengan menggunakan metode tanpa penambahan bibit kristal (unseeded experiment) pada variasi larutan pertumbuhan CaCO3 konsentrasi 0,025; 0,038; 0,050; dan 0,063 M serta pada variasi penambahan inhibitor 5, 15, 25, dan 35%. Nilai persen efektivitas tertinggi terjadi pada larutan pertumbuhan 0,025 M dengan penambahan inhibitor sebesar 35% yaitu sebesar 88,41%. Berdasarkan hasil analisis menggunakan scanning electron microscopy (SEM) dan x-ray diffraction (XRD) menunjukkan bahwa kerak CaCO3 tanpa inhibitor terdiri dari fasa kalsit dan aragonit, sementara setelah penambahan inhibitor terdiri dari fasa kalsit dan vaterit. Hasil analisis kerak CaCO3 menggunakan particle size analyzer (PSA) menunjukkan bahwa kerak CaCO3 mengalami penurunan distribusi ukuran partikel sebelum dan setelah ditambahkan inhibitor yang dapat dilihat dari rata�rata (mean) yaitu dari 10,00 menjadi 4,889 μm dan nilai tengah (median) yaitu dari 9,359 menjadi 4,467 μm. Asap cair sabut kelapa terbukti dapat digunakan sebagai inhibitor untuk pertumbuhan kerak CaCO3 menggunakan metode unseeded experiment. Kata kunci: Asap cair sabut kelapa, CaCO3, industri, inhibitor, kerak. The problem which is frequently encountered in the industrial sector especially industries that use pipes as a fluid flow process for instance the oil and gas industry is the scaling formation. One of the considerable scale which easily be discovered is calcium carbonate (CaCO3). Therefore, this research used coconut coir liquid smoke as a green inhibitor for CaCO3 scale by using unseeded experiment method at variations in the CaCO3 growth solution with concentration of 0.025; 0.038; 0.050; and 0.063 M respectively as well as variations in the addition of inhibitors as much as 5, 15, 25, and 35% sequentially. Afterwards, the highest effectiveness percent value occured in 0.025 M growth solution with the addition of 35% inhibitor that was equal to 88.41%. Based on the analysis results of scanning electron microscopy (SEM) and x-ray diffraction (XRD) showed that the CaCO3 scale without inhibitors consisted of calcite and aragonite phases, while after the addition it consisted of calcite and vaterite phases. Alternately, the particle size analyzer (PSA) results of CaCO3 scale indicated that the particle size distribution of CaCO3 scale decreased after it was added by inhibitor which can be seen from the mean started from 10.00 to 4.889 μm and the median from 9.359 to 4.467 μm. All in all, coconut coir liquid smoke has been proven to be used as an inhibitor for the growth of CaCO3 scale using the unseeded experiment method. Kata kunci: Coconut coir liquid smoke, CaCO3, industry, inhibitor, scale.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	31 Mar 2022 04:13
Terakhir diubah:	31 Mar 2022 04:13
URI:	http://digilib.unila.ac.id/id/eprint/57150

Actions (login required)

Lihat Karya Akhir