PENGARUH PENAMBAHAN KOMPOSISI MgO PADA SiO2 TERHADAP KARAKTERISTIK KOMPOSIT MgO-SiO2 BERBASIS SILIKA SEKAM PADI

REZA PAHLEPI, 0817041052 (2013) PENGARUH PENAMBAHAN KOMPOSISI MgO PADA SiO2 TERHADAP KARAKTERISTIK KOMPOSIT MgO-SiO2 BERBASIS SILIKA SEKAM PADI. FAKULTAS MIPA, UNIVERSITAS LAMPUNG.

Preview	File PDF a. COVER.pdf Download (22Kb) | Preview
Preview	File PDF hal i-xiii.pdf Download (229Kb) | Preview
Preview	File PDF l. DAFTAR ISI.pdf Download (60Kb) | Preview
Preview	File PDF m. DAFTAR TABEL & GAMBAR.pdf Download (77Kb) | Preview
Preview	File PDF o. BAB 1.pdf Download (105Kb) | Preview
Preview	File PDF p. BAB II.pdf Download (474Kb) | Preview
Preview	File PDF q. BAB III.pdf Download (128Kb) | Preview
	File PDF r. BAB IV FIX.pdf Restricted to Hanya pengguna terdaftar Download (1068Kb)
Preview	File PDF s. BAB V.pdf Download (51Kb) | Preview
Preview	File PDF t. DAPUS sip.pdf Download (178Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

ABSTRAK Telah dilakukan penelitian tentang MgO-SiO2 dari bahan baku magnesium nitrat heksahidrat dan silika sekam padi menggunakan metode sol-gel dengan komposisi MgO dan SiO2 1:1, 1:2, 1:3, 1:4, 1:5, dan 1:10. Gel yang diperoleh dari pencampuran sol magnesium oksida dan sol silika dipanaskan pada suhu 110 °C hingga dihasilkan serbuk MgO-SiO2. Sampel selanjutnya dipellet dan disintering pada suhu 700 oC. Adapun MgO-SiO2 diaplikasikan sebagai katalis dan dikarakterisasi menggunakan XRD, SEM/EDS, BET,dan uji aplikasi katalis. Hasil XRD menunjukkan struktur pada sampel yang disintering pada suhu 700 oC berfasa amorf masih terbentuk fasa magnesium silicate dan silicon oxide sebagai pembanding sampel disintering pada suhu 800 oC sampel bertranformasi menjadi fasa forsterite disertai terbentuknya fasa cristobalite dan periclase. Hasil analisis SEM (mikrostruktur) pada sampel menunjukkan bahwa sampel belum membentuk butiran, masih terjadi proses aglomerasi, pada permukaan terlihat gumpalan (Cluster) yang mengindikasikan mikrostruktur komposit MgO-SiO2 berbentuk amorf dan hasil EDS dengan tiga spot menunjukkan terdistribusi unsur utama Mg, Si, dan O secara merata pada semua spot. Hasil BET menunjukkan diameter pori pada proses adsorpsi metode BJH komposit MgO-SiO2 berukuran makropori yaitu 141 nm, sedangkan pada desorpsi metode BJH komposit MgO-SiO2 berukuran mesopori yaitu 30 nm. Hasil pengujian katalis dengan GC-MS menghasilkan senyawa utama metil kaproat, metil kaprilat, metil kaprat, metil laurat, metil miristat, dan metil palmitat sebagai komponen penyusun produk biodiesel dari minyak kelapa. Hasil analisis persen konversi dan viskositas pada biodisel menunjukkan bahwa dimana semakin banyak komposisi MgO pada silika meningkatkan nilai persen konversi dan menurunkan viskositas, sampel terbaik adalah dengan perbandingan 1:1. Kata kunci: MgO-SiO2, sekam padi, silika, sol-gel, XRD, SEM/EDS, BET, dan uji aplikasi ABSTRACT In this study, a series of MgO-SiO2 with the ratio of MgO to SiO2 of 1:1, 1:2, 1:3, 1:4, 1:5, and 1: 10 was synthesized from magnesium nitrate hexahydrate and rice husk silica using sol-gel method. The composite was prepared by mixing magnesium nitrate hexahydrate solution and silica sol. The gel produced was dried at 110 °C to produce MgO-SiO2 powder, and subsequently sintered at 700 °C for characterization using XRD, SEM/EDS, BET, and test applications catalyst. The result of XRD characterization showed that the structure of the sample at a temperature of 700 oC was sintered amorphous phase is formed magnesium silicate and silicon oxide as the comparison sample at a temperature of 800 oC was sintered sample transformed into phase with the formation of forsterite, periclase and cristobalite phase. The results of SEM analysis (microstructure) on the samples showed that the samples has not formed granules, is a process of agglomeration, the visible surface of the granular (Cluster) composite microstructure was indicated by MgO-SiO2 amorphous shape and EDS results showed three spots distributed main elements Mg, Si, and O evenly on all spots. BET results showed adsorption diameter pore at the BJH method MgO-SiO2 composite macropore size is 141 nm, whereas the BJH desorption method sized of composite MgO-SiO2 mesoporous is 30 nm. Test results with GC-MS catalyst produces methyl caproic main compound, methyl caprylate, methyl caprate, methyl laurate, methyl myristate and methyl palmitate as constituent components of biodiesel from palm oil. The results of the analysis of percent conversion and viscosity in biodiesel showed, where a growing number of composition MgO on silica increases value of percent conversion and decrease the value of viscosity, the best sample is 1:1. Key words: MgO-SiO2, rice husk, silica, sol-gel, XRD, SEM, BET, test applications catalyst.

Jenis Karya Akhir:	Skripsi
Subyek:
Program Studi:	FKIP > Prodi Pendidikan Ekonomi IPS
Pengguna Deposit:	UPT Perpustakaan Unila
Date Deposited:	08 Dec 2014 08:06
Terakhir diubah:	08 Dec 2014 08:06
URI:	http://digilib.unila.ac.id/id/eprint/5634

Actions (login required)

Lihat Karya Akhir