STUDI PENAMBAHAN CAMPURAN LIMBAH CAIR TEMPE DAN ASAP CAIR TEMPURUNG KELAPA GRADE 2 SEBAGAI INHIBITOR KERAK MAGNESIUM KARBONAT (MgCO3) MENGGUNAKAN METODE SEEDED EXPERIMENT

ALYAA , FATHIA KESUMA (2023) STUDI PENAMBAHAN CAMPURAN LIMBAH CAIR TEMPE DAN ASAP CAIR TEMPURUNG KELAPA GRADE 2 SEBAGAI INHIBITOR KERAK MAGNESIUM KARBONAT (MgCO3) MENGGUNAKAN METODE SEEDED EXPERIMENT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK.pdf

Download (31Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya staf

Download (2519Kb) | Minta salinan
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (1542Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pembentukan kerak yang terjadi pada komponen industri memberikan dampak secara teknis dan ekonomis. Kerak yang terbentuk seperti kerak magnesium karbonat (MgCO3) akan menjadi masalah yang serius pada perindustrian yang menggunakan air dalam sistem kerjanya. Oleh karena itu, pada penelitian ini telah dilakukan penambahan campuran limbah cair tempe dan asap cair tempurung kelapa grade 2 (TA) sebagai inhibitor kerak MgCO3 menggunakan metode seeded experiment. Larutan pertumbuhan MgCO3 0,10; 0,15; 0,20 dan 0,25 M diujikan pada setiap variasi dengan perbandingan konsentrasi inhibitor campuran (TA) 1:3; 2:3; 3:3 dan 4:3. Perbandingan konsentrasi yang paling efektif yaitu pada konsentrasi 4:3 kemudian campuran inhibitor (TA) 4:3 divariasikan kembali menjadi konsentrasi 0,005; 0,010 dan 0,015%. Nilai persentase efektifitas yang paling tinggi yaitu pada perbandingan inhibitor campuran (TA) 4:3 dengan konsentrasi 0,015% terhadap larutan pertumbuhan dengan konsentrasi 0,10 M sebesar 64,78 %. Berdasarkan hasil analisis menggunakan Scanning Electron Microscopy (SEM) setelah penambahan inhibitor, morfologi kristal MgCO3 menjadi berbentuk lembaran tipis pendek yang kecil dan lebih rapuh daripada tanpa penambahan inhibitor yang berbentuk lembaran panjang seperti kelopak bunga. Analisis menggunakan X-Ray Diffraction (XRD) menunjukkan fasa kristal MgCO3 yaitu hydromagnesite dan memiliki perbedaan intensitas sebelum dan sesudah penambahan inhibitor. Analisis menggunakan Particle Size Analyzer (PSA) menunjukkan adanya penurunan ukuran partikel kristal setelah ditambahkan inhibitor yakni memiliki nilai rata-rata (mean) dari 28,10 m menjadi 21,52 m dan nilai tengah (median) dari 14,41 m menjadi 9,34 m. Kata kunci : asap cair tempurung kelapa, inhibitor, kerak, limbah cair tempe, MgCO3. The scale formation that occurs in industrial components has a technical and economic impact. Scale formed like magnesium carbonate scale (MgCO3) will be a serious problem in industries that use water in their work systems. Therefore, in this study a mixture of tempeh liquid waste and grade 2 coconut shell liquid smoke (TA) was added as a MgCO3 scale inhibitor using the seeded experiment method. Growth solution of MgCO3 0.10; 0.15; 0.20 and 0.25 M were tested for each variation of the concentration ratio of mixture inhibitor (TA) 1:3; 2:3; 3:3 and 4:3. The most effective concentration ratio was in the mixture inhibitor (TA) 4:3, then the mixture inhibitor (TA) 4;3 was varied again into concentrations of 0,005; 0,010 dan 0,015%. The highest percentage value for effectiveness was in the ratio of mixture inhibitor TA (4:3) with a concentration of 0,015% to the growth solution with a concentration of 0.10 M of 64.78%. Based on the results of analysis using Scanning Electron Microscopy (SEM) after the addition of the inhibitors, the morphology crystals of MgCO3 becomes in the form of short thin sheets that are smaller and more fragile than without the addition of inhibitors which are in the form of long sheets like flower petals. Analysis using X-Ray Diffraction (XRD) showed that the crystalline phase of MgCO3 was hydromagnesite and had different intensities before and after addition of the inhibitors. Analysis using the Particle Size Analyzer (PSA) showed a decrease in crystal particle size after addition of the inhibitors, which had an average value from 28.10 m to 21.52 m and the median value from 14.41 m to 9.34 μm. Keywords : coconut shell liquid smoke, inhibitor, tempeh liquid waste, MgCO3, scale.

Jenis Karya Akhir: Skripsi
Subyek: 500 ilmu pengetahuan alam dan matematika
500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi: FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit: 2301000613 . Digilib
Date Deposited: 07 Aug 2023 01:39
Terakhir diubah: 07 Aug 2023 01:39
URI: http://digilib.unila.ac.id/id/eprint/74131

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir