PENGARUH SUHU KALSINASI (150, 250, DAN 350οC) PADA ELEKTRODE SUPERKAPASITOR BERBAHAN ZEOLIT BERBASIS SILIKA SEKAM PADI TERHADAP REVERSIBILITAS REAKSI ELEKTROKIMIA

SITI IMAS MASITOH, 1217041045 (2016) PENGARUH SUHU KALSINASI (150, 250, DAN 350οC) PADA ELEKTRODE SUPERKAPASITOR BERBAHAN ZEOLIT BERBASIS SILIKA SEKAM PADI TERHADAP REVERSIBILITAS REAKSI ELEKTROKIMIA. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

[img]
Preview
File PDF
ABSTRAK (ABSTRACT).pdf

Download (11Kb) | Preview
[img] File PDF
SKRIPSI FULL.pdf
Restricted to Hanya pengguna terdaftar

Download (2673Kb)
[img]
Preview
File PDF
SKRIPSI TANPA BAB PEMBAHASAN.pdf

Download (2673Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Penelitian ini dilakukan untuk mengetahui pengaruh suhu kalsinasi terhadap pembentukan fase zeolit, nilai konstanta standar kecepatan elektron (k0), dan keterkaitan hubungan antara fase zeolit dengan nilai konstanta standar kecepatan elektron (k0). Zeolit sintesis diperoleh dari pencampuran melalui reaksi kimia menggunakan metode sol gel antara silika yang bersumber dari sekam padi dan natrium alumina. Zeolit kemudian dikalsinasi pada suhu 150, 250, dan 350οC serta dikarakterisasi menggunakan XRD (X-Ray Diffraction) dan CV (Cyclic Voltammetry). Hasil analisis XRD pada suhu kalsinasi 150οC telah terbentuk fase Gibbsite. Pada suhu kalsinasi 250οC telah terbentuk fase Gibbsite, Bohmite, dan Quartz. Serta pada suhu kalsinasi 350οC terbentuk fase Bohmite dan Quartz. Hasil analisis CV menunjukkan nilai k0 yang bervariasi, dan mekanisme reaksi yang terjadi bersifat irreversible. Fase Gibbsite pada suhu kalsinasi 150οC diperoleh nilai k0 tertinggi sebesar 3,75x10-7. Fase Gibbsite, Bohmite dan Quartz pada suhu kalsinasi 250οC diperoleh nilai k0 tertinggi sebesar 1,52x10-7. Fase Bohmite dan Quartz pada suhu kalsinasi 350οC diperoleh nilai k0 tertinggi sebesar 2,16x10-7. Kata kunci: Elektrode, Zeolit, Elektrokimia, Reversibilitas, Superkapasitor. ABSTRACT This study was conducted to determine the effect of calcination on the zeolite phase, the constant value standard velocity of the electron (k0), and the interrelationship between the phase zeolite with constant value standard velocity electron (k0). Synthetic zeolite obtained from mixing through a chemical reaction using the silica sol gel derived from rice husk and sodium alumina. Zeolite then calcined at a temperatures of 150, 250, and 350οC and characterized using XRD (X-Ray Diffraction) and CV (Cyclic voltammetry). The results of XRD analysis on the calcination 150οC Gibbsite phase has been formed, in the calcination 250οC been formed Gibbsite, Bohmite, and Quartz. As well as the calcination 350οC formed Bohmite phase and Quartz. CV analysis results showed the k0 value varies, and the mechanism reaction is irreversible. Gibbsite phase at a calcination 150οC k0 highest values obtained by 3,75x10-7, Gibbsite phase, Bohmite and Quartz on the calcination 250οC k0 highest values obtained by 1,52x10-7, as well as the phase Bohmite and Quartz on the calcination values obtained 350οC k0 highest of 2,16x10-7. Keywords: Electrodes, Zeolite, Electrochemistry, Reversibility, Supercapacitor.

Jenis Karya Akhir: Skripsi
Subyek: > QC Physics
Program Studi: FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit: 4713960 . Digilib
Date Deposited: 30 Nov 2016 04:07
Terakhir diubah: 30 Nov 2016 04:07
URI: http://digilib.unila.ac.id/id/eprint/24562

Actions (login required)

Lihat Karya Akhir Lihat Karya Akhir