DEFORMASI KEMBANG SUSUT BALOK BETON YANG MENGGUNAKAN BAHAN SEMEN JENIS PCC

ANGGITA, YULIANA LESTARI (2023) DEFORMASI KEMBANG SUSUT BALOK BETON YANG MENGGUNAKAN BAHAN SEMEN JENIS PCC. TEKNIK, LAMPUNG.

Preview	File PDF 1. ABSTRAK ANGGITA YULIANA LESTARI 1915011039.pdf Download (122Kb) | Preview
	File PDF 2. SKRIPSI FULL ANGGITA YULIANA LESTARI 1915011039.pdf Restricted to Hanya staf Download (7Mb) | Minta salinan
Preview	File PDF 3. SKRIPSI TANPA BAB PEMBAHASAN ANGGITA YULIANA LESTARI 191501109.pdf Download (5Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Balok adalah elemen penting dalam konstruksi bangunan yang berfungsi untuk mentransfer beban dari pelat. Kemampuan tersebut tergantung pada perlakuan yang diberikan sebelum beton menerima beban. Perawatan yang benar setelah pengecoran dapat meminimalkan keretakan akibat deformasi. Deformasi beton terjadi dalam bentuk penyusutan dan pengembangan yang dapat dipengaruhi oleh temperatur dan relative humidity (RH) sekeliling. Kecenderungan pemakaian semen tipe PCC terus meningkat dibandingkan dengan OPC karena lebih ramah lingkungan dan dapat mengurangi pemanasan global. Tujuan dari penelitian ini adalah untuk mengetahui bagaimana perilaku deformasi balok beton berdasarkan umur benda uji serta hubunganya dengan temperature dan RH sekeliling beton. Penelitian ini dilakukan selama 90 hari. Digunakan 3 buah benda uji balok berukuran 15 cm x 15 cm x 60 cm, dengan kuat tekan rencana 20,75 MPa. Benda uji diletakkan di atas dua buah tumpuan. Regangan diperoleh dengan menggunakan kawat getar tertanam (EVWSG) yang berada pada 5 cm dari ujung benda uji. Pengamatan dilakukan segera setelah pengecoran. Data dari ketiga benda uji dianalisis menggunakan kriteria Dixon. Hasil penelitian menunjukkan bahwa nilai kembang susut beton pada umur 90 hari memiliki nilai lebih besar 2,34 kali daripada prediksi ACI 209R. Hal ini berarti ACI 209R tidak dapat diterapkan secara langsung dalam mendesain susut beton dan penggunaan pedoman tersebut harus disesuaikan dengan kondisi lokal dan didukung oleh penelitian dan uji coba yang sesuai di lingkungan Indonesia. Susut beton dipengaruhi oleh temperatur dan RH sekeliling beton, dibuktikan ketika RH sekeliling beton tinggi dan suhu udara yang rendah, maka penyusutan yang terjadi akan rendah, dan sebaliknya. Kata kunci: balok, susut, temperatur, RH, PCC. ABSTRACT Beams are important elements in building construction that function to transfer loads from plates. This ability depends on the treatment given before the concrete receives the load. Proper care after casting can minimize cracking due to deformation. Concrete deformation occurs in the form of shrinkage and expansion, which can be influenced by the surrounding temperature and relative humidity (RH). The tendency to use PCC type cement continues to increase compared to OPC because it is more environmentally friendly and can reduce global warming. The aim of this research is to determine the deformation behavior of concrete blocks based on the age of the test object and its relationship with the temperature and RH surrounding the concrete. This research was conducted for 90 days. Three test beams measuring 15 cm x 15 cm x 60 cm were used, with a concrete quality of 20.75 MPa. The test object is placed on two supports. The strain was obtained using an embedded vibrating wire (EVWSG) located 5 cm from the end of the test object. Observations were made immediately after casting. Data from the three test objects was analyzed using Dixon's criteria. The research results show that the swelling and shrinkage value of concrete at 90 days is 2.34 times greater than the ACI 209R prediction. This means that ACI 209R cannot be applied directly to the design of concrete shrinkage, and the use of these guidelines must be adapted to local conditions and supported by appropriate research and trials in the Indonesian environment. Concrete shrinkage is influenced by the temperature and RH around the concrete. When the RH around the concrete is high and the air temperature is low, the shrinkage that occurs will be low, and vice versa. Keywords: beam, shrinkage, temperature, RH, PCC.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 690 Pembangunan gedung
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Sipil
Pengguna Deposit:	2308822310 . Digilib
Date Deposited:	20 Nov 2023 08:07
Terakhir diubah:	20 Nov 2023 08:09
URI:	http://digilib.unila.ac.id/id/eprint/76926

Actions (login required)

Lihat Karya Akhir