VARIASI DOPING Pb TERHADAP PERTUMBUHAN FASE BAHAN SUPERKONDUKTOR Bi-2212 PADA KADAR Ca 1,10 DAN SUHU SINTERING 830℃

RIANDINI PRATIWI , 1217041043 (2017) VARIASI DOPING Pb TERHADAP PERTUMBUHAN FASE BAHAN SUPERKONDUKTOR Bi-2212 PADA KADAR Ca 1,10 DAN SUHU SINTERING 830℃. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK (ABSTRACT).pdf Download (8Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (2359Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (1966Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Penelitian tentang pengaruh doping Pb yaitu 0; 0,1; 0,2; 0,3 dan 0,4 terhadap pertumbuhan fase bahan superkonduktor Bi-2212 Ca 1,10 telah dilakukan dengan metode padatan pada suhu kalsinasi 800°C selama 10 jam dan suhu sintering 830°C selama 20 jam. Pengaruh doping Pb terhadap pertumbuhan fase bahan superkonduktor dapat dilihat berdasarkan fraksi volume, impuritas, dan derajat orientasi. Hasil penelitian menunjukan sampel tanpa doping Pb Kata kunci : superkonduktor Bi-2212, doping Pb, fraksi volume, derajat orientasi ABSTRACT Research on the effect of Pb doping is 0; 0.1; 0.2; 0.3 and 0.4 to the phase growth of the Bi-2212 Ca 1.10 superconducting material was carried out by the solid state reaction method at a calcination temperature of 800 °C. for 10 hours and sintering temperature of 830 °C. for 20 hours. The effect of Pb doping on the phase growth of superconducting material can be seen by volume fraction, impurity, and degree of orientation. The results showed that samples without Pb doping Key word : Superconductor Bi-2212, doping Pb, volume fraction, orientation degree, impurities

Jenis Karya Akhir:	Skripsi
Subyek:	> Q Science (General)
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	5713537 . Digilib
Date Deposited:	06 Sep 2017 08:11
Terakhir diubah:	06 Sep 2017 08:11
URI:	http://digilib.unila.ac.id/id/eprint/28214

Actions (login required)

Lihat Karya Akhir