PENGARUH ABU SEKAM SEBAGAI BAHAN PENGGANTI SEJUMLAH SEMEN TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON REAKTIF (REACTIVE POWDER CONCRETE)

Mufidah Aulia Annisa, 1415011098 (2019) PENGARUH ABU SEKAM SEBAGAI BAHAN PENGGANTI SEJUMLAH SEMEN TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON REAKTIF (REACTIVE POWDER CONCRETE). FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.

Preview	File PDF ABSTRAK.pdf Download (9Kb) | Preview
	File PDF SKRIPSI FULL.pdf Restricted to Hanya staf Download (937Kb)
Preview	File PDF SKRIPSI TANPA BAB PEMBAHASAN.pdf Download (938Kb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Kualitas beton dapat ditentukan dari komposisi adukan, jenis bahan, dan cara perawatan. Beton reaktif adalah salah satu jenis beton mutu tinggi yang komposisinya mengandung banyak semen dan bahan sangat halus lainnya serta di rawat dengan cara pemanasan. Abu sekam padi yang mengandung senyawa silika juga berpotensi untuk bahan adukan beton reakif. Penelitian ini dilakukan pada variasi prosentase abu sekam sebagai pengganti sejumlah semen (0%, 10%, 20%, 30%, dan 40%) dan cara perawatan benda uji prisma 40 x 40 x 160 mm (pemanasan suhu pada 180o, perawatan uap air panas pada 90 o, dan perendaman dalam air). Pengujian kuat lentur pada umur 7 hari dan kuat tekan pada umur 7 hari dan 28 hari Hasil pengujian menunjukan bahwa kuat lentur optimum 16, 48 MPa diperoleh dari komposisi 10% abu sekam dan perawatan uap air panas. Kuat tekan optimum juga diperoleh dari perawatan uap air panas, namun pada komposisi 30% abu sekam, yaitu 37,54 MPa umur 7 hari dan 54,44 MPa umur 28 hari. Dengan demikian abu sekam dapat digunakan untuk bahan pengganti sebagian semen dalam komposisi beton reaktif dengan perawatan uap air panas. Kata kunci : beton mutu tinggi, beton reaktif , reactive powder concrete, abu sekam, kuat tekan, kuat lentur. The quality of concrete can be determined by mixture composition, type of material, and treatment method. Reactive powder concrete is one of high quality performance concrete containing a lot of cement and fine powders which needs a heat treatment. Rice husk ash containing silica compounds has a potential to be used in concrete mixtures. This research was conducted with the percentage variation of rice husk ash instead of cement (0%, 10%, 20%, 30%, and 40%) and the treatments method were applied on prism samples with dimension of 40 x 40 x 160 mm (180o heating temperature, 90 o steam treatment, and water treatment). The flexural strength test was conducted at 7 days and the compressive strength was tested at 7 days and 28 days. The test results show that the optimum flexural strength was 16.48 MPa, obtained from the composition of 10% rice husk ash with steam treatment. The optimum compressive strength was also obtained by the steam treatment, but on the composition of 30% rice husk ash, which are 37.54 MPa at 7 days and 54.44 MPa at 28 days. It is concluded that rice husk ash can be used as a substitute for some cement in the composition of reactive powder concrete with steam treatment. Keywords: reactive powder concrete, rice husk ash, compressive strength, flexural strength.

Jenis Karya Akhir:	Skripsi
Subyek:	600 Teknologi (ilmu terapan) > 620 Ilmu teknik dan ilmu yang berkaitan 600 Teknologi (ilmu terapan) > 690 Pembangunan gedung
Program Studi:	Fakultas Teknik > Prodi S1-Teknik Sipil
Pengguna Deposit:	UPT . Teti Novianti
Date Deposited:	29 Mar 2022 03:07
Terakhir diubah:	29 Mar 2022 03:07
URI:	http://digilib.unila.ac.id/id/eprint/56400