STUDI PENGARUH PERLAKUAN KIMIA SERAT IJUK TERHADAP KEKUATAN TARIK KOMPOSIT SERAT IJUK/KARET ALAM

Muhammad Dhuha Syahbana, 1515021067 (2021) STUDI PENGARUH PERLAKUAN KIMIA SERAT IJUK TERHADAP KEKUATAN TARIK KOMPOSIT SERAT IJUK/KARET ALAM. Fakultas Teknik, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK - ABSTRACT - Kak Dan (20).pdf Download (113Kb) | Preview
	File PDF 2. SKRIPSI FULL - Kak Dan (20).pdf Restricted to Hanya staf Download (3718Kb)
Preview	File PDF 3. SKRIPSI TANPA BAB PEMBAHASAN - Kak Dan (20).pdf Download (2989Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Komposit merupakan material yang dapat memenuhi kebutuhan manusia sesuai dengan sifat material yang diinginkan. Bahan penyusun komposit dapat berbagi macam bahan yang salah satunya adalah karet alam. Karet alam merupakan polimer dari bahan alami. Sementara serat banyak terdapat di Indonesia salah satunya serat ijuk, komposit dengan matik karet alam serat ijuk menghasilkan material komposit hijau (green komposit), pada penelitian ini diamati pengaruh perlakuan alkali pada serat ijuk terhadap kekuatan tarik komposit karet alam / serat ijuk. Proses pembuatan komposit ini menggunakan serat satu arah dengan dilakukan fabrikasi antara karet alam dan serat ijuk kemudian dilakukan dengan pembebanan menggunakan mesin press lalu di panaskan dengan mesin oven dengan temperatur 80 ̊C selama 15 menit dan kemudian di cutting menggunakan karter untuk membentuk spesimen sesuai standar ASTMD-412 untuk dilakukan pengujian tarik dan terakhir melakukan Scanning Electron Miscroscope (SEM). Dari hasil pengujian tarik tersebut diperoleh nilai pada komposit karet alam – serat ijuk tanpa perlakuan memiliki kekuatan tarik tertinggi yaitu sebesar 13,26 MPa. Sedangkan kekuatan tarik terendah pada perlakuan sebanyak 7% dengan nilai sebesar 3,402 MPa. Dikarenakan struktur pada penguat tanpa menggunakan perlakuan lebih rapat terhadap matriks dibandingkan dengan struktur menggunakan perlakuan ijuk 7%. Berdasarkan hasil foto makro dan Scanning Electron Miscroscope menunjukkan besarnya kekuatan tarik tidak hanya dipengaruhi oleh struktur, melainkan matriks dan fiber yang homogen adalah penyebab kekuatan tarik komposit. Kata kunci : Karet Alam (KA), Komposit Karet Alam-Serat Ijuk, Kekuatan Tarik, Scanning Electron Microscope (SEM). Composites are materials that can meet human needs in accordance with the desired material properties. Composite constituent materials can be of various kinds, one of which is natural rubber. Natural rubber is a polymer made from natural materials, while there are many letters in Indonesia, one of them is palm fiber, composites with natural rubber fiber matrices produce green composite materials. In this study, the effect of alkali treatment on palm fiber fibers on the tensile strength of natural rubber fiber composites was observed. The process of making this composite uses one-way fiber which is fabricated between natural rubber and palm fiber then carried out by loading using a press machine and then heated in an oven at a termperature of 80 ̊C for 15 minutes then cut using characters to form specimens according to the ASTMD-412 standard for tensile testing and finaly a melakukan Scanning Electron Miscroscope (SEM). From the results of the tensile test, it was obtained that the value of the certified natural rubber composite without treatment had the highest tensile strength of 13,26 MPa while the lowest tensile strength was at 7% strength with a value of 3,402 MPa. This is because the structure of the reinforment without using treatment is closer to the matrix than the structure using the parent treatment of 7%. Based on the results of macro photos and scanning electron miscroscope (SEM). Shows that the magnitude of the tensile strength is not only influenced by the structure but the homogeneous matrix and fiber are the cause of the tensile strength of the composite. Keywords : Natural rubber, composite, tensile strength, scanning electron microscope (SEM).

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) 600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	UPT . Dito Nipati
Date Deposited:	23 May 2022 04:52
Terakhir diubah:	23 May 2022 04:52
URI:	http://digilib.unila.ac.id/id/eprint/61621

Actions (login required)

Lihat Karya Akhir