PREPARASI DAN KARAKTERISASI KALSIUM SILIKAT BERBAHAN DASAR CANGKANG KERANG DARAH PADA SUHU KALSINASI 1100 oC

Neta Oktavia, 1317041027 (2018) PREPARASI DAN KARAKTERISASI KALSIUM SILIKAT BERBAHAN DASAR CANGKANG KERANG DARAH PADA SUHU KALSINASI 1100 oC. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (24Kb) | Preview
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2254Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (5Mb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Kalsium silikat dapat di sintesis dengan menggunakan metode konvensional yaitu metode reaksi padatan dengan menggunakan bahan dasar sekam padi sebagai sumber silika dan cangkang kerang darah sebagai sumber CaCO3 serta dengan menggunakan CaCO3 komersil yang kemudian di kalsinasi pada suhu 1100 oC. Hasil DTA/TGA memperlihatkan adanya dekomposisi fasa CaCO3 dan masih adanya puncak-puncak eksotermik yang menandai adanya proses kristalisasi pada sampel, hal ini dapat dilihat pula pada pola XRD bahwa adanya trnasformasi dari fasa β-CaSiO3 menjadi α-CaSiO3 serta mulai munculnya fasa CaSiO3 sebagai fasa minor. Spektrum FTIR pada kedua sampel memperlihatkan bahwa terdapat puncak karakteristik dari gugus fungsi kalsium silikat yaitu adanya puncak Si-O-Ca. Selain itu, morfologi SEM memperlihatkan partikel berbentuk acicular dengan ukuran partikel kalsium silikat cangkang kerang darah lebih kecil yaitu 0,29 µm dibandingkan dengan kalsium silikat CaCO3 yaitu 0,33 µm. Kata kunci: Cangkang kerang darah, kalsium silikat, β-CaSiO3, α-CaSiO3, kalsinasi. ABSTRACT Calcium silicate can be synthesized using conventional method that is solid state reaction method by using rice husk as source of silica and blood cockle shell as source of CaCO3 and by using commercial CaCO3 as raw materials then calcined at 1100 oC. The DTA/TGA results show there are decomposition phase of CaCO3 and exothermic peaks that remarked crystallization process to the samples, it is considerably noticed on the X-Ray Diffraction there was a transformation from β-CaSiO3 to α-CaSiO3 phase and emergence of CaSiO3 phase as minor phase. The FTIR spectrum of both samples show that there was a characteristic peaks of the functional group present in the calcium silicate that is Si-O-Ca peak. Afterward, SEM morphology shows particle of acicular shaped and that size particle of blood cockle shells calcium silicate is smaller that is 0.29 μm compared with CaCO3 calcium silicate size is 0.33 μm. Keywords: Blood cockle shells, calcium silicate, β-CaSiO3, α-CaSiO3, calcination.

Jenis Karya Akhir:	Skripsi
Subyek:	> QC Physics
Program Studi:	FAKULTAS MIPA > Prodi Fisika
Pengguna Deposit:	201812668 . Digilib
Date Deposited:	03 Jul 2018 08:53
Terakhir diubah:	03 Jul 2018 08:53
URI:	http://digilib.unila.ac.id/id/eprint/32046

Actions (login required)

Lihat Karya Akhir