STUDI PENAMBAHAN CAMPURAN EKSTRAK KULIT NANAS (Ananas comosus) DAN ASAP CAIR TEMPURUNG KELAPA GRADE 2 SEBAGAI INHIBITOR KERAK MAGNESIUM KARBONAT (MgCO3) MENGGUNAKAN METODE SEEDED EXPERIMENT

MAUDI , CAHYA MUSLIMAH (2023) STUDI PENAMBAHAN CAMPURAN EKSTRAK KULIT NANAS (Ananas comosus) DAN ASAP CAIR TEMPURUNG KELAPA GRADE 2 SEBAGAI INHIBITOR KERAK MAGNESIUM KARBONAT (MgCO3) MENGGUNAKAN METODE SEEDED EXPERIMENT. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (29Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (2129Kb) | Minta salinan
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1143Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pembentukan kerak MgCO3 menyebabkan timbunan kerak cukup banyak di dalam pipa yang dapat menghambat perpindahan panas dan mengakibatkan kerugian yang sangat besar. Oleh karena itu untuk mengatasi masalah tersebut, telah dilakukan penelitian ini dengan melakukan pengujian inhibitor campuran ekstrak kulit nanas dan asap cair tempurung kelapa grade 2 (NA) pada kerak magnesium karbonat (MgCO3) menggunakan metode seeded experiment pada variasi konsentrasi larutan pertumbuhan MgCO3 sebesar 0,100; 0,150; 0,200; dan 0,2500 M yang diujikan pada variasi perbandingan konsentrasi inhibitor NA 1:3, 2:3, 3:3, dan 4:3. Perbandingan konsentrasi yang paling efektif yaitu 4:3 divariasikan kembali menjadi konsentrasi 50, 100, dan 150 ppm. Nilai persentase efektifitas yang paling tinggi yaitu pada perbandingan campuran NA 4:3 dengan konsentrasi 150 ppm terhadap larutan pertumbuhan dengan konsentrasi 0,100 M sebesar 59,14 %. Berdasarkan hasil analisis menggunakan Scanning Electron Microscopy (SEM) setelah ditambahkan inhibitor morfologi kerak MgCO3 menjadi lebih tipis dan terlihat lebih rapuh. Analisis menggunakan X-Ray Diffraction (XRD) menunjukkan kerak MgCO3 tanpa dan dengan penambahan inhibitor memiliki kemiripan puncak dengan data hasil penelitian sebelumnya nomor 96-900-7621 dengan fasa hydromagnesite. Nilai rata-rata (mean) analisis menggunakan Particle Size Analyzer (PSA) setelah ditambahkan inhibitor menunjukkan penurunan ukuran partikel kristal yakni dari 28,10 menjadi 21,07 m dan nilai tengah (median) dari 14,41 menjadi 12,95 m. Kata Kunci : asap cair tempurung kelapa, ekstrak kulit nanas, inhibitor, kerak MgCO3,. The formation of MgCO3 scale causes quite a lot of scale accumulation in the pipe which can inhibit heat transfer and result in enormous losses. Therefore, to overcome this problem, this research was carried out by testing the inhibitor mixture of pineapple peel extract and coconut shell liquid smoke grade 2 (NA) on magnesium carbonate (MgCO3) scale using the seeded experiment method at varying concentrations of MgCO3 growth solution of 0.100; 0.150; 0.200; and 0.250 M tested at various ratios of NA inhibitor concentrations 1:3, 2:3, 3:3, and 4:3. The most effective concentration ratio is 4:3, and it was varied again into concentrations of 50, 100 and 150 ppm. The highest percentage value for effectiveness is the ratio of a mixture of NA 4:3 with a concentration of 150 ppm to a growth solution with a concentration of 0.100 M of 59.10 %. Based on the results of analysis using Scanning Electron Microscopy (SEM) after adding inhibitors the morphology of the MgCO3 scale becomes thinner and looks more brittle. Analysis using X-Ray Diffraction (XRD) showed that the MgCO3 scale without and with the addition of inhibitors had a peak similarity with the previous research data number 96-900-7621 with the hydromagnesite phase. The average value (mean) analysis using the Particle Size Analyzer (PSA) after adding inhibitors showed a decrease in crystal particle size from 28.10 to 21.07 m and the median value (median) from 14.41 to 12.95 m Keywords : coconut shell liquid smoke, inhibitor, MgCO3 scale, pineapple peel extract.

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	2301992779 . Digilib
Date Deposited:	07 Aug 2023 01:42
Terakhir diubah:	07 Aug 2023 01:42
URI:	http://digilib.unila.ac.id/id/eprint/74132