STUDI TRANSPOR FENOL MENGGUNAKAN SENYAWA PEMBAWA KOPOLI(EUGENOL-DVB) DENGAN METODE SUPPORTED LIQUID MEMBRANE (SLM)

WINDI ANTIKA , 1417011112 (2018) STUDI TRANSPOR FENOL MENGGUNAKAN SENYAWA PEMBAWA KOPOLI(EUGENOL-DVB) DENGAN METODE SUPPORTED LIQUID MEMBRANE (SLM). FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM , UNIVERSITAS LAMPUNG.

	File PDF ABSTRAK.pdf Download (19Kb)
	File PDF SKRIPSI FULL.pdf Restricted to Hanya pengguna terdaftar Download (2269Kb)
	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (2270Kb)

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Keberadaan fenol di perairan menimbulkan dampak negatif bagi kesehatan dan lingkungan. Fenol merupakan polutan beracun yang terdapat pada limbah industri. Penelitian mengenai studi transpor fenol menggunakan kopoli(eugenol-DVB) sebagai senyawa pembawa berbasis membran Polytetrafluoroethylene (PTFE) dengan metode supported liquid membrane (SLM) dilakukan untuk mengatasi masalah tersebut. Beberapa parameter yang mempengaruhi transpor fenol telah dilakukan diantaranya adalah pH fasa sumber, konsentrasi fasa penerima, waktu immersion, konsentrasi senyawa pembawa dan waktu transpor. Sintesis kopoli(eugenol-DVB) dilakukan melalui reaksi kopolimerisasi antara eugenol dengan DVB 8% menggunakan katalis BF3O(C2H5)2. Produk polimer yang dihasilkan dikarakterisasi menggunakan FTIR. Konsentrasi fenol setelah proses transpor ditentukan dengan metode spektrofotometri menggunakan reagen 4- aminoantipirin dan absorbansinya diukur pada panjang gelombang λ= 456 nm. Hasil penelitian menunjukkan bahwa senyawa pembawa kopoli (eugenol-DVB) yang digunakan pada membran Polytetrafluoroethylene (PTFE) mampu mentranspor fenol pada keadaan optimum: pH fasa sumber 5,5, konsentrasi NaOH 0,1 M, waktu immersion 1 jam, konsentrasi senyawa pembawa 0,01 M dan waktu transpor selama 24 jam. Setelah 24 jam transpor, % ML Loss tidak berkurang secara signifikan yaitu sebesar 8,35 % diperkuat dengan hasil karakterisasi SEM dan FTIR. Fenol tertranspor secara efektif, ketika menggunakan membran PTFE dengan senyawa pembawa kopoli(eugenol-DVB) 8% yaitu mencapai 92,10 %. Kata Kunci : Fenol, Kopoli(eugenol-DVB), SLM abstract The presence of phenol in the water has a negative impact for health and the environment. Phenol is a toxic pollutant which was found in industrial waste. A research on the study of phenol transport using copoly (eugenol-DVB) as a carrier based on Polytetrafluoroethylene (PTFE) membrane with supported liquid membrane (SLM) method was conducted to resolve the problem. Some parameters that affect phenol transport have been carried out included source phase pH, receiving phase concentration, immersion time, concentration of the carrier and transport time. Synthesis of copoly (eugenol-DVB) was carried out through copolymerization reaction between eugenol and DVB 8% using catalyst BF3O(C2H5)2. The result of polymer product was characterized using FTIR. Phenol concentration after the transport process was determined by spectrophotometric method using 4-aminoantipyrine reagent and its absorbance was measured at a wavelength λ = 456 nm. The result showed that copoly(eugenol-DVB) was used in Polytetrafluoroethylene (PTFE) membranes was able to transport phenol at optimum conditions: source phase pH 5.5, 0.1 M NaOH concentration, 1 hour immersion time, concentration of carrier 0.01 M and transport time for 24 hours. After 24 hours of transport,% ML Loss was not significantly reduced, which was 8.35% strengthened by the results of SEM and FTIR characterization. Phenol was effectively transported, when used PTFE membranes with carrier copoly(eugenol-DVB) 8% achieved 92.10%. Keyword : Phenol, Copoly(eugenol-DVB), SLM

Jenis Karya Akhir:	Skripsi
Subyek:	> QD Chemistry
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	188807871 . Digilib
Date Deposited:	15 Oct 2018 06:41
Terakhir diubah:	15 Oct 2018 06:41
URI:	http://digilib.unila.ac.id/id/eprint/33712

Actions (login required)

Lihat Karya Akhir