ANALISIS PENGARUH PENAMBAHAN ZAT ADDITIVE ISS 2500 TERHADAP KUAT TEKAN BATU BATA DENGAN DAN TANPA PROSES PEMBAKARAN

Aria Febriantama, 1015011035 (2016) ANALISIS PENGARUH PENAMBAHAN ZAT ADDITIVE ISS 2500 TERHADAP KUAT TEKAN BATU BATA DENGAN DAN TANPA PROSES PEMBAKARAN. FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (93Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (2784Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2398Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Batu bata merupakan material yang terbuat dari tanah liat. Batu bata dibuat dengan atau tanpa campuran tambahan yang melalui beberapa proses dan tahapan. Dalam penelitian ini digunakan bahan tanah liat dengan bahan tambahan ISS 2500 (Ionic Soil Stabilizer) kadar campuran 0,9 ml, 1,2 ml, 1,5 ml dan 2,1 ml dengan tujuan memanfaatkan zat additive sekaligus diharapkan dapat meningkatkan kualitas batu bata. Maka perlu dilakukan penelitian ini, agar penelitian ini bisa dijadikan pembanding dengan yang ditetapkan SNI. Sampel tanah yang diuji pada penelitian ini yaitu tanah lempung yang berasal dari jl. Nunyai, Rajabasa. Dilakukan pemeraman selama 7 hari, serta dengan perlakuan pembakaran dan tanpa pembakaran batu bata. Berdasarkan hasil pengujian fisik tanah asli, USCS mengklasifikasikan sampel tanah sebagai tanah lempung dengan plastisitas rendah dan termasuk ke dalam kelompok ML. Hasil penelitian pengujian kuat tekan pasca pembakaran dari keempat kadar, menghasilkan nilai kuat tekan rata-rata maksimum pada kadar ISS 2500 2,1 ml sebesar 21,24 kg/cm2 yang tidak masuk kedalam kelas 25. Nilai kuat tekan rata-rata maksimum batu bata sebelum pembakaran dihasilkan oleh kadar ISS 2500 2,1 ml yaitu sebesar 4,25 kg/cm2 yang juga tidak masuk kedalam kelas 25 berdasarkan tabel kekuatan tekan batu bata (SNI tahun 1991). Kata Kunci : Batu bata, tanah lempung, iss 2500 (ionic soil stabilizer), kuat tekan. abstractBrick is a material th at made of clay. Bricks were made with or without additional mixturel through some processes and stages. I n t his study used the clay with additional mixture 2500 ISS ( Ionic Soil Stabilizer ) which has variety levels mixture of 0,9 ml , 1,2 ml , 1,5 ml and 2,1 ml with the intention to improve the quality of brick. It is necessary to do the research , so this study can be compared with SNI standards. The tested samples in this study are clay that comes from jl . Nunyai , Rajabasa . It sample was curing for 7 day and then, the samples will be done with or without burning process. Based on the results of physical testing the samples, USCS classify soil samples as clay with low plasticity and belongs to the ML group . After doing research of compressive strength testing of with and without burning process from four levels generating the compressive strength maximum average at a level of 2.1 ml both of them. With value 21,24 kg / cm2 for burning process and 4.25 kg / cm2 for without burning process. Which is both of those treatments are not included into 25 classes based on tables strength of compressed bricks ( SNI 1991 ) . Keywords: brick, clay, iss 2500 (ionic soil stabilizer), compressive strength.

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Sipil
Pengguna Deposit:	4897891 . Digilib
Date Deposited:	03 Mar 2016 02:13
Terakhir diubah:	03 Mar 2016 02:13
URI:	http://digilib.unila.ac.id/id/eprint/21395

Actions (login required)

Lihat Karya Akhir