PENGARUH VARIASI WAKTU PEMANASAN SINTESIS PERAK NITRAT (AgNO3) MENGGUNAKAN METODE REDUKSI KIMIA

Muhammad Rizki, 1917041012 (2023) PENGARUH VARIASI WAKTU PEMANASAN SINTESIS PERAK NITRAT (AgNO3) MENGGUNAKAN METODE REDUKSI KIMIA. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (4033Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sintesis perak nitrat menggunakan metode reduksi kimia dengan variasi waktu pemanasan selama 1 jam, 2 jam dan 3 jam telah berhasil dilakukan. Penelitian ini bertujuan untuk mengetahui pengaruh variasi waktu pemanasan terhadap struktur fasa, konsentrasi kandungan unsur, morfologi, dan persentase massa unsur. Proses sintesis dilakukan dengan memanaskan campuran perak dan asam nitrat pada suhu T = 85 °C selama 1 jam, 2 jam, dan 3 jam, kemudian dilakukan proses evaporasi pada suhu T = 125 °C selama 10 menit. Hasil analisis XRF pada sampel AgNO3 menunjukkan perbedaan persentase konsentrasi Ag, dengan persentase konsentrasi Ag terbesar yang dihasilkan yaitu 98,839% pada variasi waktu pemanasan 2 jam. Unsur pengotor pada hasil XRF sampel AgNO3 memiliki konsentrasi yang lebih dari 1%, dengan konsentrasi unsur pengotor terbesar yaitu tembaga (Cu). Hal ini yang menyebabkan sampel hasil sintesis berwarna biru. Hasil analisis XRD menunjukkan fasa AgNO3 memiliki struktur orthorombic, dengan persentase fasa AgNO3 terbesar yang dihasilkan yaitu 27,85% pada variasi waktu pemanasan 2 jam. Hasil analisis SEM-EDS sampel AgNO3 pada variasi waktu pemanasan selama 2 jam menunjukkan sampel mengalami aglomerasi dengan ukuran butir (21,59-120,1 μm), serta persentase massa 92,68%. Kata kunci: AgNO3, perak, asam nitrat, XRF, XRD, SEM-EDS. ABSTARCT Synthesis of silver nitrate using the chemical reduction method with variations in heating time for 1 hour, 2 hours and 3 hours has been successfully carried out. This study aims to determine the effect of variations in heating time on the phase structure, elemental concentration, morphology, and mass percentage of elements. The synthesis process was carried out by heating a mixture of silver and nitric acid at T = 85 °C for 1 hour, 2 hours and 3 hours, then the evaporation process was carried out at T = 125 °C for 10 minutes. The results of the XRF analysis on the AgNO3 samples showed differences in the percentage of Ag concentrations, with the largest percentage of Ag concentrations produced, namely 98.839% at 2 hours of heating time variation. The impurity element in the XRF results of the AgNO3 sample has a concentration of more than 1%, with the largest concentration of the impurity element, namely copper (Cu). This causes the synthesized sample to turn blue. The results of the XRD analysis showed that the AgNO3 phase had an orthorhombic structure, with the largest percentage of AgNO3 produced, namely 27.85% at 2 hours of heating time variation. The results of SEM-EDS analysis of AgNO3 samples at various heating times for 2 hours showed that the samples experienced agglomeration with grain size (21.59-120.1 μm), and a mass percentage of 92.68%. Keywords: AgNO3, silver, nitric acid, XRF, XRD, SEM-EDS.

Jenis Karya Akhir:	Skripsi
Subyek:	000 Ilmu komputer, informasi dan pekerjaan umum
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	2301308427 . Digilib
Date Deposited:	03 Aug 2023 04:32
Terakhir diubah:	03 Aug 2023 04:32
URI:	http://digilib.unila.ac.id/id/eprint/74047

Actions (login required)

Lihat Karya Akhir