SINTESIS ZEOLIT ZSM-5 DARI SILIKA SEKAM PADI DAN ALUMINIUM HIDROKSIDA SERTA UJI AKTIVITASNYA SEBAGAI KATALIS REAKSI TRANSESTERIFIKASI MINYAK KELAPA SAWIT

PUTRI DAMAYANTI, 1517011045 (2019) SINTESIS ZEOLIT ZSM-5 DARI SILIKA SEKAM PADI DAN ALUMINIUM HIDROKSIDA SERTA UJI AKTIVITASNYA SEBAGAI KATALIS REAKSI TRANSESTERIFIKASI MINYAK KELAPA SAWIT. Fakultas Matematika dan Ilmu Pengetahuan Alam, UNIVERSITAS LAMPUNG.

Preview	File PDF 1. ABSTRAK.pdf Download (310Kb) | Preview
	File PDF 2. SKRIPSI FULL.pdf Restricted to Hanya staf Download (15Mb)
Preview	File PDF 3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf Download (7Mb) | Preview

Abstrak (Berisi Bastraknya saja, Judul dan Nama Tidak Boleh di Masukan)

Sintesis zeolit ZSM-5 dilakukan dengan metode hidrotermal memanfaatkan silika sekam padi dan Al(OH)3 dengan nisbah molar Si/Al 20. Proses hidrotermal dilakukan pada suhu 180 ℃ dengan memvariasikan waktu kristalisasi yakni 24, 48, 72, 96, dan 120 jam, dilanjutkan dengan kalsinasi pada suhu 600℃ selama 6 jam. ZSM-5 dikarakterisasi dengan teknik XRD, SEM, FTIR, PSA dan BET. Difraktogram mengindikasikan adanya tiga puncak khas ZSM-5 pada 2� (8,6o - 8,7o , 23,2o , dan 23,6o -23,7o ) yang memiliki kesesuaian dengan data International Zeolite Association (IZA). Selain fase kristalin ZSM-5, dalam sampel juga terdapat fase mordenit yang diperkuat dengan adanya bentuk heksagonal dan jarum pada mikrograf sampel. Data FTIR menunjukkan gugus fungsi yang sesuai dengan ZSM-5 standar. Distribusi ukuran partikel umumnya memiliki puncak yang mirip yakni terbentuk 2 cluster dengan rentang ukuran diameter 0,077- 1,047 µm dan 0,954-2,920 µm. Analisis BET menunjukkan pori zeolit diklasifikasi kedalam mesopori yakni > 2 nm. Zeolit yang disintesis dengan waktu kristalisasi berbeda baik sebelum maupun sesudah pertukaran ion memiliki aktivitas katalitik pada reaksi transesterifikasi minyak kelapa sawit dan metanol.ZS-96 merupakan katalis dengan kinerja terbaik dengan persen konversi sebesar 84%. Produk transesterifikasi minyak kelapa sawit dengan metanol merupakan biodiesel dengan komponen yang sesuai dengan asam lemak dalam minyak kelapa sawit, dengan metil oleat dan metil palmitat sebagai komponen utama. Kata kunci : zeolit ZSM-5, hidrotermal, silika sekam padi, waktu kristalisasi, dan transesterifikasi. ZSM-5 zeolite synthesis was carried out by hydrothermal method utilizing silica extracted from rice husk and Al(OH)3 with the Si/Al molar ratio of 20. The hydrothermal process was carried out at 180℃ with varied crystallization time of 24, 48, 72, 96, and 120 hours, followed by calcination at 600 ℃for 6 hours. The prepared ZSM-5 was characterized by XRD, SEM, FTIR, PSA and BET techniques. The XRD difractograms indicate the presence of three typical peaks of ZSM-5 at 2θ of (8.6o -8.7o , 23,2o , dan 23.6o -23.7o ) which are in accordance with the International Zeolite Association (IZA) data. In addition to the ZSM-5 crystalline phase, there are also mordenite phases. The existence of these phases is supported by the presence of hexagonal shapes and needle shape on the SEM micrographs of the samples. FTIR data show the presence of absorption bands associated with chemical bonds and functional groups in ZSM-5. Particle size distributions of the samples are generally similar, showing the existence of 2 clusters with a particle diamter in the range of 0.077 µm-1.047 and 0.954-2.920 µm. According to BET analysis, pore sizes of the particles are > 2 nm, implying that the mesoporous. Zeolites synthesized with different crystallization times both before and after ion exchange have catalytic activity in the transesterification reaction of palm oil and methanol. ZS-96 is the best performing catalyst with 84% conversion. The main components of the biodiesel produced are methyl oleate and methyl palmitate, which are in agreement with the composition of palm oil. Keyword : ZSM-5 zeolite, hydrothermal, rice husk silica, crystallization time, and transesterification

Jenis Karya Akhir:	Skripsi
Subyek:	500 ilmu pengetahuan alam dan matematika > 540 Kimia dan ilmu yang berhubungan
Program Studi:	FAKULTAS MIPA > Prodi Kimia
Pengguna Deposit:	UPT . Digilib2
Date Deposited:	29 Mar 2022 13:10
Terakhir diubah:	29 Mar 2022 13:10
URI:	http://digilib.unila.ac.id/id/eprint/56541

Actions (login required)

Lihat Karya Akhir