PENGARUH PENGGUNAAN GAS ARGON + CO2 DAN TANPA GAS PADA PENGELASAN GMAW BAJA AISI 1045

Bagas , Muharam Pratama (2023) PENGARUH PENGGUNAAN GAS ARGON + CO2 DAN TANPA GAS PADA PENGELASAN GMAW BAJA AISI 1045. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK.pdf Download (30Kb) | Preview
	File PDF 2. SKRIPSI FULL.pdf Restricted to Hanya staf Download (4Mb) | Minta salinan
Preview	File PDF 3. SKRIPSI TANPA PEMBAHASAN.pdf Download (4Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Pengelasan GMAW merupakan suatu proses pengelasan yang sering menggunakan campuran gas Argon dan CO2 sebagai gas pelindung. Pengelasan ini menggunakan sumber panas energi listrik yang diubah menjadi energi panas. Sementara Baja AISI 1045 merupakan baja yang memiliki kadar karbon antara 0,43 dan 0,50% sehingga tergolong dalam baja karbon sedang. Baja ini banyak digunakan karena mempunyai sifat mampu las yang baik (machinabillity). Penelitian ini bertujuan untuk mengkaji pengaruh gas pelindung (shielding gas) dan tanpa Gas Metal Arc Welding (GMAW) terhadap sifat sambungan las berbahan baja AISI 1045, serta kekuatan sambungan las yang dibuat menggunakan dua prosedur pengelasan GMAW. Variasi gas yang digunakan dalam penelitian ini yaitu Argon+CO2 dan tanpa gas pelindung dan arus yang digunakan yaitu 100 Ampere. Dari pengujian yang dilakukan, diketahui bahwa hasil uji visual terhadap pengelasan GMAW menggunakan gas pelindung Ar+CO2 dan tanpa gas menghasilkan karakteristik pengelasan yang berbeda dimana pengelasan menggunakan gas pelindung lebih mengkilap dan tanpa gas pelindung lebih gelap. Sementara untuk perbandingan hasil uji tarikdan uji impak apabila menggunakan gas Ar+CO2 dan tanpa gas dengan menggunakan arus 100 Ampere, hasil pengujian pengelasan tanpa gas pelindung menghasilkan hasil yang lebih optimal. Kata kunci: Pengelasan GMAW, Uji Visual, Uji Impak, Uji Tarik GMAW welding is a welding process that often uses a mixture of Argon and CO2 gas as a protective gas. This welding uses a heat source, electrical energy which is converted into heat energy. Meanwhile, AISI 1045 steel is steel that has a carbon content of between 0.43 and 0.50%, so it is classified as medium carbon steel. This steel is widely used because it has good weldability (machinability). This research aims to examine the effect of shielding gas and without Gas Metal Arc Welding (GMAW) on the properties of welded joints made from AISI 1045 steel, as well as the strength of welded joints made using two GMAW welding procedures. The gas variation used in this research is Argon+CO2 and without protective gas and the current used is 100 Ampere. From the tests carried out, it is known that the visual test results of GMAW welding using protective gas Ar+CO2 and without gas produce different welding characteristics where welding using protective gas is brighter and without protective gas is darker. Meanwhile, to compare the results of the tensile test and impact test when using Ar+CO2 gas and without gas using a current of 100 Ampare, the welding test results without protective gas produced more optimal results. Keywords: GMAW Welding, Visual Test, Impact Test, Tensile Test

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Mesin
Pengguna Deposit:	2308541084 . Digilib
Date Deposited:	24 Jan 2024 04:23
Terakhir diubah:	24 Jan 2024 04:23
URI:	http://digilib.unila.ac.id/id/eprint/78270

Actions (login required)

Lihat Karya Akhir