Nadira , Anjani (2025) STUDI PENAMBAHAN ASAP CAIR CANGKANG KELAPA SAWIT DAN EKSTRAK BUAH MENGKUDU (Morinda citrifolia) SEBAGAI INHIBITOR KERAK KALSIUM KARBONAT (CaCO3). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.
|
File PDF
Nadira_ABSTRAK - Nadira Anjani.pdf Download (226Kb) | Preview |
|
![[img]](http://digilib.unila.ac.id/style/images/fileicons/text.png) |
File PDF
Nadira_SKRIPSI FULL - Nadira Anjani.pdf Restricted to Hanya staf Download (4075Kb) | Minta salinan |
|
|
File PDF
Nadira_SKRIPSI TANPA BAB PEMBAHASAN - Nadira Anjani.pdf Download (4046Kb) | Preview |
Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)
Pembentukan kerak menjadi masalah serius yang dihadapi sebagian besar bidang industri. Penumpukan kerak seperti kalsium karbonat (CaCO3) akan mengurangi efesiensi proses aliran fluida dan mempersempit diameter pipa. Oleh karena itu, dalam penelitian ini telah dilakukan pengujian inhibitor campuran asap cair cangkang kelapa sawit dan ekstrak mengkudu (AM) untuk menghambat pertumbuhan kerak CaCO3 menggunakan metode seeded experiment. Larutan pertumbuhan CaCO3 sebesar 0,0250; 0,0375; 0,0500; dan 0,0675 M diujikan pada variasi perbandingan konsentrasi inhibitor AM 5:2, 5:4, 5:6, dan 5:8. Nilai persentase efektifitas yang paling tinggi yaitu pada inhibitor dengan perbandingan konsentrasi inhibitor campuran AM 5:8 terhadap larutan pertumbuhan dengan konsentrasi 0,0250 M sebesar 160,15 %. Hasil karakterisasi menggunakan Scanning Electron Miscrocopy (SEM) setelah ditambahkan inhibitor morfologi kristal CaCO3 didominasi aroganit dan muncul fasa veterit. Analisis menggunakan X-Ray Diffraction (XRD) setelah penambahan inhibitor menunjukkan adanya penurunan intensitas dengan perbedaan fasa kristal dari kristal hardscale (kalsit) menjadi softscale (aragonit dan vaterit). Analisis menggunakan Particle Size Analyzer (PSA) menunjukkan bahwa kerak CaCO3 sebelum dan setelah penambahan inhibitor mengalami penurunan ukuran kristal yakni nilai rata-rata (mean) dari 70,92 μm menjadi 53,12 μm dan nilai tengah (median) dari 29,28 μm menjadi 19,27 μm. Kata Kunci: Mengkudu, inhibitor, CaCO3, kerak Scale formation is a serious problem faced by most industrial fields. The accumulation of scale such as calcium carbonate (CaCO3) will reduce the efficiency of the fluid flow process and narrow the pipe diameter. Therefore, in this study, a test of a mixture of liquid smoke inhibitors from palm shells and mengkudu extract (AM) was conducted to inhibit the growth of CaCO3 scale using the seeded experiment method. CaCO3 growth solutions of 0.0250; 0.0375; 0.050; and 0.0675 M were tested at variations in the AM inhibitor concentration ratio of 5:2, 5:4, 5:6, and 5:8. The highest percentage of effectiveness was in the inhibitor with a mixture of AM inhibitor concentration ratio of 5:8 to the growth solution with a concentration of 0.0250 M of 160.15%. The results of characterization using Scanning Electron Miscrocopy (SEM) after the addition of inhibitors, the CaCO3 crystal morphology was dominated by aroganite and the veterite phase appeared. Analysis using X-Ray Diffraction (XRD) after the addition of inhibitors showed a decrease in intensity with a difference in crystal phase from hardscale crystals (calcite) to softscale (aragonite and vaterite). Analysis using Particle Size Analyzer (PSA) showed that the CaCO3 crust before and after the addition of inhibitors experienced a decrease in crystal size, namely the average value (mean) from 70.92 μm to 53.12 μm and the middle value (median) from 29.28μm to 19.27 μm. Keywords: Noni, inhibitor, CaCO3, scale
| Jenis Karya Akhir: | Skripsi |
|---|---|
| Subyek: | 500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan |
| Program Studi: | FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM (FMIPA) > Prodi S1 Kimia |
| Pengguna Deposit: | UPT . Siswanti |
| Date Deposited: | 27 Oct 2025 07:42 |
| Terakhir diubah: | 27 Oct 2025 07:42 |
| URI: | http://digilib.unila.ac.id/id/eprint/92086 |
Actions (login required)
 |
Lihat Karya Akhir |